Two-Side Growth of the Cu9Ga4 Phase during the Interfacial Reactions between Sn–Ag–Cu–Ga Solders and Copper Substrates
Tóm tắt
Interfacial reactions between Sn–3.0Ag–0.5Cu–1.0Ga/1.5Ga in wt.% solders and Cu substrates have been investigated. The solder and substrate couples were annealed at 180°C for 6, 12, 18, and 24 days. Different layers of intermetallic compounds have been found to form, such as Cu6Sn5 and Cu9Ga4. Sn was also observed within the interfacial layer during the annealing. The Cu6Sn5 phase and the Cu9Ga4 phase were observed to form by turns from the substrate into the solder. The Cu9Ga4 phase grew from both the solder side and the intermetallics side. Growth of the Cu9Ga4 phase was found to depend on the Ga diffusion and the availability of the Cu6Sn5 phase.
Tài liệu tham khảo
M. Maleki, J. Cugnoni, and J. Botsis, “Microstructure-based modeling of the ageing effect on the deformation behavior of the eutectic micro-constituent in SnAgCu lead-free solder,” Acta Mater. 61, 103–114 (2013).
I. E. Anderson, “Development of Sn–Ag–Cu and Sn–Ag–Cu–X alloys for Pb-free electronic solder applications,” J. Mater. Sci.: Mater. Electron. 18, 55–76 (2007).
A. Kantarcioglu and Y. E. Kalay, “Effects of Al and Fe additions on microstructure and mechanical properties of SnAgCu eutectic lead-free solders,” Mater. Sci. Eng., A 593, 79–84 (2014).
F. J. Wang, Z. S. Yu, and K. Qi, “Intermetallic compound formation at Sn–3.0Ag–0.5Cu–1.0Zn lead-free solder alloy/Cu interface during as-soldered and as-aged conditions,” J. Alloys Compd. 438, 110–115 (2007).
A. K. Gain and L. C. Zhang, “Interfacial microstructure, wettability and material properties of nickel (Ni) nanoparticle doped tin–bismuth–silver (Sn–Bi–Ag) solder on copper (Cu) substrate,” J. Mater. Sci.: Mater. Electron. 27, 1–13 (2016).
Z. L. Ma, S. A. Belyakov, and C. M. Gourlay, “Effects of cobalt on the nucleation and grain refinement of Sn–3Ag–0.5Cu solders,” J. Alloys Compd. 682, 326–337 (2016).
G. H. Chen, J. S. Ma, and Z. T. Geng, “Fabrication and Properties of lead-free Sn–Ag–Cu–Ga solder alloy,” Mater. Sci. Forum 1747, 475–479 (2005).
Q. K. Zhang, W. M. Long, W. M. Yu, X. Q. Yu, Y. Y. Pei, and P. X. Qiao, “Effects of Ga addition on microstructure and properties of Sn–Ag–Cu/Cu solder joints,” J. Alloys Compd. 622, 973–978 (2015).
D. Luo, S. B. Xue, and Z. Q. Li, “Effects of Ga addition on microstructure and properties of Sn–0.5Ag–0.7Cu solder,” J. Mater. Sci.: Mater. Electron. 25, 3566–3571 (2014).
X. J. Nan, S. B. Xue, P. Z. Zhai, and D. X. Luo, “Effect of Pr addition on properties of Sn–0.5Ag–0.7Cu–0.5Ga lead-free solder,” J. Electron. Mater. 45, 1–6 (2016).
H. M. Chen, C. J. Guo, J. P. Huang, and H. Wang, “Influence of gallium addition in Sn–Ag–Cu lead-fee solder,” J. Mater. Sci: Mater. Electron. 26, 5459–5464 (2015).
H. M. Chen, G. F. Shang, W. Y. Hu, and H. Wang, “Growth kinetics of intermetallic compounds during interfacial reactions between SnAgCuGa lead-free solder and Cu substrate,” Powder Metall. Met. Ceram. 55, in press (2017).