Adhesion and reliability of underfill/subtrate interfaces in flip chip BGA packages: metrology and characterization
Tóm tắt
This paper discusses the methodologies of fracture mechanics that are used to study interfacial delamination by modeling delamination as a crack propagating along the interface between two materials. Specifically, adhesion and subcritical debonding at interface between silicon nitride passivated Silicon die and silica/alumina filled epoxy underfill are investigated. Adhesion was measured in terms of a critical value of the applied strain energy release rate, G (J/m/sup 2/). Subcritical debond growth rates were characterized as a function of applied G. Adhesion and subcritical debonding were studied by varying interfacial chemistry, process and environmental factors. Interfacial chemistry was modified by using different adhesion promoters and by varying the COOH acid content. Process variable such as filler bead settling was studied. The effects of environmental variables were studied with temperature and humidity controlled environments.
Từ khóa
#Adhesives #Flip chip #Packaging #Metrology #Delamination #Strain measurement #Chemistry #Silicon compounds #Energy measurement #Environmental factorsTài liệu tham khảo
chau, 1999, Novel Flipchip Underfills, 49th ECTC Conference
kook, 2001, Environmentally-Assisted Subcritical Debonding of a Polymer/Metal Interface, J of App Physics
10.1016/0032-3861(83)90139-8
10.1177/002199839302700403
todd, 2000, Effects of Post-Reflow Cleaning Processes on the Performance of Flip-Chip Devices, International Acoustic Microimaging Society
craig, 1998, The Effects of Flux Materials on the Moisture Senstivity and Reliability of Flip-Chip-on-Board Assemblies, IEEE Transactions on Components Packaging and Manufacturing Technology Part C, 21
10.1021/ja00769a042
10.1021/ja00769a041
lane, 1997, Materials Reliability in Microelectronics VII, Proc MRS Annu Meeting, 473, 21, 10.1557/PROC-473-21
dai, 1998, 1998 48th Electronic Components & Technology Conference
10.1002/jor.1100160612
10.1115/1.2792642
10.1557/PROC-563-263
10.1557/PROC-565-123
hohlfelder, 2000, Adhesion of Epoxy Underfill to Benzocyclobutene-Passivated Silicon, J Mater Res
10.1080/00218467108081160
ritter, 1997, Fatigue Crack Propagation at Polymer Adhesive Interfaces, J Adhesion, 63, 265, 10.1080/00218469708017223
hilling, 1965, Chapter 17: Surfaces, Stress Dependent Surface Reactions and Strengths, High-strength Materials, 682
10.1007/BF00550196
liechti, 1997, International Journal of Fracture, 86, 10.1023/A:1007472628431
10.1111/j.1151-2916.2000.tb01237.x
dauskardt, 1998, Eng Fract Mech, 61, 10.1016/S0013-7944(98)00052-6
hutchinson, 1992, Mixed Mode Cracking in Layered Materials, Advances in Applied Mechanics, 29, 63, 10.1016/S0065-2156(08)70164-9
10.1007/BF00032381
anderson, 1995, Fracture Mechanics Fundamentals and Applications
10.1115/1.3173668
kanninen, 1973, An Augmented Double Cantilever Beam Model for Studying Crack Propagation and Arrest, International Journal of Fracture, 9, 83
wong, 1997, Chapter 14 Package Sealing and Encapsulation in MicroelectronicsPackaging Handbook Semiconductor Packaging Part II, 2
ma, 1997, Materials Reliability in Microelectronics VII, Proc MRS Annu Meeting, 473, 3, 10.1557/PROC-473-3
harper, 1996, Electronic Packaging and Interconnection Handbook
10.1111/j.1151-2916.1967.tb15145.x
10.1111/j.1151-2916.1999.tb02208.x
10.1179/msc.1980.14.8-9.450
10.1007/BF00752191
10.1007/BF00543692
kohnstam, 1970, The Kinetic Effects of Pressure, Progress in Reaction Kinetics, 335
10.1111/j.1151-2916.1993.tb03989.x