A literature survey on the stability and significance of residual stresses during fatigue
Tóm tắt
Many manufacturing processes can induce residual stresses in components. These residual stresses influence the mean stress during cyclic loading and so can influence the fatigue life. However, the initial residual stresses induced during manufacturing may not remain stable during the fatigue life. This paper provides a broad and extensive literature survey addressing the stability of surface and near‐surface residual stress fields during fatigue, including redistribution and relaxation due to static mechanical load, repeated cyclic loads, thermal exposure and crack extension. The implications of the initial and evolving residual stress state for fatigue behaviour and life prediction are addressed, with special attention to fatigue crack growth. This survey is not a critical analysis; no detailed attempt is made to evaluate the relative merits of the different explanations and models proposed, to propose new explanations or models or to provide quantitative conclusions. Primary attention is given to the residual stresses resulting from four major classes of manufacturing operations: shot peening and related surface treatments, cold expansion of holes, welding and machining.
Từ khóa
Tài liệu tham khảo
Totten G., 2002, Handbook of Residual Stress and Deformation of Steel
Anonymous, 2002, Handbook for Damage Tolerant Design
Rosenthal D., 1959, Metal Fatigue, 170
Vöhringer O.(1983)Relaxation of residual stresses. In:Proceedings of European Conference on Residual Stresses(Edited byE.Karlsruhe W.MacherauchandV.Hauk). DGM Informationsgesellschaft pp.47–80.
Vöhringer O., 1987, Advances in Surface Treatments, Technology—Applications—Effects: Residual Stresses, Vol. 4, 367
Löhe D., 2002, Handbook of Residual Stress and Deformation of Steel, 54
Löhe D., 2002, Handbook of Residual Stress and Deformation of Steel, 27
Lu J., 2002, Handbook of Residual Stress and Deformation of Steel, 11
Fitzpatrick M. E., 1998, Fatigue crack/residual stress field interactions and their implications for damage‐tolerant design, J. Mater., 7, 190
Lu J., 2005, Handbook on Residual Stress
Vöhringer O.(1987)Changes in the state of the material by shot peening. In:Proceedings of the 3rd International Conference on Shot Peening (ICSP3) Garmisch‐Partenkirchen Germany (Edited byH.Wohlfahrt R.KoppandO.Vöhringer).DGM Informationsgesellschaft Verlag Oberursel pp.185–204.
Ezeilo A. Webster G. Webster P. J.andWebster P. S.(1993)Comparison of shot peening residual stress distributions in a selection of materials. In:Proceedings of the 5th International Conference on Shot Peening (ICSP5) Oxford UK (Edited byD.Kirk) pp.275–282.
Meister T. J., 1996, Surface Performance of Titanium: Proceedings of Symposium on Surface Performance of Titanium, 253
Cao W., 1994, Thermomechanical relaxation of residual stress in shot peened nickel base superalloy, Mater. Sci. Technol., 10, 947, 10.1179/mst.1994.10.11.947
Tufft M.(2002)Modeling of fatigue behavior due to shot peening conditions. In:Proceedings of the 8th International Conference on Shot Peening (ICSP‐8) Garmisch‐Partenkirchen Germany (Edited byL.Wagner).Wiley‐VCH GmbH. KGaA pp.530–539.
Robertson G. T., 1971, The effects of shot size on the residual stresses resulting from shot peening, Shot Peener, 11, 46
Reed E. C., 1960, J. Engng. Ind., 76
Dorr T.andWagner L.(1999)Fatigue response of various titanium alloys to shot peening. In:Surface Treatment IV: Computer Methods and Experimental Measurements Proceedings of the 4th International Conference on Computer Methods and Experimental Measurements for Surface Treatment Effects Assisi Italy pp.349–357.
Lautridou J. C., 1996, Effect of shot‐peening on the fatigue strength of nickel‐based super‐alloys produced by powder metallurgy, Bulletin du Cercle d'âetudes des Mâetaux, 16, 21.1
Happ M. B. Mourer D. P.andSchmidt R. L.(1987)Residual stress analysis and LCF test results for peened bolt hole and dovetail configurations. In:Proceedings of the ASM Conference on Residual Stress in Design Process and Materials Selection.ASM International Cincinnati Ohio pp.127–136.
Everett Jr. R. A. Matthews W. T. Prabhakaran Newman Jr. J. C.andDubberly M. J.(2000)The effects of shot and laser peening on crack growth and fatigue life in 2024 aluminum alloy and 4340 steel. In:USAF Structural Integrity Program Conference San Antonio Texas .
Prevéy P. S. Hornbach D. Ravindranath R.andCammett J. T.(2003a)Application of low plasticity burnishing to improve damage tolerance of a Ti‐6Al‐4V first stage fan blade. In:Proceedings of the 44th AIAA/ASME/ASCE/AHS Structures Structural Dynamics & Materials Conference. Norfolk Virginia .
Prevéy P. S. Jayaraman N.andRavindranath R. A.(2003b)Effect of surface treatments on HCF performance and FOD tolerance of a Ti‐6Al‐4V vane. In:Proceedings of the 8th National Turbine Engine High Cycle Fatigue (HCF) Conference. Monterey California .
Prevéy P. S. Jayaraman N.andShepard M. J.(2004)Improved HCF performance and FOD tolerance of surface treated Ti‐6‐2‐4‐6 compressor blades. In:Proceedings of the 9th National Turbine Engine High Cycle Fatigue Conference. Pinehurst North Carolina .
Wagner L., 1999, Fatigue Behavior of Titanium Alloys, 253
Misumi M., 1987, Deceleration of small crack growth by shot‐peening, Int. J. Mater. Product Technol., 2, 36
Berns H., 1986, Impact Surface Treatment, 31
Prevéy P. S. Telesman J. Gabb T.andKantzos P.(2000)FOD resistance and fatigue crack arrest in low plasticity burnished IN718. In:Proceedings of the 5th National Turbine Engine High Cycle Fatigue Conference Chandler Arizona .
Wilks M. D. B. Nowell D.andHills D. A.(1994)The influence of residual stress on crack growth rate. In:Proceedings of the 4th International Conference on Residual Stresses Baltimore Maryland pp.1238–1245.
Vöhringer O. Hirsch Th.andMacherauch E.(1984)Relaxation of shot peening induced residual stresses of TiAl6V4 by annealing or mechanical treatment. In:Proceedings of the 5th International Conference on Titanium Munich FRG Vol. 4 pp.2203–2210.
Gray H., 1987, Proceedings of the 3rd International Conference on Shot Peening (ICSP3), 447
Wagner L., 1997, Surface Performance of Titanium, 199
Prevéy P. S. Hornbach D. J.andMason P. W.(1997)Thermal residual stress relaxation and distortion in surface enhanced gas turbine engine components. In:Proceedings of the 17th Heat Treating Society Conference and Exposition and the 1st International Induction Heat Treating Symposium Indianapolis Indiana ASM pp.3–12.
Khadhraoui M., 1997, Experimental investigations and modelling of relaxation behaviour of shot peening residual stresses at high temperature for nickel base superalloys, Mater. Sci. Technol., 13, 360, 10.1179/mst.1997.13.4.360
Prevéy P. S.(2000)The effect of cold work on the thermal stability of residual compression in surface enhanced IN718. In:Proceedings of the 20th ASM Materials Solutions Conference & Exposition St. Louis Missouri pp.426–434.
Cammett J. T. Prevéy P. S.andJayaraman N.(2005)The effect of shot peening coverage on residual stress cold work and fatigue in a nickel‐based superalloy. In:Proceedings of the 9th International Conference on Shot Peening (ICSP‐9) Paris Marne la Vallée France Paper 261.
Masmoudi N., 1988, International Conference on Residual Stresses, 710
Gabb T. P., 2004, Stress relaxation in powder metallurgy superalloy disks, TMS Letters, 1, 115
Hoffmann J., 1987, Proceedings of the 3rd International Conference on Shot Peening (ICSP3), 239
Schulze V., 1993, Proceedings of the 5th International Conference on Shot Peening (ICSP5), 265
Menig R., 2002, Proceedings of the 8th International Conference on Shot Peening (ICSP‐8), 498
Prevéy P., 2002, Proceedings of the 8th International Conference on Shot Peening (ICSP‐8), 293
Krull P., 1999, Proceedings of the 7th International Conference on Shot Peening (ICSP7)
Roth M., 2002, Proceedings of the 8th International Conference on Shot Peening (ICSP‐8), 208
Potter J. M., 1976, Proceedings of the 25th Conference on Application of X‐Ray Analysis, 309
Eigenmann B. Schulze V.andVöhringer O.(1994)Surface residual stress relaxation in steels by thermal or mechanical treatment. In:Proceedings of the 4th International Conference on Residual Stresses Baltimore Maryland pp.598–607.
Hanagarth H., 1990, Proceedings of the 4th International Conference on Shot Peening (ICSP4), 337
Eigenmann B., 1995, Computer Methods and Experimental Measurements for Surface Treatment Effects II, Proceedings of the International Conference on Computer Methods and Experimental Measurements for Surface Treat, 17
Holzapfel H., 1996, Proceedings of the 6th International Conference on Shot Peening (ICSP6), 385
Holzapfel H., 1996, Proceedings of the 6th International Conference on Shot Peening (ICSP6), 413
Kirk D., 1987, Proceedings of the 3rd International Conference on Shot Peening (ICSP3), 213
Cammett J. T., 1993, Proceedings of the 5th International Conference on Shot Peening (ICSP5), 283
Prevéy P. S. Shepard M. J.andSmith P. R.(2001)The effect of low plasticity burnishing on the HCF performance and FOD resistance of Ti‐6Al‐4V. In:Proceedings of the 6th National Turbine Engine High Cycle Fatigue (HCF) Conference Jacksonville Florida .
Altenberger I., 2002, Proceedings of the 8th International Conference on Shot Peening (ICSP‐8), 483
Noster U., 2002, Proceedings of the 8th International Conference on Shot Peening (ICSP‐8), 447
Berkley S. G., 1997, 41st Annual Air Transport Association Non‐Destructive Testing Forum
Berkley S. G., 1999, 1999 USAF ASIP Conference
Vukelich S. Russ S. Berkley S.andBradley E. F.(2002)Residual stress measurement and its application to achieve predicted full life potential of low cycle fatigue (LCF) limited engine disks. In:Proceedings of the 9th International Symposium on Transport Phenomena and Dynamics of Rotating Machinery Honolulu Hawaii .
Belassel M. Brauss M.andBerkley S. G.(2000)Residual stress relaxation in nickel base alloys subjected to low cycle fatigue. In:Proceedings of the 6th International Conference on Residual Stresses: ICRS‐6 Oxford UK pp.144–151.
Seppi F. L.(1975)Relief of shot‐peened compressive layer by fatigue loading. In:Proceedings of the of a Workshop on Nondestructive Evaluation of Residual Stress San Antonio Texas NTIAC‐76‐2 pp.73–74.
Meguid S. A.andHammond D. W.(1989)Fatigue fracture and residual stress relaxation in shot‐peened components. In:Proceedings of the 2nd International Conference on Residual Stresses ICRS 2 Nancy France pp.797–802.
Rasouli Yazdi S.andLu J.(1999)Prediction of relaxation of residual stress induced by shot peening in aluminum alloys. In:Proceedings of the SEM Annual Conference on Theoretical Experimental and Computational Mechanics pp.880–883.
Bonnafé J. P., 1987, Proceedings of the 3rd International Conference on Shot Peening (ICSP3), 485
Fontanari V., 2001, Surface Treatment V, Proceedings of the 5th International Conference on Computer Methods and Experimental Measurements for Surface Treatment Effects, 333
Zinn W., 1999, Mechanical surface treatments of lightweight materials—effects on fatigue strength and near‐surface microstructures, J. Mater., 8, 145
Taira S.andMurakami Y.(1960)On the changes in residual stresses due to repeated stressing. In:Proceedings of the 3rd Japan Congress on Testing Materials Kyoto Japan pp.52–55.
Kodama S., 1972, Proceedings of the International Conference of Mechanical Behavior of Materials, Vol. II, 111
Schulze V., 1996, Proceedings of the 6th International Conference on Shot Peening (ICSP6), 403
Wick A. Schulze V.andVöhringer O.(1999)Influence of the shot peening temperature on the relaxation behaviour of residual stresses during cyclic bending. In:Proceedings of the 7th International Conference on Shot Peening Warsaw Poland pp.102–109.
Wick A. Schulze V.andVöhringer O.(1999)Shot peening and stress peening of AISI 4140 at increased temperatures. In:Proceedings of the 7th International Conference on Shot Peening Warsaw Poland pp.110–116.
Menig R., 2002, Proceedings of the 8th International Conference on Shot Peening (ICSP‐8), 311
Menig R., 2002, Proceedings of the 8th International Conference on Shot Peening (ICSP‐8), 317
Iida K.andHirose Y.(1999)The residual stress distribution in shot peened carburized steel under fatigue. In:Proceedings of the 7th International Conference on Shot Peening Warsaw Poland pp.96–101.
Zeller R., 1993, Residual Stresses, 907
Teodosio J. R., 2003, THERMEC′2003, Parts 1‐5, International Conference on Processing & Manufacturing of Advanced Materials
Qui Q., 1987, Proceedings of the 3rd International Conference on Shot Peening (ICSP3), 231
Torres M., 2002, Proceedings of the 8th International Conference on Shot Peening (ICSP‐8), 37
Bignonnet A., 1987, Proceedings of the 3rd International Conference on Shot Peening (ICSP3), 659
Neff P. J., 1981, Residual Stress for Designers and Metallurgists, 119
Bergström J.andEricsson T.(1984)Relaxation of shot peening induced compressive stress during fatigue of notched steel samples. In:Proceedings of the 2nd International Conference on Shot Peening ICSP‐2 Chicago Illinois pp.241–248.
Bergström J., 1987, Proceedings of the 3rd International Conference on Shot Peening (ICSP3), 221
Bignonnet A. Lieurade H. P. Picouet L.andCastex L.(1987)Shot peening of welded joints and residual stress relaxation during fatigue. In:Proceedings of the 3rd International Conference on Shot Peening (ICSP3) Garmisch‐Partenkirchen Germany (Edited byH.Wohlfahrt R.KoppandO.Vöhringer) DGM Informationsgesellschaft Verlag Oberursel pp.585–593.
Cao W., 1988, International Conference on Residual Stresses, 631
Iida K., 1996, Proceedings of the 6th International Conference on Shot Peening (ICSP6), 397
Lu J., 1987, Proceedings of the 3rd International Conference on Shot Peening (ICSP3), 391
Lu J., 1988, International Conference on Residual Stresses, 784
Phillips J. L., 1974, Sleeve Coldworking Fastener Holes. Vol. 1
Sha G. T., 1980, Emerging Technologies in Aerospace Structures, Design, Structural Dynamics and Materials Proceedings . The Aerospace Conference—Century 2—Emerging Technology Conferences, 125
Ezelio A. N. Webster P. S. Webster G. A.andWebster P. J.(1994)Influence of cyclic loading on residual stress distribution caused by cold hole expansion. In:Proceedings of the 4th International Conference on Residual Stresses Baltimore Maryland pp.1275–1284.
Prawoto Y., 2001, Advances in Fracture Research, ICF10, Proceedings of the 10th International Conference on Fracture
Cannon D. F. Sinclair J.andSharpe K. A.(1985)Improving the fatigue performance of bolt holes in railway rails by cold expansion. In:Proceedings of the International Conference and Exposition on Fatigue Corrosion Cracking Fracture Mechanics and Failure Analysis Salt Lake City Utah pp.353–369.
Underwood J. H., 2001, Advances in Fracture Research, ICF10, Proceedings of the 10th International Conference on Fracture
Zhang Y., 2002, UK ABAQUS User Group Conference
Wang D. Q., 1998, Proceedings of the 4th European Conference on Residual Stresses, 619
Kokaly M. T. Ransom J. S. Restis J. H.andReid L.(2005)Observations and analysis of fatigue crack growth from cold expanded holes. In:Proceedings of the 8th Joint NASA/FAA/DoD Conference on Aging Aircraft Palm Springs California .
Saunder T. J., 2000, Proceedings of the 4th Joint DoD/FAA/NASA Conference on Aging Aircraft
Mann J. Y., 1983, Stress fields associated with interference fitted and cold‐expanded holes, Metals Forum, 6, 43
Hermann R.andMoffatt J.(1991)Experiments and analysis of the fatigue life improvements in fastener holes of aluminium‐lithium alloy 2091. In:Proc eedings of the International Aluminum‐Lithium Conference Garmisch‐Partenkirchen Germany pp.621–626.
Adams N. J. I., 1973, Welding Research Supplement, 508‐s
Dalle Donne C., 2001, Advances in Fracture Research, ICF10, Proceedings of the 10th International Conference on Fracture
Terada H., 1985, Analysis of stress intensity factor of a crack approaching welding bead, Int. J. Fract., 27, 83, 10.1007/BF00040387
Miyamoto H., 1973, Significance of Defects in Welded Structures, Proceedings of the Japan‐U. S. Seminar, 189
Fukuda S., 1980, Numerical Methods in Fracture Mechanics, 615
Fukuda S., 1979, An experimental study of effect of welding residual stress upon fatigue crack propagation based on observation of crack opening and closure, Transact. Japan Welding Res. Inst., 8, 265
Wang G. S.(1996)To analyse fatigue crack growth in residual stress field at welded joints. In:Proceedings of the of the 6th International Fatigue Congress – Fatigue ′96 Berlin Germany (Edited byG.LütjeringandH.Nowack) Pergamon Vol. II pp.1219–1224.
Iida K., 1997, Residual stress relaxation by reversed loading, Welding in the World/Le Soudage dans le Monde, 39, 138
Iida K., 1998, Relaxation of welding residual stresses by reversed and repeated loadings, Welding in the World/Le Soudage dans le Monde, 41, 314
Takanashi M., 2000, Relaxation behavior of welding residual stresses by fatigue loading in smooth longitudinal butt welded joints, Welding World, 44, 28
Nitschke‐Pagel Th.andWohlfahrt H.(2000)Residual stress relaxation in welded high strength steels under different loading conditions. In:Proceedings of the 6th International Conference on Residual Stresses: ICRS‐6 Oxford UK pp.1495–1502.
Han S. T. Lee, 2002, Residual stress relaxation of welded steel components under cyclic load, Mater. Technol., 73, 414
Lopez Martinez L. Lin R. Want D.andBlom A. F.(1997)Investigation of residual stresses in as‐welded and TIG‐dressed specimens subjected to static/spectrum loading. In:Proceedings of the of the North European Engineering and Science Conference (NESC): Welded High‐Strength Steel Structures Stockholm Sweden (Edited byA. F.Blom) EMAS Publishing London UK .
Fukuda S., 1979, Recent Research on Mechanical Behavior of Solids, 401
James M. R., 1981, Residual Stress for Designers and Metallurgists, 169
Kuhn G., 1991, Residual Stresses—III: Science and Technology, Proceedings of the International Conference on Residual Stresses, 1294
Morrow J., 1958, Symposium on Basic Mechanisms of Fatigue, ASTM STP 237, 83
Morrow J., 1960, Relaxation of residual stresses due to fatigue loading, SAE Trans., 68, 40
Martin J. F., 1971, Computer based simulation of cyclic stress‐strain behavior with applications to fatigue, Mater. Res. Std., 11, 23
Jhansale H. R., 1973, Cyclic Stress‐Strain Behavior—Analysis, Experimentation, and Failure Prediction, ASTM STP 519, 246
Taira S. Honda K.andAbe T.(1964)X‐ray investigation on fatigue damage of metals (on the changes in half‐value breadth of x‐ray diffraction line and macro‐residual stress in torsional fatigue with mean stress). In:Proceedings of the 7th Japan Congress on Testing Materials Society of Materials Science Kyoto pp.26–30.
Pattinson E. J., 1962, Fading of residual stresses due to repeated loading, Metallurgia, 66, 228
Gould R. W., 1972, Advances in X‐Ray Analysis, 354