Synthesis of Nanosized Copper Powder by an Aqueous Route
Tóm tắt
Nanostructured, crystalline copper powder was produced at ambient temperature by aqueous reduction of a copper salt by sodium borohydride. Conditions were optimized to produce boron-free copper powder with an average particle diameter of 200 nm, surface area of 5.48 m * m/g, and oxygent content of 0.155%. The effects of different experimental conditions on average particle size of the powder were also studied. The sintering phenomenon exhibited by produced copper particles at 100°C may be attributed to the low oxygen content of the powder along with other size variation-dependent factors.
Tài liệu tham khảo
R. Birringer, H. Gleiter, H. P. Klein, and P. Markquadrt, Phys. Lett. 102A, 360 (1984).
H. Gleiter, Prog. Mater. Sci. 33, 223 (1989).
R. Sarraf-Mamoory, G. P. Demopoulos, and R. A. L. Drew, Metallurg. Mater. Trans. 27B, 577 (1996).
S. Yatsuya and R. Uyeda, Oyo Buturi (a monthly publication of J. Soc. Appl. Phys.) 142, 1067 (1973).
H. Ishihawa, K. Otsuka, M. Nitta, and Y. Yonehanna, Kawasaki Steel Tech. Report No. 23, Oct. (1990).
G. P. Demopoulos and P. A. Distin, U.S. Patent 4, 541, 861 (1985).
H. Sasaki and T. Nagai, Metall. Rev. MMIG 6, 128 (1989).
G. M. Swinkels, R. M. G. S. Berezowsky, P. Kawulka, C. R. Kirby, G. L. Bolton, D. E. G. Maschmeyer, E. F. G. Milner, and B. M. Parekh, Scherritt-Cominco Process C.I.M. Bull. 71, 105 (1971).
G. S. Whiting, G. L. Bolton, B. R. Sutherland, and B. H. Rosof, Conference on Advances in Powder Metallurgy and Particulate Materials 1993 USA (Metal Powder Indust. Fed., 105 College Rd., East, Princeton, NJ, 1993).
J. Shen, Z. Li, Q. Yan, and Y. Chen, J. Phys. Chem. 97, 8504 (1993).
G. N. Glavee, K. J. Klabunde, C. M. Sorensen, and J. C. Hadjipanayis, Langmuir, 8, 771 (1992).
J. Saida, A. Inoue, and T. Masumoto, Metal Trans. A 22, 2125 (1991).
V. Y. Gertsman and R. Birringer, Scripta Metall. Mater. 30, 577 (1994).
Sherritt Gordons Mines Limited/Specialty Metal Products Canada, Powder Metall. Int. 18, 201 (1986).