Structure and morphology control in thin films of regioregular poly(3‐hexylthiophene)

Journal of Polymer Science, Part B: Polymer Physics - Tập 49 Số 17 - Trang 1218-1233 - 2011
Martin Brinkmann1
1Institut Charles Sadron CNRS‐Université de Strasbourg 23 rue du Loess 67034 Strasbourg Cedex France

Tóm tắt

AbstractThis review focuses on the structural control in thin films of regioregular poly(3‐hexylthiophene) (P3HT), a workhorse among conjugated semiconducting polymers. It highlights the correlation existing between processing conditions and the resulting structures formed in thin films and in solution. Particular emphasis is put on the control of nucleation, crystallinity and orientation. P3HT can generate a large palette of morphologies in thin films including crystalline nanofibrils, spherulites, interconnected semicrystalline morphologies and nanostructured fibers, depending on the elaboration method and on the macromolecular parameters of the polymer. Effective means developed in the recent literature to control orientation of crystalline domains in thin films, especially by using epitaxial crystallization and controlled nucleation conditions are emphasized. © 2011 Wiley Periodicals, Inc. J Polym Sci Part B: Polym Phys 49: 1218–1233, 2011

Từ khóa


Tài liệu tham khảo

10.1103/RevModPhys.73.681

10.1002/adma.200903193

10.1126/science.290.5499.2123

10.1038/16393

10.1038/44359

10.1016/S1359-0286(02)00006-2

Organic Photovoltaics C. Brabec U. Scherff V. Diakonov 2008 Wiley‐VCH

10.1016/S1369-7021(07)70018-4

Wunderlich B., 1973, In Macromolecular Physics, Vol. 1. Structure, Morphology, Defects

10.1016/S1369-7021(10)70080-8

10.1021/ma00043a019

10.1016/0379-6779(92)90239-F

10.1021/ma951510u

10.1021/ma970655t

10.1021/ma0521349

10.1002/adma.200501838

10.1002/adma.200700014

10.1021/ma7026512

10.1002/pssa.200723423

10.1016/0032-3861(84)90156-3

10.1002/polb.1991.090291007

10.1016/S0032-3861(96)00876-2

10.1021/ma101162x

10.1021/ma00186a013

10.1021/ma9719059

10.1016/S0032-3861(00)00235-4

10.1016/0079-6700(90)90025-V

10.1021/ma901955c

10.1021/ma100551m

10.1103/PhysRevB.79.115207

10.1021/jp1008219

Mena‐Osteriz E., 2000, Angew. Chem. Int. Ed., 39, 2680

10.1002/adma.200304580

10.1002/1521-4095(20020418)14:8<609::AID-ADMA609>3.0.CO;2-7

10.1016/j.synthmet.2004.08.026

10.1063/1.1561435

10.1021/ja055192i

10.1002/adfm.200600673

10.1002/macp.1961.020430110

10.1016/0032-3861(92)90555-B

10.1021/ma047415f

10.1021/cm0513637

10.1002/adfm.200400017

10.1016/j.synthmet.2006.04.012

10.1002/adfm.200902273

10.1038/nmat1590

10.1002/adma.200305275

10.1002/adfm.200400297

10.1063/1.2734387

10.1021/cm049617w

10.1002/adfm.200701459

10.1038/nmat1928

10.1016/j.solmat.2009.11.018

Porzio W., 2011, Eur. Polym. J.

10.1021/ma025887t

10.1021/ma702802x

10.1021/ma900021w

10.1021/ma8023415

10.1063/1.1914768

10.1103/PhysRevLett.98.206406

10.1063/1.3110904

10.1021/ma048159

10.1002/polb.1993.090310614

10.1021/ma801128v

10.1002/adfm.200600922

10.1002/adfm.200801655

10.1002/adfm.200901471

10.1021/ma901955c

10.1002/app.25050

10.1021/ma000977o

10.1021/ma9005445

10.1002/adfm.201001682

10.1002/pol.1966.110040709

10.1038/nmat2405

10.1039/b719946e

10.1021/ja056923h

10.1002/marc.200900225

10.1063/1.1530720

10.1038/352414a0

10.1002/pol.1981.180191204

10.1002/pol.1981.180191205

10.1002/pol.1983.180211207

10.1007/BF00647793

10.1002/pol.1967.110050209

10.1016/0032-3861(94)90933-4

10.1021/ma901623s

10.1002/adma.200802722

10.1021/ma071390d

Brinkmann M., 2009, L'Actualité Chimique, 326, 31

10.1021/ma101313m

10.1002/adfm.200900966

10.1039/b306630d

10.1021/ma102424e

10.1016/j.tsf.2004.08.155

10.1021/ja054698y

10.1021/ma102529f

10.1021/ma200119s

Thông tin
Thông tin xuất bản

Journal of Polymer Science, Part B: Polymer Physics

Tập 49 Số 17

1218-1233

Thông tin tác giả