Tribological Characteristics and Wear Features of Powder Tin Bronze with the Addition of Ultrafine Oxides
Tóm tắt
The effect of the introduction of ultrafine particles of alumina, nickel oxides and a mixture of their oxides on the mechanical and tribological properties, structure and wear characteristics of powder tin bronze is studied. The increase in the content of alumina from 2 to 5 wt % leads to a decrease in strength by 1.2–1.4 times, and from 5 to 10 wt % it does not affect the change in the tensile strength of powder bronze and leads to a slight decrease in the compressive strength. With an increase in the alumina content from 2 to 10%, the coefficient of friction and the wear rate of powder bronze decrease, and the seizure pressure increases. The addition of nickel oxide to alumina promotes the formation of a homogeneous structure, lower porosity and smaller pore size, an increase in strength, a decrease in coefficient of friction of powder bronze from 0.028 to 0.022, by 2.5 times of wear rate, as well as an increase in seizure pressure from 4 to 7.0 MPa.
Tài liệu tham khảo
Antsiferov, V.N., Bobrov, V.G., Druzhinin, L.K., et al., Poroshkovaya metallurgiya i napylennye pokrytiya (Powder Metallurgy and Sprayed Coatings), Moscow: Metallurgiya, 1987.
Shehata, F., Fathy, A., Abdelhameed, M., and Moustafa, S.F., Preparation and properties of Al2O3 nanoparticle reinforced copper matrix composites by in situ processing, Mater. Des., 2009, vol. 30, no. 7, pp. 2756–2762.
Kopeliovich, D., Lead based engine bearing overlays. http://www.substech.com/dokuwiki/doku.php?id=lead_ based_engine_bearing_overlays. Accessed November, 2017.
Yong, L.Y. and Langdon, T.G., Creep behavior of an Al-6061 metal matrix composite reinforced with alumina particulates, Acta Mater., 1997, vol. 45, no. 11, pp. 4797–4806.
Patoliya, D.M. and Sharma, S., Preparation and characterization of zirconium dioxide reinforced aluminum metal matrix composites, Int. J. Innovative Res. Sci.,Eng. Technol., 2015, vol. 4, pp. 3315–3321.
Gupta, P., Kumar, D., et al., Structural and mechanical behaviour of 5% Al2O3-reinforced Fe metal matrix composites (MMCs) produced by powder metallurgy (P/M) route, Bull. Mater. Sci., 2013, vol. 36, pp. 859–868.
Shamsuddin, S., Jamaludin, S.B., et al., The effects of Al2O3 amount on the microstructure and properties of Fe–Cr matrix composites, Metall. Mater. Trans. A, 2010, vol. 41, no. 13, pp. 3452–3457.
Feldshtein, E.E. and Dyachkova, L.N., On the properties and tribological behaviors of P/M iron based composites reinforced with ultrafine particulates, Composites, Part B, 2014, vol. 58, pp. 16–24.
Dyachkova, L.N. and Solov’yanchik, I.N., Improvement of the mechanical and tribotechnical properties of iron-based powder materials by the addition of ultrafine additives, Vests. Nats. Akad. Navuk Bel., 2007, no. 3, pp. 21–26.
Kavalerskaya, N.E., Interaction of nickel with alumina in hydrodechlorination and hydrogenation catalysts, Doctoral (Chem.) Dissertation, Moscow, 2013.