Shape-Controlled Synthesis of Colloidal Platinum Nanoparticles

American Association for the Advancement of Science (AAAS) - Tập 272 Số 5270 - Trang 1924-1925 - 1996
Temer S. Ahmadi1, Zhong Lin Wang2, Travis C. Green1, A. Henglein3, Mostafa A. El‐Sayed1
1T. S. Ahmadi, T. C. Green, M. A. El-Sayed, School of Chemistry and Biochemistry, Georgia Institute of Technology, Atlanta, GA 30332, USA.
2Z. L. Wang, School of Material Sciences and Engineering, Georgia Institute of Technology, Atlanta, GA 30332, USA.
3A. Henglein, Hahn-Meitner Institut, Abteilung Kleinteilchenforschung, 14109 Berlin, Germany.

Tóm tắt

The shapes and sizes of platinum nanoparticles were controlled by changes in the ratio of the concentration of the capping polymer material to the concentration of the platinum cations used in the reductive synthesis of colloidal particles in solution at room temperature. Tetrahedral, cubic, irregular-prismatic, icosahedral, and cubo-octahedral particle shapes were observed, whose distribution was dependent on the concentration ratio of the capping polymer material to the platinum cation. Controlling the shape of platinum nanoparticles is potentially important in the field of catalysis.

Từ khóa


Tài liệu tham khảo

AHMADI T.S. unpublished data.

BRUCHE B, KOLLOID Z 170, 97 (1960).

BRUGGER P.A., ULTRAFINE AND SPECIFIC CATALYSTS AFFORDING EFFICIENT HYDROGEN EVOLUTION FROM WATER UNDER VISIBLE-LIGHT ILLUMINATION, JOURNAL OF THE AMERICAN CHEMICAL SOCIETY 103, 2923 (1981).

CHARLES S.C., FERROMAGNETIC MAT 2, (1980).

CLINT J.H., SYNTHESIS AND CHARACTERIZATION OF COLLOIDAL METAL AND SEMICONDUCTOR PARTICLES PREPARED IN MICROEMULSIONS, FARADAY DISCUSSIONS 95, 219 (1993).

CURTIS A.C., A MORPHOLOGY-SELECTIVE COPPER ORGANOSOL, ANGEWANDTE CHEMIE-INTERNATIONAL EDITION IN ENGLISH 27, 1530 (1988).

DUFF D.G., FORMATION OF A POLYMER-PROTECTED PLATINUM SOL - A NEW UNDERSTANDING OF THE PARAMETERS CONTROLLING MORPHOLOGY, JOURNAL OF PHYSICAL CHEMISTRY 99, 15934 (1995).

HENGLEIN A, ABSORPTION-SPECTRUM AND SOME CHEMICAL-REACTIONS OF COLLOIDAL PLATINUM IN AQUEOUS-SOLUTION, JOURNAL OF PHYSICAL CHEMISTRY 99, 14129 (1995).

HIRAI H, POLYMER-PROTECTED COPPER COLLOIDS AS CATALYSTS FOR SELECTIVE HYDRATION OF ACRYLONITRILE, CHEMISTRY LETTERS: 1047 (1983).

KIRKLAND A.I., ANNU REP PROG CHEM C 87, 247 (1990).

LEFF D.V., THERMODYNAMIC CONTROL OF GOLD NANOCRYSTAL SIZE - EXPERIMENT AND THEORY, JOURNAL OF PHYSICAL CHEMISTRY 99, 7036 (1995).

MILLIGAN W.O., MORPHOLOGY OF COLLOIDAL GOLD - COMPARATIVE STUDY, JOURNAL OF THE AMERICAN CHEMICAL SOCIETY 86, 3461 (1964).

RAMPINO L.D., JOURNAL OF THE AMERICAN CHEMICAL SOCIETY 63, 2745 (1942).

SCHON G, A FASCINATING NEW FIELD IN COLLOID SCIENCE - SMALL LIGAND STABILIZED METAL-CLUSTERS AND THEIR POSSIBLE APPLICATION IN MICROELECTRONICS .2. FUTURE-DIRECTIONS, COLLOID AND POLYMER SCIENCE 273, 202 (1995).

THOMAS J.M., COLLOIDAL METALS - PAST, PRESENT AND FUTURE, PURE AND APPLIED CHEMISTRY 60, 1517 (1988).

TURKEVICH J, DISCUSS FARADAY SOC 11, 55 (1951).