Ductile failure analysis of API X65 pipes with notch-type defects using a local fracture criterion

International Journal of Pressure Vessels and Piping - Tập 84 Số 8 - Trang 512-525 - 2007
Chang-Kyun Oh1, Yun‐Jae Kim2, Jong-Hyun Baek3, Young Pyo Kim3, Woo‐Sik Kim3
1Korea University
2Department of Mechanical Engineering, Korea University, 5 Ka, Anam-dong, Sungbuk-Ku, Seoul 136 701, Republic of Korea
3Korea Gas Corp.

Tóm tắt

Từ khóa


Tài liệu tham khảo

Cosham, 2004, The effect of dents in pipelines-guidance in the pipeline defect assessment manual, Int J Pressure Vessels Pip, 81, 127, 10.1016/j.ijpvp.2003.11.004

Wilkowski, 2000, Progress in development of acceptance criteria for local thinned areas in pipe and piping components, Nucl Eng Des, 195, 149, 10.1016/S0029-5493(99)00245-9

2000

Kanninnen, 1982

ASME. ASME boiler and pressure vessel code section XI. 1992.

McClintock, 1968, A criterion of ductile fracture by the growth of holes, J Appl Mech, 35, 363, 10.1115/1.3601204

Rice, 1969, On the ductile enlargement of voids in triaxial stress fields, J Phys Mech Solids, 17, 201, 10.1016/0022-5096(69)90033-7

Clausing, 1970, Effect of plastic strain state on ductility and toughness, Int J Fract Mech, 6, 71, 10.1007/BF00183662

Hancock, 1976, On the mechanisms of ductile failure in high-strength steels subject to multi-axial stress states, J Phys Mech Solids, 24, 147, 10.1016/0022-5096(76)90024-7

Gurson, 1977, Continuum theory of ductile rupture by void nucleation and growth—yield criteria and flow rules for porous ductile media, J Eng Mater Technol, 99, 2, 10.1115/1.3443401

Mackenzie, 1977, On the influence of state of stress on ductile failure initiation in high strength steels, Eng Fract Mech, 9, 167, 10.1016/0013-7944(77)90062-5

Ritchie, 1985, On macroscopic and microscopic analyses for crack initiation and crack growth toughness in ductile alloys, Metall Trans A, 16A, 233, 10.1007/BF02816050

Garrison, 1987, Ductile fracture, J Phys Chem Solids, 48, 1035, 10.1016/0022-3697(87)90118-1

Thomason, 1990

Anderson, 1995

Alves, 1999, Influence of hydrostatic stress on failure of axisymmetric notched specimens, J Phys Mech Solids, 47, 643, 10.1016/S0022-5096(98)00060-X

Bao, 2004, On fracture locus in the equivalent strain and stress triaxiality space, Int J Mech Sci, 46, 81, 10.1016/j.ijmecsci.2004.02.006

Bao, 2005, Dependence of ductile crack formation in tensile test on stress triaxiality, stress and strain ratios, Eng Fract Mech, 72, 505, 10.1016/j.engfracmech.2004.04.012

Oh, 2007, Development of stress-modified fracture strain for ductile failure of API X65 steel, Int J Fract, 143, 119, 10.1007/s10704-006-9036-3

American Petroleum Institute. Specification for line pipe. 2000.

Hibbitt, Karlson & Sorensen, Inc. ABAQUS version 6.4 user's manual. 2005.

American Society of Mechanical Engineer. Manual for remaining strength of corroded pipelines. ANSI/ASME B31.G, 1991.

Kiefner JF, Vieth PH. A modified criterion for evaluating the remaining strength of corroded pipe. American Gas Association, Catalog no. L51609, PR3-805. 1989.

Leis BN, Stephens DR. An alternative approach to assess the integrity of corroded line pipe—part I: current status. Part II: alternative criterion. In: Proceedings of the 7th international offshore and polar engineering conference, 1997.

Oh CK, Kim YJ, Baek JH, Kim YP, Kim WS. A micro-mechanical model of ductile fracture for API X65 steels and application to pre-strain effects on deformation and fracture. Int J Mech Sci 2007; in press.