Two-Dimensional Silicon/Carbon from Commercial Alloy and CO2 for Lithium Storage and Flexible Ti3C2Tx MXene-Based Lithium–Metal Batteries

ACS Nano - Tập 14 Số 12 - Trang 17574-17588 - 2020
Yongling An1,2, Yuan Tian1, Yuchan Zhang1, Chuanliang Wei1, Liwen Tan1, Chenghui Zhang3, Naxin Cui3, Shenglin Xiong1, Jinkui Feng1,2, Yitai Qian4
1SDU & Rice Joint Center for Carbon Nanomaterials, Key Laboratory for Liquid−Solid Structural Evolution & Processing of Materials (Ministry of Education), School of Materials Science and Engineering, State Key Laboratory of Crystal Materials, Shandong University, Jinan 250061, People’s Republic of China
2Shenzhen Institute of Shandong University, Shandong University, Shenzhen 518057, People’s Republic of China
3School of Control Science and Engineering, Shandong University, Jinan, 250061, People’s Republic of China
4Hefei National Laboratory for Physical Science at Microscale, Department of Chemistry, University of Science and Technology of China, Hefei 230026, People's Republic of China

Tóm tắt

Từ khóa


Tài liệu tham khảo

10.1038/s41586-019-1682-5

10.1126/science.aal4373

10.1126/science.aan8285

10.1038/s41586-019-1175-6

10.1038/nenergy.2017.108

10.1038/s41467-020-15217-9

10.1038/s41565-020-0690-9

10.1126/sciadv.aax0651

10.1002/adma.201506111

10.1038/s41467-019-08383-y

10.1038/s41560-019-0398-y

10.1126/sciadv.aaw4856

10.1038/s41467-019-09510-5

10.1021/acsnano.8b08821

10.1038/nnano.2014.6

10.1002/aenm.201601481

10.1021/acsnano.8b01558

10.1002/adfm.201502330

10.1021/acsnano.9b07241

10.1002/anie.201903709

10.1016/j.ensm.2018.09.019

10.1021/nl3014814

10.1021/nn3052023

10.1038/nenergy.2015.29

10.1002/adfm.201908721

10.1038/s41467-018-05398-9

10.1016/j.nanoen.2011.08.003

10.1021/acsnano.6b06828

10.1016/j.nanoen.2016.04.043

10.1002/adma.201605650

10.1038/nmat2725

10.1038/nchem.1802

10.1038/nnano.2012.35

10.1021/acsnano.8b02219

10.1038/nnano.2007.411

10.1038/nenergy.2016.113

10.1002/aenm.201902913

10.1002/aenm.201803070

10.1002/aenm.202002298

10.1038/s41467-019-13434-5

10.1016/j.ensm.2020.07.006

10.1021/acsnano.9b06653

10.1038/ncomms10998

10.1038/ncomms9597

10.1038/ncomms8393

10.1038/s41467-017-01823-7

10.1002/aenm.201800595

10.1002/adma.201701777

10.1002/adma.201800838

10.1002/adma.201705523

10.1021/acsnano.5b07977

10.1002/aenm.201901896

10.1016/j.mattod.2018.06.005

10.1021/acsami.8b21893

10.1021/acsnano.8b08088

10.1038/nenergy.2016.10

10.1002/aenm.201702322

10.1021/acsnano.0c00184

10.1038/nnano.2014.152

10.1021/acsnano.9b05599

10.1038/s41586-019-1904-x

10.1126/science.aba8311

10.1038/s41586-018-0109-z

10.1002/adfm.201707578

10.1002/adma.201803220

10.1038/s41560-020-0640-7

10.1002/adma.201506124

10.1002/adma.202002850

10.1016/j.chempr.2017.01.003

10.1021/acsenergylett.9b00539

10.1016/j.nanoen.2018.03.036

10.1016/j.ensm.2018.03.012

10.1021/acsenergylett.8b02376

10.1038/s41560-018-0276-z

10.1016/j.ensm.2018.07.010

10.1038/s41563-019-0305-8

10.1002/adma.201806470

Thông tin
Thông tin xuất bản

ACS Nano

Tập 14 Số 12

17574-17588

Thông tin tác giả