Controlling the anodizing conditions in preparation of an nanoporous anodic aluminium oxide template
Tóm tắt
Porous anodic aluminium oxide (AAO) template is commonly used in the synthesis of one-dimensional nanostructures, such as nanowires and nanorods, due to its simple fabrication process. Controlling the anodizing conditions is important because of their direct influence on the size of AAO template pores; it affects the size of nanostructures that are fabricated in AAO template. In present study, several alumina templates were fabricated by a two-step electrochemical anodization in different conditions, such as the time of first process, its voltage, and electrolyte concentration. The effect of these factors on pore diameters of AAO templates was investigated using scanning electron microscopy (SEM).
Tài liệu tham khảo
Li X., Ling X., Sun L., Liu L., Zeng D., Zheng Q., Compos. Part B-Eng., 43 (2012), 70.
Zhang J.M., Wang X.-C., Zhang Y., Xu K.W., Comput. Theor. Chem., 963 (2011), 273.
Wedekind S., Donati F., Oka H., Rodary G., Sander D., Kirschner J., Surf. Sci., 606 (2012), 1577.
Chen H., Shi D., Qi J., Jia J., Wang B., Phys. Lett. A, 373 (2009), 371.
Ma C., Zhu L., Chen S., Zhao Y., Mater. Lett., 108 (2013), 114.
Yousefi R., Jamali-Sheini F., Khorsand Zak A., Azarang M., Ceram. Int., 39 (2013), 5191.
Chen J., Wang Y., Deng Y., J. Alloy. Compd., 552 (2013), 65.
Sáaedi A., Yousefi R., Jamali-Sheini F., Cheraghizade M., Khorsand Zak A., Huang N.M., Superlattice. Microst., 61 (2013), 91.
Hadia N.M.A., Mohamed H.A., J. Alloy. Compd., 547 (2013), 63.
Yu C., Zhang X., Leng M., Shaga A., Liu D., Chen F., Wang C., J. Alloy. Compd., 570 (2013), 86.
Yuan G., Li Y., Bao N., Miao J., Ge C., Wang Y., Mater. Chem. Phys., 143 (2014), 587.
Tan X. J., Liu H. J., Wei J., Shi J., Tang X. F., Uher C., Carbon, 53 (2013), 286.
Liu Y.B., Zhou S.M., Yuan X.Y., Lou S.Y., Gao T., Shi X.J., Wu X.P., Mater. Lett., 84 (2012), 116.
Maleak N., Potpattanapol P., Bao N.N., Ding J., Wongkokuo W., Tang I. M., Thongmee S., J. Magn. Magn. Mater., 354 (2014), 262.
Ma X., Thin Solid Films, 520 (2012), 5752.
Ramulu T.S., Venu R., Anandakumar S., Rani V.S., Yoon S.S., Kim C.G., Thin Solid Films, 520 (2012), 5508.
Senthilkumaar S., Thamiz Selvi R., Ganapathy Subramaniam N., Kang T.W., Superlattice. Microst., 51 (2012), 73.
Garabagiu S., Mihailescu G., Mater. Lett., 65 (2011), 1648.
Zhang J., Kielbasa J.E., Carroll D.L., Mater. Chem. Phys., 122 (2010), 295.
Manzano C.V., Martín J., Martín-González M.S., Micropor. Mesopor. Mat., 184 (2014), 177.
Wang H.J., Zou C.W., Yang B., Lu H.B., Tian C.X., Yang H.J., Li M., Liu C.S., Fu C.S., Liu J.R., Electrochem. Commun., 11 (2009), 2019.
Ishrat S., Maaz K., Joon Lee K., Jung M.H., Kim G.H., J. Solid State Chem., 199 (2013), 160.
Saedi A., Ghorbani M., Mater. Chem. Phys., 91 (2005), 417.
Ju H., Lee J. K., Lee J., Lee J., Curr. Appl. Phys., 12 (2012), 60.
Chang M., Cao X.L., Xu X.J., Zhang L., Phys. Lett. A, 372 (2008), 273.
Xu D., Xu Y., Chen D., Guo G., Gui L., Tang Y., Chem. Phys. Lett., 325 (2000), 340.
Thongmee S., Pang H.L., Ding J., Lin J.Y., J. Magn. Magn. Mater., 321 (2009), 2712.
Yang W., Wu Z., Lu Z., Yang X., Song L., Microelectron. Eng., 83 (2006), 1971.
Fu J., Cherevko S., Chung C.H., Electrochem. Commun., 10 (2008), 514.
Peng X.S., Meng G.W., Zhang J., Wang X.F., Zhao L.X., Wang Y.W., Zhang L.D., Mater. Res. Bull., 37 (2002), 1369.
Michalska-Domańska M., Norek M., Stpniowski W.J., Budner B., Electrochim. Acta, 105 (2013), 424.
Masuda H., Fukuda K., Science, 268 (1995), 1466.
Chung C.K., Liao M.W., Chang H.C., Lee C.T., Thin Solid Films, 520 (2011), 1554.
Belwalkar A., Grasing E., Geertruyden Van W., Huang Z., Misiolek W.Z., J. Membrane Sci., 319 (2008), 192.