On the internal structure of pressure‐sensitive adhesives

Wiley - Tập 15 Số 2 - Trang 483-500 - 1971
Kazuo Kamagata1, Hideo Kosaka1, Kinnosuke Hino1, Mitsuo Toyama1
1Research Department, Nichiban Co. Ltd., Nerima‐ku, Tokyo, Japan

Tóm tắt

AbstractThe internal structure of pressure‐sensitive adhesives was studied using electron microscopy and measurements of mechanical loss, tensile modulus, viscosity, stress relaxation, and critical surface tension. The adhesives were blends of natural rubber and the pentaerythritol ester of hydrogenated rosin. Compositions containing up to 40 wt‐% resin are homogeneous mixtures. The temperature dispersion of mechanical loss shows a single peak, and the peak value remains almost constant. When the resin concentration exceeds 40 wt‐%, phase separation occurs. The disperse phase is resin containing a small amount of rubber. Two peaks, or a peak and a shoulder, appear in the temperature–loss peak curves. It is postulated that one of the peaks corresponds to the phase in which resin is uniformly dispersed in the rubber and the other peak corresponds to the resin phase which contains a small amount of rubber. Evidence for homogeneity in compositions containing 40 wt‐% or less resin and of heterogeneity at higher concentrations of resin was also obtained from the electron microscope observations. The relationships between the internal structure of pressure‐sensitive adhesives and viscosity, Young's modulus, the relaxation spectrum, tack, and critical surface tension are discussed.

Từ khóa


Tài liệu tham khảo

C. W.Hock J. Polym. Sci. C No. 3 139 (1963).

K.FukuzawaandT.Kosaka Preprints of 6th Symposium on Adhesion and Adhesives Osaka Japan June 5–6 1968 p. 51.

K.FukuzawaandT.Kosaka Preprints of 7th Symposium on Adhesion and Adhesives Tokyo Japan June 3–4 1969 p. 79.

10.1080/00218466908078882

Dahlquist C. A., 1966, Adhesion, Fundamentals and Practices, 143

10.1021/ja01212a028

ASTME 28‐58T Softening Point by Ring and Ball Apparatus Am. Soc. Test. Mater. Philadelphia Pennsylvania 1967.

10.1295/koron1944.23.97

Kamagata K., 1969, J. Adhesion Soc. Japan, 5, 364

Kamagata K., J. Adhesion

10.1021/ba-1964-0043.ch001

10.2324/gomu.24.298

Fukuzawa K., 1968, J. Adhesion Soc. Japan, 4, 249

10.1002/pol.1950.120050507

Bull R. F., 1968, Adhesive Age, 20

10.1002/app.1969.070130310

Dahlquist C. A., 1969, Aspects of Adhesion, 183

Thông tin
Thông tin xuất bản

Wiley

Tập 15 Số 2

483-500

Thông tin tác giả