Carbonization behavior of polyimide films with various chemical structures

Wiley - Tập 44 Số 3 - Trang 521-525 - 1992
Michio Inagaki1, Tsutomu Ibuki2, Tsutomu Takeichi2
1Faculty of Engineering, Hokkaido University, Kita‐ku, Sapporo 060, Japan
2Materials Science, Toyohashi University of Technology, Tempaku-cho, Toyohashi, 441 Japan

Tóm tắt

AbstractSix kinds of polyimide films with different molecular structures were synthesized and carbonized up to 1100°C. The carbonization behavior of polyimides was followed by measuring the changes in weight, size, and electrical conductivity. Pyrolysis gases evolved on the way to carbonize up to 1000°C were analyzed by gas chromatography.All films showed appreciable shrinkage and became a black color above 500°C. No cracks and pores were observed on the films heated up to 1100°C, even under the scanning electron microscope. A large weight decrease of 35–50% was observed in a narrow temperature range from 500 to 650°C, which seemed to be due to the departure of CO groups as either CO or CO2. An additional weight decrease occurred gradually above 800°C, due to N2 departure. A remarkable increase of electrical conductivity along the film surface, more than 2 orders, was observed with the increase in heat‐treatment temperature. The polyimide film with a flat molecular structure (PMDA/PPD) gave the highest conductivity: 3.7 × 102S/cm.

Từ khóa


Tài liệu tham khảo

10.1002/pen.760220103

Hergenrother P. M., 1984, CHEMTECH, 496

10.1002/pol.1976.230110105

Scola D. A., 1986, 31st National SAMPE Symposium, 31, 1844

10.1295/polymj.19.73

10.1016/0008-6223(75)90225-0

10.1007/BF00551305

M.Inagaki L. J.Meng T.Ibuki andY.Hishiyama Carbon to appear.

Y.HishiyamaandM.Inagaki J. Mater. Res. to appear.

10.1016/0022-3093(69)90026-X

10.7209/tanso.1987.68

10.1002/app.1985.070301116

10.1002/app.1988.070350502

10.1016/0008-6223(89)90131-0

10.1557/JMR.1991.1108

Thông tin
Thông tin xuất bản

Wiley

Tập 44 Số 3

521-525

Thông tin tác giả