Phenylene sulfide polymers. II. Structure of polymers obtained by the Macallum polymerization

Wiley - Tập 43 Số 141 - Trang 167-181 - 1960
Robert W. Lenz1, Carl E. Handlovits1
1Polymer Research Laboratory, The Dow Chemical Company, Midland, Michigan

Tóm tắt

AbstractPolymers prepared by the Macallum homopolymerization and copolymerization were compared to a linear phenylene sulfide polymer prepared by the self‐condensation of sodium p‐chlorothiophenoxide. The properties compared included solubility, softening point, melting point, x‐ray diffraction pattern, infrared spectrum, and thermal stability. For the last named, both differential thermal analyses and thermal gravimetric analyses were obtained. The linear polyphenylene sulfide and the Macallum polymers were found to be essentially identical in all of these properties, even though the sulfur contents ofthe latter were generally higher by 15–20% of the amount present than in the linear polymer. Consideration of this identity and of the probable mechanism of the Macallum polymerization led to the postulation of a structure for the Macallum polymers consisting of a crosslinked core to which are attached more or less extended, linear chains.

Từ khóa


Tài liệu tham khảo

10.1002/pol.1959.1204113828

10.1021/jo01159a020

Macallum A. D. U. S. Pat. 2 513 188 (1950).

Macallum A. D. U. S. Pat. 2 538 941 (1951).

Flory P. J., 1953, Principles of Polymer Chemistry, 376

10.1002/recl.19160350102

Bennett G. M., 1929, Ann. Repts. on Progr. Chem., 26, 132

Rudenko M. G., 1951, Doklady Akad. Nauk. S.S.S.R., 81, 207

Chem. Abstr., 46, 7515d

10.1126/science.109.2838.522

Stockmayer W. H., 1945, Advancing Fronts in Chemistry. I. High Polymers, 69

Thông tin
Thông tin xuất bản

Wiley

Tập 43 Số 141

167-181

Thông tin tác giả