Hydrophobicity Improvement of Cement-Based Materials Incorporated with Ionic Paraffin Emulsions (IPEs)
Tóm tắt
Cement-based materials are non-uniform porous materials that are easily permeated by harmful substances, thereby deteriorating their structural durability. In this work, three ionic paraffin emulsions (IPEs) (i.e., anionic paraffin emulsion (APE), cationic paraffin emulsion (CPE), and non-ionic paraffin emulsion (NPE), respectively) were prepared. The effects of incorporation of IPEs into cement-based materials on hydrophobicity improvement were investigated by environmental scanning electron microscopy (ESEM), Fourier transform infrared (FTIR) spectroscopy, transmission and reflection polarizing microscope (TRPM) tests and correlation analyses, as well as by compressive strength, impermeability, and apparent contact angle tests. Finally, the optimal type and the recommended dose of IPEs were suggested. Results reveal that the impermeability pressure and apparent contact angle value of cement-based materials incorporated with IPEs are significantly higher than those of the control group. Thus, the hydrophobicity of cement-based materials is significantly improved. However, IPEs adversely affect the compressive strength of cement-based materials. The apparent contact angle mainly affects impermeability. These three IPEs impart hydrophobicity to cement-based materials. In addition, the optimal NPE dose can significantly improve the hydrophobicity of cement-based materials.
Từ khóa
Tài liệu tham khảo
Zheng, 2019, Application of a capillary crystalline material to enhance cement grout for sealing tunnel leakage, Constr. Build. Mater., 214, 497, 10.1016/j.conbuildmat.2019.04.095
Azarsa, P., Gupta, R., and Biparva, A. (2020). Inventive Microstructural and Durability Investigation of Cementitious Composites Involving Crystalline Waterproofing Admixtures and Portland Limestone Cement. Materials, 13.
Min, 2018, Investigation on the Sulfuric Acid Corrosion Mechanism for Concrete in Soaking Environment, Adv. Mater. Sci. Eng., 2018, 1, 10.1155/2018/3258123
Wang, 2018, Improving cracking resistance of cement mortar by thermo-sensitive poly N-isopropyl acrylamide (PNIPAM) gels, J. Clean. Prod., 176, 1292, 10.1016/j.jclepro.2017.11.242
Hu, 2019, Effects of polypyrrole coated rebar on corrosion behavior of tunnel lining with the combination effect of sustained loading and pre-existing cracks when exposed to chlorides, Constr. Build. Mater., 221, 318, 10.1016/j.conbuildmat.2019.06.092
He, 2020, Thermal and Mechanical Properties of Geopolymers Exposed to High Temperature: A Literature Review, Adv. Civ. Eng., 2020, 1
Bušić, R., Benšić, M., Miličević, I., and Strukar, K. (2020). Prediction Models for the Mechanical Properties of Self-Compacting Concrete with Recycled Rubber and Silica Fume. Materials, 13.
Liu, 2017, Superhydrophobic and self-cleaning behavior of Portland cement with lotus-leaf-like microstructure, J. Clean. Prod., 156, 775, 10.1016/j.jclepro.2017.03.211
Wang, 2020, A superhydrophobic coating to create multi-functional materials with mechanical/chemical/physical robustness, Chem. Eng. J., 381, 122539, 10.1016/j.cej.2019.122539
He, 2020, Damage mechanism and interfacial transition zone characteristics of concrete under sulfate erosion and Dry-Wet cycles, Constr. Build. Mater., 255, 119340, 10.1016/j.conbuildmat.2020.119340
Wang, 2020, Adhesion Improvement between RAP and Emulsified Asphalt by Modifying the Surface Characteristics of RAP, Adv. Mater. Sci. Eng., 2020, 1, 10.1155/2020/6563520
Izarra, 2019, A hydrophobic release agent containing SiO2-CH3 submicron-sized particles for waterproofing mortar structures, Constr. Build. Mater., 199, 30, 10.1016/j.conbuildmat.2018.12.018
Li, 2020, Effect of granulated blast furnace slag on the self-healing capability of mortar incorporating crystalline admixture, Constr. Build. Mater., 239, 117818, 10.1016/j.conbuildmat.2019.117818
Hua, W., Kar, P., Roy, P., Bu, L., Shoute, L.C.T., Kumar, P., and Shankar, K. (2018). Resistance of Superhydrophobic Surface-Functionalized TiO2 Nanotubes to Corrosion and Intense Cavitation. Nanomaterials, 8.
Liu, J., Janjua, Z.A., Roe, M., Xu, F., Turnbull, B., Choi, K.-S., and Hou, X. (2016). Super-Hydrophobic/Icephobic Coatings Based on Silica Nanoparticles Modified by Self-Assembled Monolayers. Nanomaterials, 6.
Vogel, 2017, Static response of double shell concrete lining with a spray-applied waterproofing membrane, Tunn. Undergr. Space Technol., 68, 106, 10.1016/j.tust.2017.05.022
Li, 2018, Design of SiO2/PMHS hybrid nanocomposite for surface treatment of cement-based materials, Cem. Concr. Compos., 87, 89, 10.1016/j.cemconcomp.2017.12.008
Feng, 2019, Integral hydrophobic concrete without using silane, Constr. Build. Mater., 227, 116678, 10.1016/j.conbuildmat.2019.116678
Zhu, 2013, Influence of silane-based water repellent on the durability properties of recycled aggregate concrete, Cem. Concr. Compos., 35, 32, 10.1016/j.cemconcomp.2012.08.008
Ministry of Housing and Urban-Rural Development of the People’s Republic of China (2009). Standard for Test Method of Basic Properties of Construction Mortar, JGJ/T 70-2009, China Architecture & Building Press.
Wang, 2020, Laboratory investigation on effects of microwave heating on early strength of cement bitumen emulsion mixture, Constr. Build. Mater., 236, 117439, 10.1016/j.conbuildmat.2019.117439
Zhenjun, 2020, Early-stage road property improvements of cold recycled asphalt emulsion mixture with microwave technology, J. Clean. Prod., 263, 121451, 10.1016/j.jclepro.2020.121451
Deng, 2018, Inversely designed micro-textures for robust Cassie–Baxter mode of super-hydrophobicity, Comput. Methods Appl. Mech. Eng., 341, 113, 10.1016/j.cma.2018.06.034