Low temperature impact toughness of the main gas pipeline steel after long-term degradation
Tóm tắt
The correlation of microstructure, temperature and Charpy V-notch impact properties of a steel 17G1S pipeline steel was investigated in this study. Within the concept of physical mesomechanics, the dynamic failure of specimens is represented as a successive process of the loss of shear stability, which takes place at different structural/scale levels of the material. Characteristic stages are analyzed for various modes of failure, moreover, typical levels of loading and oscillation periods, etc. are determined. Relations between low temperature derived through this test, microstructures and Charpy (V-notch) toughness test results are also discussed in this paper.
Tài liệu tham khảo
Nykyforchyn H. M., Effect of hydrogen on the kinetics and mechanism of fatigue crack growth in structural steels, Mat Sci, 33, 1997, 504–515
Zagyrski A., Matysiak H., Tsyrulnyk O. T., Zvirko I. I., Nykyforchyn H. M., Kurzydlowski K., Corrosion and stress corrosion cracking of exploited storage tank steel, Mat Sci, 40, 2004, 421–433
Krasovskii A. Ya., Lokhman I. V., Orynyak I. V., Stress-corrosion failures of main pipelines, Strength of Materials, 44, 2012, 129–143
Kotrechko S. O., Krasowsky A. Ya., Meshkov Yu. Ya., Torop V. M., Effect of long-term service on the tensile properties and capability of pipeline steel 17GS to resist cleavage fracture, Int J Press Vess Piping, 81, 2004, 337–344
Nykyforchyn H., Lunarska E., Tsyrulnyk O. et al. Environmentally assisted ‘in-bulk’ steel degradation of long term service gas trunkline, Eng. Failure Analysis, 17, 2010, 624–632
Majid Z. A., Mohsin R. Failure Investigation of natural gas pipeline, Arabian J for Sci. and Eng, 37, 2012, 1083–1088
Pilkey A. K., Lambert S. B., Plumtree A., Stress corrosion cracking of X-60 line pipe steel in a carbonate-bicarbonate solution, Corrosion, 51, 1995, 91–96
Zong C., Zhu G., Mao W., Effect of crystallographic texture on the anisotropy of Charpy impact behavior in pipeline steel, Mater Sci Eng A, 563, 2013, 1–7
Balokhonov R. R., Stefanov Yu. P., Makarov P. V., Smolin I. Yu., Deformation and fracture of surfacehardened materials at meso- and macroscale levels, Theor Appl Fracture Mech, 33, 2000, 9–16
Wang W., Shan Y. Y., Yang K., Study of high strength pipeline steels with different microstructures, Mater Sci Eng A, 502, 2009, 38–44
Maruschak P. O., Bishchak R. T., Vuherer T., Laws governing the dynamic fracture of two-layer bimetallic composites. Metallurgist, 55, 2011, 444–449
Kryzhanivs’kyi E. I., Nykyforchyn H. M., Specific features of hydrogen-induced corrosion degradation of steels of gas and oil pipelines and oil storage reservoirs, Mat Sci, 47, 2011, 127–136
Botvina L. R., Blinov V. M., Tyutin M. R., Bannykh I. O., Blinov E. V., Fracture of high-nitrogen 05Kh20G10N3AMF steel during impact loading. Russian Metallurgy (Metally) 2012, 2012, 239–247
Makarov P. V., Localized deformation and fracture of polycrystals at mesolevel, Theor. Appl. Fracture Mech., 33, 2000, 23–30
Wang J. Q., Atrens A., Cousens D. R., Nockolds C., Bulcock S., Boundary Characterisation of X65 Pipeline Steel Using Analytical Electron Microscopy, J. Mater. Sci., 34, 1999, 1711–1719
Balokhonov R. R., Makarov P. V., Romanova V. A., Smolin I. Yu., Simulation of crystal plasticity under dynamic loading, Comput Mat Sci, 16, 1999, 355–361
Torop V. M., Orynyak I. V., The evaluation of structural strength of pipes and pressure vessels with axial cracks. Int J of Pressure Vessels and Piping, 53, 1993, 159–179
Maruschak P., Baran D., Gliha V., A multiscale approach to deformation and fracture of heatresistant steel under static and cyclic loading. Medžiagotyra, 19, 2013, 29–33