Two layered silica protective film made by a spray-and-dip coating method on 304 stainless steel

Journal of Sol-Gel Science and Technology - Tập 55 - Trang 207-212 - 2010
Taejin Hwang1, HeungYeol Lee1, Hohyeong Kim1, GyunTak Kim1
1Surface Nano-Technology Team, Korea Institute of Industrial Technology (KITECH), Yeonsu-gu, Incheon, Republic of Korea

Tóm tắt

The silica coating has attracted much attention because of its superior corrosion resistance with almost no harm to human health and to the environment. In this study, a two layered silica film was tried to get an enhanced corrosion resistance. The silica film was prepared on the hairline finish 304 stainless steel surfaces by-a-spray- and subsequent-dip-coating process. The spray coating solution was prepared by mixing sodium silicate solution, silica colloid, tetraethyl orthosilicate (TEOS), methyltriethoxysilane (MTES), ethanol, and distilled water. Then the solution was sprayed onto the stainless steel surface, and was dried and heat treated. The dip coating solution was prepared by a simple mixing of TEOS and acidic water into ethanol, and the prior spray coated sample was dipped into the solution. The outer dip coated layer was intended to cover spray coated rough and porous layer and hence to enhance the corrosion resistance. A homogeneous and crack free surface was successfully obtained after the dip coating. The prepared silica film was characterized using scanning electron microscopy, potentiodynamic polarization scan, and electrochemical impedance spectroscopy. The two layered film showed an enhanced corrosion resistance. The enhancement was attributed to a protecting effect of the dip coated layer where the diffusion of ionic species was successfully impeded.

Tài liệu tham khảo

Peguet L, Balki B, Baroux B (2009) Corros Sci 51:493–498

Lo KH, Shek CH, Lai JKL (2009) Mater Sci Eng R 65:39–104

Cho YK, Jang WS, Yoo S, Kim SG, Kim SW (2008) Surf Coat Technol 202:5390–5394

Stappen MV, Bruyn KD, Quaeyhaegens C, Stals L, Poulek V (1995) Surf Coat Technol 74–75:143–146

Andritschky M, Atfeh M, Pischow K (2009) Surf Coat Technol 203:952–956

Shen GX, Chen YC, Lin CJ (2005) Thin Solid Films 489:130–136

García C, Ceré S, Durán A (2004) J Non-Cryst Solids 348:218–224

López DA, Rosero-Navarro NC, Ballarre J, Durán A, Aparicio M, Ceré S (2008) Surf Coat Technol 202:2194–2201

Rams J, Lopez AJ, Lopez MD, Ureña A (2007) Surf Coat Technol 202:1144–1148

Tiwari SK, Mishra T, Gunjan MK, Bhattacharyya AS, Singh TB, Singh R (2007) Surf Coat Technol 201:7582–7588

Brinker CJ, Scherer GW (1990) Sol-gel science. Academic Press, Inc, Boston

Brinker CJ, Hurd AJ, Schunk PR, Frye GC, Ashley CS (1992) J Non-Cryst Solids 147–148:424–436

Checmanowski JG, Szczygieł B (2008) J Non-Cryst Solids 354:1786–1795

Feil F, Fürbeth W, Schütze M (2009) Electrochim Acta 54:2478–2486

Thim GP, Oliveira MAS, Oliveira EDA, Melo FCL (2000) J Non-Cryst Solids 273:124–128

Ballarre J, Lópes DA, Cavalieri AL (2008) Thin Solid Films 516:1082–1087

Pepe A, Galliano P, Ceré S, Aparicio M, Durán A (2005) Mater Lett 59:2219–2222

Schmidt HK, Jonschker G, Goedicke S, Mennig M (2000) J Sol-Gel Sci Technol 19:39–51

Schmidt HK (1994) J Non-Cryst Solids 178:302–312

Suegama PH, Melo PGD, Recco AAC, Tschiptschin AP, Aoki IV (2008) Surf Coat Technol 202:2850–2858

Thông tin
Thông tin xuất bản

Journal of Sol-Gel Science and Technology

Tập 55

207-212

Thông tin tác giả