Syntheses of Disordered and Al-Rich Hydrotalcite-Like Compounds
Tóm tắt
Hydrotalcite-like compounds, [Mg1-xAlx(OH)2]x+ [xX−·n H2O], where X− = ½CO32− or OH−, were prepared by hydrothermal syntheses at
$$P_{H{_2}O}=100\;MPa$$
and T = 100°–350°C. Starting materials were MgO, γ-Al2O3, H2O, and MgC2O4·2H2O. The synthesis depended on temperature, pressure, the Al/(Al + Mg) ratio x, and the CO2 content of the starting material. Previously an Al content of x = 0.33 was thought to be the upper limit in these double-layer compounds, but by using pressure the Al-content was increased to x = 0.44. Up to x = 0.33, a0 decreased linearly to about 3.04 Å, but for x ≥0.33, a0 remained nearly constant at this value. For the synthesized products the layer thickness c’ varied between 7.40 and 7.57 Å in contrast to the natural phases wherein c’ varies from 7.60 to 7.80 Å. At higher temperatures CO2-free syntheses, i.e., those without Mg-oxalate, resulted in a disordered hydrotalcite-like phase. The transition temperature between the ordered and the disordered hydrotalcite-like phase depended on the Al-content, x.
Tài liệu tham khảo
Allmann, R. (1970) Doppelschichtstrukturen mit brucitähnlichen Schichtionen [Me(II)1-xMe(III)x(OH)2]x+: Chimie 24, 99–108.
Allmann, R. and Jepsen, H. P. (1969) Die Struktur des Hydrotalkits: N. Jb. Minéral. Mh. 1969, 544–551.
Brindley, G. W. and Kikkawa, S. (1979) A crystal-chemical study of Mg,Al and Ni,Al hydroxy-perchlorates and hydroxycarbonates: Amer. Mineral. 64, 836–843.
Brindley, G. W. (1980) Lattice parameters and composition limits of mixed Mg,Al hydroxy structures: Mineral. Mag. 43, p. 1047.
Cemÿ, P. (1963) Hydrotalkit z Vezné na zâpadni Morave: Acta Musei Moraviae 48, 23–30.
Feitknecht, W. and Gerber, M. (1942) Zur Kenntnis der Doppelhydroxyde und der basischen Doppelsalze. III. Über Magnesium-Aluminiumdoppelhydroxyd: Helv. Chim. Acta 25, 131–137.
Gastuche, M. C., Brown, G., and Mortland, M. M. (1967) Mixed magnesium-aluminium hydroxides I: Clay Miner. 7, 177–192.
Koritnig, S. and Süsse, P. (1975) Meixnerit, Mg6Al2(OH)18-4H20, ein neues Magnesium-Aluminium Hydroxid-Mineral: Tschermaks Min. Petr. Mitt. 22, 79–87.
Mascolo, G. and Marino, O. (1980) A new synthesis and characterization of magnesium-aluminium hydroxides: Mineral. Mag. 43, 619–621.
Miyata, S. (1980) Physico-chemical properties of synthetic hydrotalcites in relation to composition: Clays & Clay Minerals 28, 50–56.
Roy, D. M., Roy, R., and Osborn, E. F. (1953) The system MgO-Al2O3-H2O and influence of carbonate and nitrate ions on the phase equilibria: Amer. J. Sci. 251, 337–361.
Serna, C. J., Rendon, J. L., and Iglesias, J. E. (1982) Crystalchemical study of layered [Al2Li(OH)6]+ [X-·n H2O]: Clays & Clay Minerals 30, 180–184.
Taylor, H. F. W. (1973) Crystal structures of some double hydroxide minerals: Mineral. Mag. 39, 377–389.