Channel cracking during thermal cycling of thin film multi-layers
Tóm tắt
This paper describes mechanisms that can lead to film channel cracking, even in scenarios when layer thickness is small. Computational models are used to illustrate conditions that lead to the introduction of channel cracks and their subsequent cycle- or time-dependent propagation. Results for elastic structures with periodic features are briefly reviewed to illustrate that small low-modulus sections promote cracking in adjacent layers because they allow for the release of strain energy in adjacent sections with high residual stress. Inelastic deformation in layers adjacent to the cracked layer may also act to increase the channel crack driving force, by allowing for increasing displacements that serve to release strain energy. Two inelastic mechanisms form the primary focus in this effort: rate-independent plasticity and creep. Analyses of a cracked film on an elastic-plastic layer reveal pronounced cyclic displacements (as known as ratcheting) when the misfit thermal strain amplitude in the ductile layer exceeds twice its yield strain. Similar behavior occurs in cracked films on layers susceptible to creep. Simulations are presented for both isolated cracks and periodic arrays of cracks, and illustrate that the likelihood of cracking grows dramatically with time. In both inelastic regimes, the upper limit on deformation is dictated by the residual stress in the elastic layer and the substrate dimensions. These results are discussed in the context of analytical models developed elsewhere and potential experiments.
Tài liệu tham khảo
Ambrico, J.M. and Begley, M.R. (2002). The role of initial flaw size and plasticity in adjacent layers in channeling crack growth in thin films. Thin Solid Films 419, 144–153.
Ambrico, J.M., Jones, E.E. and Begley, M.R. (2001). Cracking in thin multilayers with finite-width and periodic architectures. International Journal of Solids and Structures 39, 1443–1462.
Begley, M.R. and Evans, A.G. (2001). Progressive cracking in a multi-layer system upon thermal cycling. Journal of Applied Mechanics 68, 513–520.
Beuth, J.L. and Klingbeil, J.W. (1996). Cracking of thin films bonded to elastic plastic substrates. Journal of the Mechanics and Physics of Solids 44, 1411–1428.
Beuth, J.L. (1992). Cracking of thin bonded films in residual tension. International Journal of Solids and Structures 29, 1657–1675.
Huang, M. Suo, Z. Ma, Q., and Fujimoto, H. (2000). Thin film cracking and ratcheting caused by temperature cycling. Journal of Materials Research 15, 1239–1242.
Huang, M., Suo, Z. and Ma, Q. (2001). Metal film crawling in interconnected structures caused by cyclic temperatures. Acta Materialia 49, 3039–3049.
Huang, M., Suo, Z. and Ma, Q. (2002). Plastic ratcheting induced cracks in thin film structures. Journal of the Mechanics and Physics of Solids 50, 1079–1098.
Hutchinson, J.W. and Suo, Z. (1992). Mixed mode cracking in layered materials. Advances in Applied Mechanics 29, 63–191.
Hu, M.S. and Evans, A.G. (1989). The cracking and decohesion of thin films on ductile substrates. Acta Metallurgica et Materialia 37, 917–925.
Liu, X.H., Suo, Z., Ma, Q. and Fujimoto, H. (2000). Developing design rules to avert cracking and debonding in integrated circuit structures. Engineering Fracture Mechanics 66, 387–402.
Maier, G. (2001). Low-dielectric constant polymers for microelectronics. Progress in Polymer Science 26, 3–65.
Weiss, D., Gao, H. and Arzt, E. (2001). Constrained diffusional creep in UHV-produced copper thin films. Acta Materialia 49, 2395–2403.