Synthesis and photoluminescence properties of MZr2(PO4)3:Eu3+; Bi3+ (M=Na; K) phosphors
Tóm tắt
A series of new red phosphors, MZr2(PO4)3:Eu3+; Bi3+ (M=Na; K), were synthesized using the solidstate reaction method, and their photoluminescence spectra were measured. The MZr2(PO4)3:Eu3+; Bi3+ (M=Na; K) phosphors were efficiently excited by an ultraviolet (UV; 395 nm) source, and showed intense orange-red emission at 595 nm. Further investigation of the concentration-dependent emission spectra indicated that the MZr2(PO4)3:Eu3+; Bi3+ (M=Na; K) phosphors exhibit the strongest luminescence intensity when y = 0.01 in NaZr2(0:95−y)(PO4)3:Eu
0.10
3+
, Bi
2
3+
and y = 0.09 in NaZr2(0.95−y)(PO4)3:Eu
0.10
3+
, Bi
2
3+
, whereas the relative PL intensity decreases with increasing Bi3+ concentration due to concentration quenching. The addition of Bi3+ widens the excitation band of NaZr2(0.95−y)(PO4)3:Eu
0.10
3+
, Bi
2
3+
around 320 nm, which provides the useful idea of broadening the excitation band around 300–350 nm to fit the ultraviolet chip.
Tài liệu tham khảo
X. Xiao, B. Yan, J. Alloy. Compd. 456, 447 (2008)
C. Q. Zhu, S. G. Xiao, J.W. Ding, X. L. Yang, R. F. Qiang, Mater. Sci. Engin. B 150, 95 (2008)
N. Xie, Y. L. Huang, X. B. Qiao, L. Shi, H. J. Seo, Mater. Lett. 64, 1000 (2010)
Y. H. Wang, Y. K. Sun, J. C. Zhang, Z. E. Ci, Z. Y. Zhang, L. Wang, Physica B 403, 2071 (2008)
Z. Wang, H. Liang, M. Gong, Q. Su, Opt. Mater. 29, 896 (2007)
X. Liu, J. Lin, J. Lumin. 122–123, 700 (2007)
V. I. Petkov, A. I. Orlova, O. V. Egorkova, J. Struct. Chem. 37, 933 (1996)
V. I. Petkov, A. I. Orlova, G. N. Kazantsev, S. G. Samoilov, M. L. Spiridonova, J. Therm. Anal. Calorim. 66, 623 (2001)
J. Alamo, R. Roy, J. Mater. Sci. 21, 444 (1986)
Z Wu, J. Shi, J. Wang, M. Gong, Q. Su, J. Solid State Chem. 179, 2356 (2006)
Z. C. Wu, J. Liu, M. L. Gong, Chem. Phys. Lett. 466, 88 (2008)
I. M. Nagpure, S. Saha, S. Dhoble, J. Lumin. 129, 898 (2009)
B. Yan, J. F. Gu, J. Non-Cryst. Solid. 355, 826 (2009)
J. S. Kim, P. E. Jeon, J. C. Choi, H. L. Park, Solid State Commun. 133, 187 (2005)
R. Roy, D. K. Agrawal, J. Alamo, R. A. Roy, Mater. Res. Bull. 19, 471 (1984)
Z. J. Zhang, H. H. Chen, X. X. Yang, J. T. Zhao, G. B. Zhang, C. S. Shi, J. Phys. D: Appl. Phys. 41, 105503 (2008)
M. Hirayama, N. Sonoyama, A. Yamada, R. Kanno, J. Solid State Chem. 182, 730 (2009)
K. R. Reddy, K. Annapurna, S. Buddhudu, Mater. Res. Bull. 31, 1355 (1996)
S. Shionoya, W. M. Yen, Phosphor Handbook, CRC Press, Boca Raton, 1999, pp. 190–191
J.P. Rainho, L.D. Carlos, J. Rocha, J. Lumin. 87–89, 1083 (2000)
Y. Yong, J. Mater. Sci. Lett. 12, 1033 (1993)
J. M. Winand, A. Rulmont, P. Tarte, J. Mater. Sci. 25, 4008 (1990)
Y. H. Wang, C. F. Wu, J. Wei, J. Lumin. 126, 503 (2007)
Z. Xia, D. Chen, M. Yang, T. Ying, J. Phys. Chem. Solids 71, 175 (2010)
H. B. Liang, J. S. Shi, Q. Su, S. Y. Zhang, Y. Tao, Mater. Chem. Phys. 92, 180 (2005)