Low-loss shallow-rib waveguides were fabricated using As2Se3 chalcogenide glass and polyamide-imide polymer. Waveguides were patterned directly in the As2Se3 layer by photodarkening followed by selective wet etching. Theory predicted a modal effective area of 3.5–4 µm2, and this was supported by near-field modal measurements. The Fabry-Perot technique was used to estimate propagation losses as low as ~0.25 dB/cm. First-order Bragg gratings near 1550 nm were holographically patterned in some waveguides. The Bragg gratings exhibited an index modulation on the order of 0.004. They were used as a means to assess the modal effective indices of the waveguides. Small core As2Se3 waveguides with embedded Bragg gratings have potential for realization of all-optical Kerr effect devices.

We describe the fabrication and characterization of omnidirectional reflectors based on silver-doped chalcogenide glass and polymer. We deposited periodically alternating layers of thermally evaporated Ge33As12Se55 chalcogenide glass, sputtered silver, and spun-cast polyamide-imide polymer. The silver was subsequently dissolved into each adjacent chalcogenide glass layer, either by exposing the multilayer to visible light (photodoping) or by heating the sample. The resultant silver concentration within the chalcogenide glass layers is estimated to be ~20 at. %. Silver doping red-shifts the band edge of the glass, and produces an increase of ~0.3–0.4 in the refractive index. The glass retains good transparency in the near infrared after doping, and the technique enables the omnidirectional bandwidth to be increased from ~100 nm to ~200 nm in the 1550 nm wavelength region.