Tribological investigations of sol-gel ceramic films
Tóm tắt
Tribological properties of the TiO2, doped TiO2, Al2O3 and SiO2 thin films prepared by different sol-gel processes are reported. The results indicate that doping deteriorates the wear resistance of TiO2; organic modifier can improve the tribological property of Al2O3 significantly; and the SiO2 film prepared from inorganic salt sodium silicate registers much better wear resistance than that from ethyl orthosilicate.
Tài liệu tham khảo
Hirai, S., Shimakage, K., Sekiguchi, M. et al., Zirconium oxide coating on anodized aluminum by the sol-gel process combined with ultraviolet irradiation at ambient temperature, J. Am. Ceram. Soc., 1999, 82 (8): 2011–2016.
Paterson, M. J., Paterson, J. K., Ben-Nissan, B., The dependence of structural and mechanical properties on film thickness in sol-gel zirconia films, J. Mater. Res., 1998, 13: 388–395.
Suzuki, S., Ando, E., Abrasion of thin films deposited onto glass by the taber test, Thin Solid Films, 1999, 340: 194–200.
Hsu, S. M., Fundamental mechanisms of friction and lubrication of materials, Langmuir, 1996, 12: 4482–4485.
Krim, J., Atomic-scale origins of friction, Langmuir, 1996, 12: 4564–4566.