XPS study of passive films formed on an iron—aluminium intermetallic compound in acid solution

Surface and Interface Analysis - Tập 21 Số 6-7 - Trang 435-441 - 1994
S. Frangini1, R. Giorgi1, J. Lascovich1, A. Mignone1
1ENEA CRE Casaccia, Dipartimento Innovazione, Settore Nuovi Materiali, P.O. Box 2400, 00100 Rome, Italy

Tóm tắt

AbstractSurface films grown on the intermetallic B2‐FeAl alloy after wet‐mechanical polishing and after a wide range of anodic polarization conditions in 1N H2SO4 have been analysed by x‐ray photoelectron spectroscopy. The results clearly indicate a remarkable enrichment of aluminium within all the films regardless of the growth conditions. Analysis of the metal–oxygen bonds has made it possible to distinguish several oxidized species. It has been found that most of the iron hydroxides are concentrated on the film surfaces, whereas aluminium hydroxides appear more homogeneously distributed over the depth of the oxide films. The thickness of the film shows an abrupt increase at 1 V, accompanied by a marked increment of Al hydroxide species.

Từ khóa


Tài liệu tham khảo

10.1557/JMR.1991.1779

10.1016/0010-938X(93)90145-7

N.De Cristofaro S.Frangini A.Mignone submitted to Corrosion Science.

N.De Cristofaro S.Frangini R.Giorgi J.Lascovich A.Mignonesubmitted to Corros. Science.

10.1103/PhysRevB.5.4709

10.1002/sia.740180708

10.1002/sia.740151106

10.1002/sia.740030506

10.1016/0368-2048(79)85001-X

10.1016/S0010-938X(77)80002-4

Konno H., 1978, Passivity of Metals, 585

10.1016/0169-4332(88)90076-1

10.1016/S0010-938X(76)80005-4

10.1016/0010-938X(76)90125-6

10.1002/sia.740110403

10.1002/sia.740151108

10.1016/0378-5963(82)90023-X

10.1016/0039-6028(88)90014-3

10.1116/1.571450

10.1016/0039-6028(89)90001-0

10.1016/0169-4332(89)90009-3

10.1016/0010-938X(83)90058-6

10.1016/0013-4686(80)80006-5

10.1002/sia.740010102

10.1016/0368-2048(90)80012-Y

10.1149/1.2069514

Thông tin
Thông tin xuất bản

Surface and Interface Analysis

Tập 21 Số 6-7

435-441

Thông tin tác giả