The effect of bone microstructure on the initiation and growth of microcracks

Journal of Orthopaedic Research - Tập 23 Số 2 - Trang 475-480 - 2005
Fergal J. O’Brien1, David Taylor2, T. Clive Lee1,3
1Department of Anatomy, Royal College of Surgeons in Ireland, 123 St. Stephen's Green, Dublin 2, Ireland
2Dept. of Mechanical and Manufacturing Engineering, Trinity College, Dublin 2 Ireland
3Department of Mechanical and Manufacturing Engineering, Trinity College, Dublin 2, Ireland

Tóm tắt

AbstractOsteonal bone is often compared to a composite material and to metals as discontinuities within the material may provide sites of stress concentration for crack initiation and serve as barriers to crack growth. However, little experimental data exist to back up these hypotheses. Fluorescent chelating agents were applied at specific intervals to bone specimens fatigue tested in cyclic compression at a stress range of 80 MPa. The failed specimens were sectioned and labelled microcracks identified using UV epifluorescence microscopy. Microcrack lengths were measured and their relationship to cement lines surrounding secondary osteons recorded. Microcrack length at the time of encountering a cement line was also measured. Microcracks of less than 100 μm stopped growing when they encountered a cement line. Microcracks of greater than 100 μm in length continued to grow after encountering a cement line surrounding an osteon. Only microcracks greater than 300 μm in length were capable of penetrating osteons and these microcracks were the only ones which were observed to cause failure in the specimen. These experimental data support the hypothesis that secondary osteons act as barriers to crack propagation in compact bone. However, it shows that this microstructural barrier effect is dependent on the crack length at the time of encountering an osteon. For the vast majority of cracks, osteons act as barriers to growth but for the minority of cracks that are long enough and do break through the cement line, an osteon may actually act as a weakness in the bone and facilitate crack propagation. © 2004 Orthopaedic Research Society. Published by Elsevier Ltd. All rights reserved.

Từ khóa


Tài liệu tham khảo

10.1016/S0021-9290(01)00025-2

10.1002/jor.1100160308

10.1016/0021-9290(93)90023-8

10.1016/0021-9290(85)90204-0

10.1016/0021-9290(88)90132-7

10.1016/0021-9290(77)90005-7

Carter DR, 1977, Compact bone fatigue damage: a microscopic examination, Clin Ortho Rel Res, 127, 265

10.1159/000145373

10.1002/jor.1100180222

10.1046/j.1469-7580.2002.00123.x

10.1016/S0142-1123(00)00054-2

10.1016/S8756-3282(99)00241-0

10.1016/S0021-9290(82)80001-8

Martin RB, 1989, The structure, function and adaptation of cortical bone

10.1002/ar.1092420203

10.1046/j.1469-7580.2000.19730413.x

10.1016/S0021-9290(01)00200-7

10.1016/S0021-9290(03)00066-6

10.1007/BF02223298

10.1016/8756-3282(94)90271-2

10.1016/8756-3282(95)00370-3

10.1016/S0021-9290(98)00050-5

10.1016/S0736-0266(01)00009-2

10.1016/S0021-9290(98)00133-X

10.1016/S0021-9290(99)00112-8

10.1243/0954411971534494

10.1016/1350-4533(94)90039-6

Thông tin
Thông tin xuất bản

Journal of Orthopaedic Research

Tập 23 Số 2

475-480

Thông tin tác giả