Low temperature diffusion bonding of stainless steel
Tóm tắt
Diffusion bonding of stainless steel (SS) has been attempted in temperature range of 623–773 K using multiple inter-layers of nickel, copper and silver. The intermediate layers were electro-deposited taking care to avoid oxidation at the interfaces. The bonded area was examined for the formation of any intermetallic compound through electron probe micro-analyzer (EPMA) and nano-indentation technique. Results indicate the absence of brittle intermetallics at the interfaces and the strength of the bonding was found to be satisfactory. The bond strength was found to be 130 ± 10 MPa and the bond was found to be leak tight with negligible leak rate.
Tài liệu tham khảo
Khan T I, and Kaczmarczyk N, Proceedings of Intl. Symp. Adv. Mater., Khan, M A, Hussian and Khan A Q, editors. Islamabad, Pakistan, (1999) 19.
Cox M, Carpenter R and Kim M, Metall. Mater. Trans. A, 33(A), (2002) 437.
Ridley N, Salehi M T and Pilling J, J. Mater. Sci. Tech. 8 (1992) 791.
Woo Yeol Kim, Chung Jun Kang and Syoon Park, J. Korean Inst. Met. 29 (1991) 1274.
Jung J P, Kang C S and Lee B Y, J. Korean Inst. Met. 29 (1991) 529.
Naimon E R, Doyle J H, Rice C R, Vigil D and Walmsley D R. Weld. J. 60 (1981) 17 20
Massalski T B, (Ed.). Binary Alloy Phase Diagrams Sec Ed, American Society of Metals, Metals Park Ohio. (1990) 29, 1266 and 1444.
Bhanumurthy K, Krishnan J, Kale G B and Banerjee S, J. Nucl. Mater. 217 (1974) 67.
Bhanumurthy K, Kale G.B, Banerjee S, Krishnan J, Derose D J, Pappachan A L, Grover A K and Totlani M K, Diffusion bonding of aluminum alloys to stainless steel, BARC Report (2001) BARC R-011 30.
Philbert J, Defect Diffusion Forum 66–69 (1989) 995.
Pavlina E J and van Tyne C J, Jl. Mater.Eng.Perf. 17(6) (2008) 888.
Kassener M E, Rosen R S and Henshall G A, Metall. Trans. 21 A, (1990) 3085.
Oliver W C and Pharr GM, J. Mater. Res. 7 (1992) 1564.
Poole W J, Ashby M F, and Fleck N A Scripta Mater. 34 (1996) 559.
Pharr G M, Mater. Sci. Eng. A 253 (1998) 151.
Saha R, Xue Z Huang and Nix W D, J. Mech. Phys. Solids 49 (2001) 1997.
Beegan D, Chowdhury S and Laugier M T, Surf. Coating Tech. 192 (2005) 57.