Preparation of new polyelectrolyte/ silver nanocomposites and their humidity-sensitive properties
Tóm tắt
A simple strategy was developed based on polyelectrolyte/silver nanocomposite to obtain humidity-sensitive membranes. The major component of a humid membrane is the polyTEAMPS/silver nanocomposite obtained by thermal heating the mixture of a polyelectrolyte and silver isopropylcarbamate complex. Humidity sensors prepared from polyTEAMPS/silver (w/w=100/0 and 100/6) nanocomposites had an average impedance of 292, 8.83 and 0.86 kΩ, and 5,327, 140 and 0.93 kΩ at 30, 60 and 95% relative humidity (RH), respectively. Hysteresis, temperature dependence and response time were also measured. Activation energies and complex impedance spectroscopy of the various components of the polyelectrolyte/silver nanocomposite films were examined for the humiditysensing membrane.
Tài liệu tham khảo
N. Yamazoe and Y. Shimizu,Sens. Actuat.,10, 372 (1986).
Y. Sakai, Y. Sadaoka, and M. Matsuguchi,Sens. Actuat. B,35, 85 (1996).
Y. Sakai, M. Matsuguchi, Y. Sadaoka, and K. Hirayama,J. Electrochem. Soc.,140, 432 (1993).
Y. Sakai, M. Matsuguchi, and T. Hurukawa,Sens. Actuat. B,66, 135 (2000).
C. W. Lee, H. W. Rhee, and M. S. Gong,Sens. Actuat. B,73, 124 (2001).
H. W. Rhee, M. H. Lee, and M. S. Gong,Sens. Actuat. B,73, 185 (2001).
C. W. Lee, S. W. Joo, B. K. Coi, and M. S. Gong,J. Mater. Sci.,37, 4615 (2002).
C. W. Lee, J. G. Kim, and M. S. Gong,Macromol. Res.,13, 265 (2005).
H. S. Park, C. W. Lee, and M. S. Gong,Macromol. Res.,12, 311 (2004).
H. S. Park, C. W. Lee, J. G. Kim, and M. S. Gong,Macromol. Res.,13, 96 (2005).
P. G. Su, I. C. Chen, and R. J. Wu,Anal. Chim. Acta.,103, 449 (2001).
C. R. Mayer, V. Cabuil, T. Lalot, and R. Thouvenot,Angew. Chem. Int. Ed.,38, 3672 (1999).
A. N. Shipway and I. Willner,Chem. Commun., 2035 (2001).
L. T. Chang and C. C. Yen,J. Appl. Polym. Sci.,55, 371 (1995).
S. Shanmugam, B. Viswanathan, and T. K. Varadarajan,Mater. Chem. Phys.,95, 51 (2005).
W. C. Lin and M.C. Yang,Macromol. Rapid Commun.,26, 1942 (2005).
C. D. Feng, S. L. Sun, H. Wang, C. U. Segre, and J. R. Stetter,Sens. Actuat. B,40, 217 (1997).
P. G. Su and W.Y. Tsai,Sens. Actuat. B,100 407 (2004).
J. Wang, B. Xu, J. Zhang, G. Liu, T. Zhang, F. Qiu, and M. Zhao,J. Mater. Sci. Lett.,18, 1603 (1999).
J. Wang, Q. Lin, T. Zhang, R. Zhou, and B. Xu,Sens. Actuat. B,81, 248 (2002).
J. Wang, B. K. Xu, S. P. Ruan, and S. P. Wang,Mater. Chem. Phys.,78, 746 (2003).
Y. Li, M. J. Yang, and Y. She,Talanta,62, 707 (2004).
R. Alessio, D. B. Dell’Amico, F. Calderazzo, U. Englert, A. Guarini, L. Labella, and P. Strasser,Helv. Chim. Acta.,18, 219 (1998).
D. B. Dell’Amico, F. Calderazzo, L. Labella, F. Marchetti, and G. Pampaloni,Chem. Rev.,103, 3857 (2003).
M. S. Park, T. H. Lim, Y. M. Jeon, J. G. Kim, S. W. Joo, and M. S. Gong,J. Colloid Interface Sci., in press.
A. L. Dearden, P. J. Smith, D.-Y. Shin, N. Reis, B. Derby, and P. O’Brien,Macromol. Rapid Commun.,26, 315 (2005).
O. L. A. Monti, J. T. Fourkas, and D. J. Nesbitt,J. Phys. Chem. B,108, 1604 (2004).
N. Singh and P. K. Khanna,Mater. Chem. Phys.,104, 367 (2007).