An application for the fracture characterisation of quasi-brittle materials taking into account fracture process zone influence

Advances in Engineering Software - Tập 72 - Trang 66-76 - 2014
V. Veselý1,2, P. Frantík1
1Brno University of Technology, Faculty of Civil Engineering, Institute of Structural Mechanics, Brno, Czech Republic
2VŠB – Technical University of Ostrava, Faculty of Civil Engineering, Department of Structural Mechanics, Ostrava, Czech Republic

Tài liệu tham khảo

Anderson, 2004

Ayatollahi, 2012, Size effects on fracture toughness of quasi-brittle materials–a new approach, Eng Fract Mech, 92, 89, 10.1016/j.engfracmech.2012.06.005

Ayatollahi, 2011, An over-deterministic method for calculation of coefficients of crack tip asymptotic field from finite element analysis, Fatigue Fract Eng Mater Struct, 34, 159, 10.1111/j.1460-2695.2010.01504.x

Bažant, 1996, Analysis of work-of-fracture method for measuring fracture energy of concrete, ASCE J Eng Mech, 122, 138, 10.1061/(ASCE)0733-9399(1996)122:2(138)

Bažant, 1990, Determination of fracture energy, process zone length and brittleness number from size effect, with application to rock and concrete, Int J Fract, 44, 111, 10.1007/BF00047063

Bažant, 1998

Bažant, 2005

Broek, 1986

Červenka, 2005

Duan, 2003, Boundary effect on concrete fracture and non-constant fracture energy distribution, Eng Fract Mech, 70, 2257, 10.1016/S0013-7944(02)00223-0

Duan, 2007, Size effect on specific fracture energy of concrete, Eng Fract Mech, 74, 87, 10.1016/j.engfracmech.2006.01.031

Frantík P. FyDiK application, <http://www.kitnarf.cz/fydik>; 2007–2011.

Frantík, 2009, Fractality of simulated fracture, Key Eng Mater, 409, 154, 10.4028/www.scientific.net/KEM.409.154

Frantík, 2011, Efficient lattice modelling of fracture process zone extent in cementitious composites

Frantík, 2013, Parallelization of lattice modelling for estimation of fracture process zone extent in cementitious composites, Adv Eng Softw, 60–61, 48, 10.1016/j.advengsoft.2012.11.020

Hillerborg, 1976, Analysis of crack formation and crack growth in concrete by means of fracture mechanics and finite elements, Cem Concr Res, 6, 773, 10.1016/0008-8846(76)90007-7

Hu, 2004, Influence of fracture process zone height on fracture energy of concrete, Cem Concr Res, 34, 1321, 10.1016/j.cemconres.2003.12.027

Hu, 2007, Size effect: influence of proximity of fracture process zone to specimen boundary, Eng Fract Mech, 74, 1093, 10.1016/j.engfracmech.2006.12.009

Hu, 1992, Fracture energy and fracture process zone, Mater Struct, 25, 319, 10.1007/BF02472590

Hutař, 2006, Effect of constraint on fatigue propagation near threshold in medium carbon steel, Comput Mater Sci, 37, 51, 10.1016/j.commatsci.2005.12.025

Jandejsek, 2011, X-ray dynamic defectoscopy utilizing digital image correlation, Nucl Instrum Methods Phys Res Sect A, 633, S185, 10.1016/j.nima.2010.06.162

Jansen, 2000, Simplification of the testing and analysis procedure for the two parameter fracture model, ACI, SP201-01, 1

Jakůbek, 2006, Experimental system for high resolution X-ray transmission radiography, Nucl Instrum Methods Phys Res Sect A, 563, 278, 10.1016/j.nima.2006.01.033

Jeng, 1985, Two parameter fracture model for concrete, J Eng Mech ASCE, 111, 1227, 10.1061/(ASCE)0733-9399(1985)111:10(1227)

Jirásek, 2008

Karihaloo, 1995

Karihaloo, 1999, Size effect in shallow and deep notched quasi-brittle structures, Int J Fract, 95, 379, 10.1023/A:1018633208621

Karihaloo, 2003, A simple method for determining the true specific fracture energy of concrete, Magn Concr Res, 55, 471, 10.1680/macr.2003.55.5.471

Karihaloo, 2003, Coefficients of the crack tip asymptotic field for wedge splitting specimens, Eng Fract Mech, 70, 2407, 10.1016/S0013-7944(03)00005-5

Karihaloo, 2001, Higher order terms of the crack tip asymptotic field for a notched three-point bend beam, Int J Fract, 112, 111, 10.1023/A:1013392324585

Karihaloo, 2001, Higher order terms of the crack tip asymptotic field for a wedge-splitting specimen, Int J Fract, 112, 129, 10.1023/A:1013366025494

Kumar, 2011

Landis, 1999, Micro–macro fracture relationship and acoustic emission in concrete, Constr Build Mater, 13, 65, 10.1016/S0950-0618(99)00009-4

Luong, 1990, Infrared thermovision of damage processes in concrete and rock, Eng Fract Mech, 35, 291, 10.1016/0013-7944(90)90207-W

Maji, 1988, Process zone and acoustic-emission measurements in concrete, Exp Mech, 27, 10.1007/BF02328992

Mihashi, 1996, Correlation between characteristics of fracture process zone and tension-softening properties of concrete, Nucl Eng Des, 165, 359, 10.1016/0029-5493(96)01205-8

Mindess, 1991, Fracture process zone detection, 231

Muralidhara, 2010, Fracture process zone size and true fracture energy of concrete using acoustic emission, Constr Build Mater, 24, 479, 10.1016/j.conbuildmat.2009.10.014

Nallathambi, 1986, Determination of specimen-size independent fracture toughness of plain concrete, Magn Concr Res, 38, 67, 10.1680/macr.1986.38.135.67

Otsuka, 2000, Fracture process zone in concrete tension specimen, Eng Fract Mech, 65, 111, 10.1016/S0013-7944(99)00111-3

Ouyang, 1991, Damage assessment in concrete using quantitative acoustic emission, ASCE J Eng Mech, 117, 2681, 10.1061/(ASCE)0733-9399(1991)117:11(2681)

Reinhardt, 1999, Crack extension resistance based on the cohesive force in concrete, Eng Fract Mech, 64, 563, 10.1016/S0013-7944(99)00080-6

RILEM Draft Recommendation TC 50-FMC, 1985, Determination of the fracture energy of mortar and concrete by means of three-point bend test on notched beams, Mater Struct, 18, 285

RILEM Draft Recommendation TC 89-FMT, 1990, Determination of fracture parameters (KIcs and CTODc) of plain concrete using tree-point bend tests, Mater Struct, 23, 457

RILEM Draft Recommendation TC 89-FMT, 1990, Size effect method for determining fracture energy and process zone size of concrete, Mater Struct, 23, 461

Sakata, 1995, Crack evaluation in concrete members based on ultrasonic spectroscopy, Am Concr Inst Mater J, 71, 686

Seitl, 2011, Two-parameter fracture mechanical analysis of a near-crack-tip stress field in wedge splitting test specimens, Comput Struct, 89, 1852, 10.1016/j.compstruc.2011.05.020

Šestáková, 2013, How to enhance efficiency and accuracy of the over-deterministic method used for determination of the coefficients of the higher-order terms in Williams expansion, Appl Mech Mater, 245, 120, 10.4028/www.scientific.net/AMM.245.120

Shah, 1995

Shah, 1990, Experimental methods for determining fracture process zone and fracture parameters, Eng Fract Mech, 35, 3, 10.1016/0013-7944(90)90178-J

Su, 2007, Determination of coefficients of the crack tip asymptotic field by fractal hybrid finite elements, Eng Fract Mech, 74, 1649, 10.1016/j.engfracmech.2006.09.009

Tada, 2000

Tong, 1997, A hybrid element approach to crack problems in plane elasticity, Int J Numer Methods Eng, 7, 297, 10.1002/nme.1620070307

Trunk, 2001, Influence of size on fracture energy of concrete, Mater Struct, 34, 260, 10.1007/BF02482204

van Mier, 1997

Vavřík D, Fíla T, Jandejsek I, Veselý V, Frantík P, Keršner Z. Fracture process in silicate composite specimens – X-ray dynamic observation and numerical modelling. In: Proc of of 19th European conference on fracture–fracture mechanics for durability, reliability and safety, Kazan, Rusia, August 2631, 2012. Kazan Scientific Centre of the Russian Academy of Sciences; 2012. p. 9, [pap. 566].

Vidya Sagar, 2009, An experimental study on fracture process zone in HSC three point bend beam specimen using acoustic emission method, J Struct Eng, 36

Vidya Sagar, 2010, Verification of the applicability of lattice model to concrete fracture by AE study, Int J Fract, 161, 121, 10.1007/s10704-009-9431-7

Veselý, 2010, Reconstruction of a fracture process zone during tensile failure of quasi-brittle materials, Appl Comput Mech, 4, 237

Veselý, 2009, Cracked volume specified work of fracture, 10.4203/ccp.91.194

Veselý, 2010, Estimation of fracture process zone extent in cementitious composites, Chem Listy, 104, 382

Veselý, 2011, Fracture process zone extent and energy dissipation in silicate composites with different cohesive behaviour, 259

Veselý, 2007, Structural geometry, fracture process zone and fracture energy, vol. 1, 111

Veselý, 2012, Influence of boundary conditions on higher order terms of near-crack-tip stress field in a WST specimen, Key Eng Mater, 488-489, 399, 10.4028/www.scientific.net/KEM.488-489.399

Veselý, 2013, Accurate description of near-crack-tip fields for the estimation of inelastic zone extent in quasi-brittle materials, Key Eng Mater, 525–526, 529

Wikipedia, the free encyclopedia – stress (mechanics). Yield surface, <http://en.wikipedia.org/wiki/Yield_surface>; 2011 [cited 10.01.13].

Williams, 1957, On the stress distribution at the base of stationary crack, J Appl Mech ASME, 24, 109, 10.1115/1.4011454

Xu, 1999, Determination of double-K criterion for crack propagation in quasi-brittle fracture, Part I: Experimental investigation of crack propagation, Int J Fract, 98, 111, 10.1023/A:1018668929989

Xu, 1999, Determination of double-K criterion for crack propagation in quasi-brittle fracture, Part II: Analytical evaluating and practical measuring methods for three-point bending notched beams, Int J Fract, 98, 151, 10.1023/A:1018740728458

Yu, 2010, Problems with Hu-Duan boundary effect model and its comparison to size-shape effect law for quasi-brittle fracture, J Eng Mech ASCE, 136, 40, 10.1061/(ASCE)EM.1943-7889.89

Thông tin
Thông tin xuất bản

Advances in Engineering Software

Tập 72

66-76

Thông tin tác giả