Superior Perovskite Oxide‐Ion Conductor; Strontium‐ and Magnesium‐Doped LaGaO3: I, Phase Relationships and Electrical Properties

Journal of the American Ceramic Society - Tập 81 Số 10 - Trang 2565-2575 - 1998
Kevin Huang1, R. Tichy1, John B. Goodenough1
1Center for Materials Science and Engineering, ETC 9.102, University of Texas, Austin, Texas 78712

Tóm tắt

The single‐phase, cubic‐perovskite region of the LaO1.5‐SrO‐Gao1.5‐MgO phase diagram was determined from room‐temperature and high‐temperature X‐ray diffraction. Two impurity phases were identified, LaSrGaO4 and aSrGa3O7. The conductivity of the oxygen‐deficient perovskite phase was shown to be essentially a purely oxide‐ion conductivity sigmao over a wide range of oxygen partial pressures 10‐22 lessthan equal to PO2 lessthan equal to 1 atm. The highest values of sigmao = 0.17 and 0.08 S/cm were found for La0.8Sr0.2Ga0.83Mg0.17O0.2815 at 800° and 700°C, respectively; they remain stable over a week‐long test. The Arrhenius plot of sigmao is curved, dividing into a high‐temperature region T > T* similar/congruent 600°C and a low‐temperature region T < T*. Above T* all the oxygen vacancies appear to be mobile; below T* they progressively condense into clusters of ordered vacancies.

Từ khóa


Tài liệu tham khảo

10.1021/ja00088a016

Feng M., 1994, A Superior Oxide‐Ion Electrolyte, Eur.J. Solid State Inorg. Chem., 31, 663

10.1111/j.1151-2916.1996.tb08554.x

10.1149/1.1837262

10.1149/1.1836692

Schreinemakers F. A. H., 1909, Gleichgewichte in Quaternären Systemen, Z. Phys. Chem., 65, 553, 10.1515/zpch-1909-6534

10.1016/0167-2738(96)00260-3

10.1111/j.1151-2916.1998.tb02341.x

Steele B. C. H., 1995, Proceedings of the 4th International Symposium on Solide Oxide Fuel Cells, 1028

10.1111/j.1151-2916.1964.tb14368.x

Goodenough J. B., 1995, Solid State Electrochemistry, 43

Atkins P., 1982, Physical Chemistry, 187

10.1016/S0167-2738(88)80013-4

10.1016/0167-2738(82)90046-7

Meyer W., 1937, Ü ber die Beziehungen Zweischen der Energiekonstanten ɛ under der Mengenkonstanten a in der Leitwerts‐Temperaturformel bei Oxydischen Halbleitern, Z. Tech. Phys., 18, 588

10.1016/0167-2738(86)90317-6

10.1016/0167-2738(87)90078-6

10.1016/0167-2738(83)90004-8

10.1021/ja964128l

10.1007/BF00616848

10.1006/jssc.1995.1320

10.1016/0167-2738(92)90089-8

A.Skoworn P.Huang andA.Petric “Structure Study of Lanthanum Gallate Doped with Strontium and Magnesium ” submitted to Solid State Ionics..

Thông tin
Thông tin xuất bản

Journal of the American Ceramic Society

Tập 81 Số 10

2565-2575

Thông tin tác giả