Comparing In Vivo Performance of Two Highly Cross-Linked Polyethylene Thermal Treatments: Remelting vs Annealing in Acetabular Liners

Journal of Arthroplasty - Tập 34 - Trang 1509-1513 - 2019
Alison Suraci1, Hakim Louati2, Kathryn N. Culliton2, Paul E. Beaulé1,3
1Division of Orthopaedic Surgery, The Ottawa Hospital General Campus, Ottawa, Ontario, Canada
2Orthopaedic Biomechanics Laboratory, Division of Orthopaedic Surgery, The Ottawa Hospital Research Institute, Civic Campus, Ottawa, Ontario, Canada
3Faculty of Medicine, The University of Ottawa, Ottawa, Ontario, Canada

Tài liệu tham khảo

Bragdon, 2013, The 2012 John Charnley Award: clinical multicenter studies of the wear performance of highly crosslinked remelted polyethylene in THA, Clin Orthop Relat Res, 471, 393, 10.1007/s11999-012-2604-0

Broomfield, 2017, The relationship between polyethylene wear and periprosthetic osteolysis in total hip arthroplasty at 12 years in a randomized controlled trial cohort, J Arthroplasty, 32, 1186, 10.1016/j.arth.2016.10.037

Devane, 2017, Highly cross-linked polyethylene reduces wear and revision rates in total hip arthroplasty, J Bone Joint Surg Am, 99, 1703, 10.2106/JBJS.16.00878

Harris, 1995, The problem is osteolysis, Clin Orthop Relat Res, 46

Leung, 2007, Incidence and volume of pelvic osteolysis at early follow-up with highly cross-linked and noncross-linked polyethylene, J Arthroplasty, 22, 134, 10.1016/j.arth.2007.04.006

Dumbleton, 2002, A literature review of the association between wear rate and osteolysis in total hip arthroplasty, J Arthroplasty, 17, 649, 10.1054/arth.2002.33664

Abu-Amer, 2007, Aseptic loosening of total joint replacements: mechanisms underlying osteolysis and potential therapies, Arthritis Res Ther, 9, S6, 10.1186/ar2170

Hamai, 2016, Comparison of 10-year clinical wear of annealed and remelted highly cross-linked polyethylene: a propensity-matched cohort study, J Mech Behav Biomed Mater, 59, 99, 10.1016/j.jmbbm.2015.12.022

Medel, 2007, Comparative fatigue behavior and toughness of remelted and annealed highly crosslinked polyethylenes, J Biomed Mater Res B Appl Biomater, 83, 380, 10.1002/jbm.b.30807

Reinitz, 2015, Oxidation and other property changes of retrieved sequentially annealed UHMWPE acetabular and tibial bearings, J Biomed Mater Res B Appl Biomater, 103, 578, 10.1002/jbm.b.33240

Dumbleton, 2006, The basis for a second-generation highly cross-linked UHMWPE, Clin Orthop Relat Res, 453, 265, 10.1097/01.blo.0000238856.61862.7d

Kurtz, 2011, History and systematic review of wear and osteolysis outcomes for first-generation highly crosslinked polyethylene, Clin Orthop Relat Res, 469, 2262, 10.1007/s11999-011-1872-4

Livingston, 1997, Complications of total hip arthroplasty associated with the use of an acetabular component with a Hylamer liner, J Bone Joint Surg Am, 79, 1529, 10.2106/00004623-199710000-00010

Stryker, 2007

Glyn-Jones, 2008, The creep and wear of highly cross-linked polyethylene, J Bone Joint Surg Br, 90–B, 556, 10.1302/0301-620X.90B5.20545

Estok, 2005, The measurement of creep in ultrahigh molecular weight polyethylene: a comparison of conventional versus highly cross-linked polyethylene, J Arthroplasty, 20, 239, 10.1016/j.arth.2004.08.008

Martell, 1997, Determination of polyethylene wear in total hip replacements with use of digital radiographs, J Bone Joint Surg Am, 79, 1635, 10.2106/00004623-199711000-00004

Collier, 2003, Evaluation of contemporary software methods used to quantify polyethylene wear after total hip arthroplasty, J Bone Joint Surg Am, 85–A, 2410, 10.2106/00004623-200312000-00020

Kraay, 2010, Reassessment of computerized wear measurement for total hip arthroplasty with correction for projectional image distortion, J Bone Joint Surg Am, 92, 1858, 10.2106/JBJS.I.00832

D’Antonio, 2005, Five-year experience with Crossfire highly cross-linked polyethylene, Clin Orthop Relat Res, 441, 143, 10.1097/00003086-200512000-00024

Martell, 2003, Clinical performance of a highly cross-linked polyethylene at two years in total hip arthroplasty: a randomized prospective trial, J Arthroplasty, 18, 55, 10.1016/S0883-5403(03)00341-3

Nakahara, 2010, Minimum five-year follow-up wear measurement of longevity highly cross-linked polyethylene cup against cobalt-chromium or zirconia heads, J Arthroplasty, 25, 1182, 10.1016/j.arth.2009.09.006

Engh, 2006, A randomized prospective evaluation of outcomes after total hip arthroplasty using cross-linked marathon and non–cross-linked enduron polyethylene liners, J Arthroplasty, 21, 17, 10.1016/j.arth.2006.05.002

Bitsch, 2008, Reduction of osteolysis with use of marathon cross-linked polyethylene, J Bone Joint Surg Am, 90, 1487, 10.2106/JBJS.F.00991

Epinette, 2016, Comparative results from a national Joint registry hip data set of a new cross-linked annealed polyethylene vs both conventional polyethylene and ceramic bearings, J Arthroplasty, 31, 1483, 10.1016/j.arth.2015.12.041

Ries, 1996, Fatigue strength of polyethylene after sterilization by gamma irradiation or ethylene oxide, Clin Orthop Relat Res, 87

Ramani, 1998, Process-Induced Effects in Compression Molding of Ultra-High Molecular Weight Polyethylene (UHMWPE), 5

Hammerberg, 2010, Wear and range of motion of different femoral head sizes, J Arthroplasty, 25, 839, 10.1016/j.arth.2009.07.007

Frankel, 1990, Radiographic demarcation of the acetabular bone-cement interface. The effect of femoral head size, J Arthroplasty, 5, S1, 10.1016/S0883-5403(08)80017-4

Muratoglu, 1999, Unified wear model for highly crosslinked ultra-high molecular weight polyethylenes (UHMWPE), Biomaterials, 20, 1463, 10.1016/S0142-9612(99)00039-3

Takada, 2017, Comparison of wear rate and osteolysis between second-generation annealed and first-generation remelted highly cross-linked polyethylene in total hip arthroplasty. A case control study at a minimum of five years, Orthop Traumatol Surg Res, 103, 537, 10.1016/j.otsr.2017.02.004

Kurtz, 2006, Otto Aufranc Award Paper: significance of in vivo degradation for polyethylene in total hip arthroplasty, Clin Orthop Relat Res, 453, 47, 10.1097/01.blo.0000246547.18187.0b

Kurtz, 2015, Retrieval analysis of sequentially annealed highly crosslinked polyethylene used in total hip arthroplasty, Clin Orthop Relat Res, 473, 962, 10.1007/s11999-014-4113-9

Yun, 2016, Polyethylene liner dissociation is a complication of the DePuy pinnacle cup: a report of 23 cases, Clin Orthop Relat Res, 474, 441, 10.1007/s11999-015-4396-5

Duffy, 2009, Fracture of a cross-linked polyethylene liner due to impingement, J Arthroplasty, 24, 158.e15, 10.1016/j.arth.2007.12.020

Hill, 2016, Early catastrophic failure of a PINNACLE MARATHON® polyethylene acetabular liner: a report of a malpositioned PINNACLE DUOFIX HA® acetabular shell resulting in point loading and accelerated wear, Hip Int, 26, e52, 10.5301/hipint.5000447

Mayer, 2012, Late liner disassociation of a Pinnacle system acetabular component, Orthopedics, 35, e561, 10.3928/01477447-20120327-29

Tower, 2007, Rim cracking of the cross-linked longevity polyethylene acetabular liner after total hip arthroplasty, J Bone Joint Surg Am, 89, 2212, 10.2106/JBJS.F.00758

Ast, 2014, Fractures of a single design of highly cross-linked polyethylene acetabular liners: an analysis of voluntary reports to the United States food and drug administration, J Arthroplasty, 29, 1231, 10.1016/j.arth.2013.12.022

McCalden, 2005, Radiographic methods for the assessment of polyethylene wear after total hip arthroplasty, J Bone Joint Surg Am, 87, 2323

Thông tin
Thông tin xuất bản

Journal of Arthroplasty

Tập 34

1509-1513

Thông tin tác giả