Low Carbon Concrete Prepared with Scattering-Filling Coarse Aggregate Process
Tóm tắt
The volume fraction of the coarse aggregate in the conventional plastic concrete is controlled relatively low to ensure a required workability. In this paper, a new type of coarse aggregate interlocking concrete with strength ranging from C30 to C80 was prepared with scattering-filling aggregate process. The strength of concrete prepared with this method increases obviously whereas the shrinkage decreases significantly, the cement dosage in the concrete decreased 20 % at the same time. The micro-hardness of the ITZ between the cement paste and scattering-filling aggregate is higher than that of the original aggregate, the ITZ become narrower and tighter also. The interlocking and more even distribution of the coarse aggregate and the water absorption of the addition of extra amount of coarse aggregates contribute to the strength and performance improvement of the concrete prepared with scattering-filling aggregate process.
Tài liệu tham khảo
Alexanderson, J. (1971). The influence of the properties of cement and aggregates on the consistency of concrete. Proceedings RILEM Seminar,23(2), 12–22.
Beshr, H., Almusallam, A. A., & Maslehuddin, M. (2003). Effect of coarse aggregate quality on the mechanical properties of high strength concrete. Construction and Building Materials,17(2), 97–103.
Beste, U., & Jacobson, S. (2003). Micro scale hardness distribution of rock types related to rock drill wear. Wear,254(5), 1147–1154.
Counto, U. J. (1964). The effect of elastic modulus of the aggregate on the elastic modulus, creep and creep recovery of concrete. Magazine of Concrete Research,16(2), 129.
Hirsch, T. J. (1962). Modulus of elasticity of concrete affected by elastic module of cement paste matrix and aggregate. ACI Materials Journal,59(3), 427–451.
Mehta, P. K. (1999). Concrete technology for sustainable development. Concrete International,21(11), 47–53.
Mehta, P. K., & Monteiro, P. J. M. (1993). Concrete: Microstructure, properties, and materials. New York, NY: McGraw-Hill.
Mindess, S., Young, J. F., & David, D. (2003). Concrete (2nd ed.). New Jersey, NJ: Pearson Education Inc.
Mizuguchi, H. (1998). A review of environmentally friendly concrete. Concrete International,36(1), 9–12.
Nadeau, J. C. (2003). A multiscale model for effective module of concrete incorporating ITZ water–cement ratio gradients, aggregate size distributions, and entrapped voids. Cement and Concrete Research,33(1), 103–113.
Neville, F. M. (1981). Properties of concrete. London, UK: Pitman publishing limited.
Nilsen, A. U., & Monteiro, P. J. M. (1993). Concrete: A three phase material. Cement and Concrete Research,23(2), 147–151.
Özturan, T., & Çeçen, C. (1997). Effect of coarse aggregate type on mechanical properties of concretes with different strengths. Cement and Concrete Research,27(2), 165–170.
Ping, X., & Beaudoin, J. J. (1992). Effects of transition zone microstructure on bond strength of aggregate portland cement paste interfaces. Cement and Concrete Research,22(1), 23–26.
Van Oss, H. G., & Padovani, A. C. (2003). Cement manufacture and the environment, Part II: environmental challenges and opportunities. Journal of Industrial Ecology,7(1), 93–126.
Shen, W., Dong, R., Li, J., et al. (2010a). A study on the coarse aggregate interlocking concrete. Construction and building material,24(11), 2312–2316.
Shen W, Cai Z, Zhou M. High strength coarse aggregate interlocking concrete: preparation and properties, 8th International symposium on Utilization of High-Strength and High Performance Concrete (fib), 2008, Tokyo, Japan, 188–192.
Shen, W., Zhang, T., Zhou, M., et al. (2010b). Investigation on the scattering-filling coarse aggregate self-consolidating concrete. Materials and Structures,43(10), 1343–1350.
Stock, A. F., Hannant, D. J., & Williams, R. I. T. (1979). The effect of aggregate concentration upon the strength and modulus of elasticity of concrete. Magazine of Concrete Research,31(2), 225–234.