Effects of fly ash addition on physical properties of porous clay-fly ash composites via polymeric replica technique
Tóm tắt
The porous composites of clay and fly ash have the potential to be used in many fields, such as catalyst support and gas adsorbents. In this study, various ratios of fly ash (1–2) with different percentage of suspension (50–70 wt%) were applied to produce porous clay-fly ash composites via polymeric replica technique. Fabrication process starts by mixing clay and fly ash in distilled water to form slurry. The process is followed by fully immersing polymer sponge in slurry. The excess slurry is then removed through squeezing. Finally, the sponge coated with slurry is sintered at 500 and 1250 °C for 1 h. It is found that the compressive strength of porous composites improves significantly (0.178–1.28 MPa) when the amount of clay-fly ash suspension mixture (50–70 wt%) increases. The compressive strength of porous composites is mainly attributed to the mullite, quartz and amorphous phase formations. These results are supported by X-ray diffraction analysis. On the other hand, increase in the amount of suspension reduces the apparent density (from 2.44 to 2.32 g/cm3) and porosity (from 97 to 85 %). The reduction in apparent density is believed to be caused by the presence of high fly ash content in porous composites. The melted fly ash cenospheres have closed the internal pores and increased density of samples. Higher suspension level not only reduces porosity, but also increases close pores of the porous composites. The results are justified through the observation from the structures of porous clay-fly ash composites.
Tài liệu tham khảo
Colombo P (2006) Conventional and novel processing methods for cellular ceramics. Philo Trans R Soc A 364:109. doi:10.1098/rsta.2005.1683
Petrasch J, Meier F, Meier H, Friess H, Steinfeld A (2008) Int J Heat Fluid Fl 29:315. doi:10.1016/j.ijheatfluidflow.2007.09.001
Ackermann S, Scheffe JR, Duss J, Steinfeld A (2014) Materials 7:7173. doi:10.3390/ma7117173
Damoah LNW, Zhang L (2011) Acta Metall. 59:896. doi:10.1016/j.actamat.2010.09.064
Emmel M, Aneziris CG (2012) Ceram Int 38:5165. doi:10.1016/j.ceramint.2012.03.022
Faure R, Rossignol F, Chartier T, Bonhomme C et al (2011) J Eur Ceram Soc 31:303. doi:10.1016/j.jeurceramsoc.2010.10.009
Thompson CR, Marín P, Díez FV, Odóñez S (2013) Chem Eng J 221:44. doi:10.1016/j.cej.2013.01.080
Lo YW, Wei WCJ, Hsueh CH (2011) Mater Chem Phys. 129:326. doi:10.1016/j.matchemphys.2011.04.023
Zhang R, Feng J, Cheng X, Gong L, Li Y, Zhang H (2014) Energ Buildings 81:262. doi:10.1016/j.enbuild.2014.06.028
Schwartzwalder K, Arthur VS (1963) Patent US3090094. May 21
Muhamad Nor MAA, Lee CH, Ahmad ZA, Md Akil H (2008) J Mater Process Technol 207:235. doi:10.1016/j.jmatprotec.2007.12.099
Binner J, in Cellular Ceramics: Structure, Manufacturing, Properties and Applications, eds. by M. Scheffler, P. Colombo (Wiley-VCH, Weinheim, 2005)
Del-Gallo P, Cornillac M, Rossignol F, Faure R, Chartier T, Gary D (2011) Patent US20110097259 A1. April 28
Lee JH, Choi HJ, Yoon SY, Kim BK, Park HC (2013) J Porous Mater 20:219. doi:10.1007/s10934-012-9591-0
Kim KH, Yoon SY, Park HC (2014) Materials 7:5982. doi:10.3390/ma7085982
Qian H, Cheng X, Zhang H, Zhang R, Wang YH (2014) Int J App Ceram Technol 11:858. doi:10.1111/ijac.12204
Bowen NL, Greig JW (1924) J. Amer. Soc. 7:238. doi:10.1111/j.1151-2916.1924.tb18190.x
Jung JS, Park HC, Stevens R (2001) J Mater Sci Lett 20:1089. doi:10.1023/A:1010934728570
Souto PM, Menezes RR, Kiminami RHGA (2009) J Mater Process Technol 209:548. doi:10.1016/j.jmatprotec.2008.02.029
Anggono J (2005) Jurnal Teknik Mesin 7:1
Souto A, Guitian F, Aza S (1999) J Am Ceram Soc 82:2660. doi:10.1111/j.1151-2916.1999.tb02138.x
Chmielarz L, Kuśtrowski P, Piwowarska Z, Dudek B, Gil B, Michalik M (2009) Appl Catal B Environ 88:331. doi:10.1016/j.apcatb.2008.11.001
Bineesh KV, Kim DK, Kim MI, Park DW (2011) Appl Clay Sci 53:204. doi:10.1016/j.clay.2010.12.022
Pinto ML, Marques J, Pires J (2012) Sep Purif Technol 98:337. doi:10.1016/j.seppur.2012.07.003
Sarkar S, Bandyopadhyay S, Larbot A, Cerneaux S (2012) J. Membr. Sci. 392–393:130. doi:10.1016/j.memsci.2011.12.010
Sengphet KKD, K. Pasomsouk, T. Sato, M.N. Ahmad Fauzil, Radzali O (2013) Int J Sci Res Pub 3:1
Görhan G, Şimşek O (2013) Constr Build Mater 40:390. doi:10.1016/j.conbuildmat.2012.09.110
Koseonglu K, Polat M, Polat H (2010) J Hazard Mater 176:957. doi:10.1016/j.jhazmat.2009.11.133
Zhang HY, Zhao YC, Qi JY (2011) Waste Manage 31:331. doi:10.1016/j.wasman.2010.10.017
El-Didamony H, El-Rahman EA, Osman RM (2012) Ceram Int 38:201. doi:10.1016/j.ceramint.2011.06.050
Sukmak P, Horpibulsuk S, Shen SL, Chindaprasirt P, Suksiripattanapong C (2013) Constr Build Mater 47:1125. doi:10.1016/j.conbuildmat.2013.05.104
Sukmak P, Horpibulsuk S, Shen SL (2013) Constr Build Mater 40:566. doi:10.1016/j.conbuildmat.2012.11.015
Phetchuay C, Horpibulsuk S, Suksiripattanapong C, Chinkulkijniwat A, Arulrajah A, Disfani MM (2014) Constr Build Mater 69:285. doi:10.1016/j.conbuildmat.2014.07.018
Jamaludin AR, Kasim SR, Abdullah MZ (2014) Zainal A. Ahmad. Ceram Int 40:4777. doi:10.1016/j.ceramint.2013.09.023
Jovanovic M, Volkov-Husovic T (2012) Sci Sinter 44:161–168. doi:10.2298/SOS1202161J
ASTM International (2012) ASTM C 618-12 Standard specification for coal fly ash and raw or calcined natural pozzolan for use in concrete, United States.
Chinese National Standard (1996) GB/T 1964-1996 Test method for crushing strength of porous ceramic. GB/T, Beijing
Schneider H, Okada K, Pask J (1994) Mullite and Mullite Ceramics. Wiley, Chichester, pp 83–104
Schairer JF, Bowen NL (1955) Amer. J. Sci. 253:681. doi:10.2475/ajs.253.12.681
Muan A (1957) J Am Ceram Soc 40:121. doi:10.1111/j.1151-2916.1957.tb12588.x
Snow RB (1943) J. Europe. Ceram. Soc. 2:11. doi:10.1111/j.1151-2916.1943.tb15177.x
Cangemi JM, Claro Neto S, Chierice GO, Santos AM (2006) Polímeros, 16:129. doi: 10.1590/S0104-14282006000200013
Trovati G, Sanches SA, Neto SC, Mascarenhas YP, Chierice GO (2010) J Appl Polymer Sci 115:263. doi:10.1002/app.31096
Monash P, Niwas R, Pugazhenthi G (2011) Clean Technol Environ. Policy 13:141. doi:10.1007/s10098-010-0292-6
Souza AE, Teixeira SR, Santos GTA, Longo E (2013) Ceramica 59:147. doi:10.1590/S0366-69132013000100017
Murray HH (2007) Applied clay mineralogy: occurances, processing and applications of kaolins. Elsevier, Kidlington, pp 85–110
Gabal MA, Hoff D, Kasper G (2007) J. Therm. Anal. Calorim. 89:109. doi:10.1007/s10973-005-7494-x
Ferrari S, Belevi H, Baccini P (2002) Waste Manage 22:303. doi:10.1016/S0956-053X(01)00049-6
Rocca S, van Zomeren A, Costa G, Dijkstra JJ, Comans RNJ, Lombardi F (2013) Waste Manage 33:373. doi:10.1016/j.wasman.2012.11.004
Paya J, Monzo J, Borrachero MV, Perris E, Amahjour F (1998) Cement Concrete Res 28:675. doi:10.1016/S0008-8846(98)00030-1
Liu KC, Thomas G, Caballero A, Moya JS, de Aza S (1994) J Am Ceram Soc 77:1545. doi:10.1111/j.1151-2916.1994.tb09755.x
Sultana P, Das S, Bagchi B, Bhattacharya A, Basu R, Nandy P (2011) Bull Mater Sci 34:1663. doi:10.1007/s12034-011-0374-z
Nour WMN, Awad HM (2008) J Aust Ceram Soc 44:27
Kumar S, Singh KK, Ramachandrarao P (2001) J Mater Sci 36:5917. doi:10.1023/A:1012936928769
Rajamannan B, Kalyana C (2013) Sundaram, G. Viruthagiri, N. Shanmugam. Int J Latest Sci Technol 2:486
Dong YC, Diwu J, Feng XF, Feng XY, Liu XQ, Meng GY (2008) J Alloys Compd 460:651. doi:10.1016/j.jallcom.2007.06.043
Dong YC, Hampshire S, Zhou JE, Jin ZL, Wang JD, Meng GY (2011) J Europe Ceram Soc 31:687. doi:10.1016/j.jeurceramsoc.2010.12.012
Rohatgi PK, Menzes PL, Lovell MR (2012) In: By M. Nosonovsky, B. Bhushan (eds) Green Tribology, Green Energy and Technology. Springer, Berlin. p 429
Zhao Y, Wang C, Xu H, Liu J (2012) Adv Mater Res 415–417:1038. doi:10.4028/www.scientific.net/AMR.415-417.1038
Shao YF, Jia DC, Liu BY (2009) J Eur Ceram Soc 29:1529. doi:10.1016/j.jeurceramsoc.2008.09.012
Wang CF, Liu JC, Du HY (2012) A Guo 38:4395. doi:10.1016/j.ceramint.2012.01.044
Montanaro J, Jorand Y et al (1998) J Eur Ceram Soc 18:1339. doi:10.1016/S0955-2219(98)00063-6
Han YS, Li JB, Chen YJ (2003) Mater Res Bull 38:373. doi:10.1016/S0025-5408(02)01026-7
Akpinar S, Altun IA, Onel K (2010) J Europe Ceram Soc 30:2727. doi:10.1016/j.jeurceramsoc.2010.05.005
Liu P, Chen GF (2014) Porous materials: processing and applications. Elsevier, Kidlington, pp 221–302
Guo Y, Zhang Y, Huang H, Meng K, Hu K, Hu P (2014) Ceram Int 40:6677. doi:10.1016/j.ceramint.2013.11.128