Visual analysis of solidification and δ–γ transformations in steels

Materials Science and Technology - Tập 29 Số 5 - Trang 631-635 - 2013
X F Zhang1, Yu‐ichi Komizo1
1Joining and Welding Research Institute, Osaka University, 11-1 Mihogaoka, Ibaraki, Osaka 567-0047, Japan

Tóm tắt

The theory of solidification of steels and the kinetics of austenite to α-ferrite phase transformation were extensively studied; however, comparatively, little information is available concerning the kinetics of the δ-ferrite to austenite transformation due to the difficulty of making in situ observations. In the present study, a laser scanning confocal microscopy with an infrared image furnace was implemented with which the in situ observations at the high temperature of the dynamic behaviour of the δ/ γ grain nucleation and growth and interphase boundaries of the steels are made possible. The solidification mode of the carbon steel and the austenitic stainless steel during welding can be directly observed, and the definitive sequence of phase transformation that led to the final microstructure was detected in real time. Finally, new experimental results will be presented and compared with previous studies.

Từ khóa


Tài liệu tham khảo

10.4028/www.scientific.net/RC.35

10.1007/978-1-4899-3051-4

10.1179/136217110X12785889549868

10.1080/09500839.2011.587464

10.2355/isijinternational.38.794

10.1016/S1359-6454(99)00022-1

10.1007/s11663-003-0016-y

10.2355/isijinternational.44.414

10.1016/j.commatsci.2005.02.006

10.2355/isijinternational.46.847

10.2355/isijinternational.44.565

Thông tin
Thông tin xuất bản

Materials Science and Technology

Tập 29 Số 5

631-635

Thông tin tác giả