Tribocorrosion Behavior of Aluminum/Alumina Composite Manufactured by Anodizing and ARB Processes
Tóm tắt
In the present work, tribocorrosion behavior of Al/Al2O3 composite strips manufactured by anodizing and accumulative roll bonding (ARB) processes was investigated. The alumina quantity was 0.48, 1.13, and 3.55 vol.% in the aluminum matrix. Tribocorrosion experiments were conducted using a ball-on-plate tribometer, where the sliding contact was fully immersed in 1 wt.% NaCl solution. The composite sample served as a working electrode and its open circuit potential (OCP) was monitored before, during, and after sliding. In order to characterize the electrochemical behavior of the surface before and after sliding electrochemical impedance spectroscopy (EIS) was used and wear was also measured. Furthermore, the influence of quantity and distribution of reinforcement particles in the matrix on OCP and EIS was evaluated. It was found that the quantity, shape, size, and dispersion of alumina particles in the aluminum matrix strongly affected the measured tribocorrosion characteristics. The results showed that inhomogeneous, lower quantity, fine, and acicular-shape alumina particles cause serious materials loss in tribocorrosion process.
Tài liệu tham khảo
L. Benea, F. Wenger, P. Ponthiaux, and J.P. Celis, Tribocorrosion Behaviour of Ni-SiC Nano-Structured Composite Coatings Obtained by Electrodeposition, Wear, 2009, 266, p 398–405
M. Azzi, M. Paquette, J.A. Szpunar, J.E. Klemberg-Sapieha, and L. Martinu, Tribocorrosion Behaviour of DLC-Coated 316L Stainless Steel, Wear, 2009, 267, p 860–866
T.M. Lillo, Enhancing Ductility of Al6061 + 10 wt.% B4C Through Equal-Channel Angular Extrusion Processing, Mater. Sci. Eng. A, 2005, 410–411, p 443–446
K.M. Shorowordi, T. Laoui, A.S.M.A. Haseeb, J.P. Celis, and L. Froyen, Microstructure and Interface Characteristics of B4C, SiC and Al2O3 Reinforced Al Matrix Composites: A Comparative Study, J. Mater. Process. Technol., 2003, 142, p 738–743
A. Upadhyaya and G.S. Upadhyaya, Sintering of Copper-Alumina Composites Through Blending and Mechanical Alloying Powder Metallurgy Routes, Mater. Des., 1995, 16, p 41–45
D.Y. Ying and D.L. Zhang, Processing of Cu-Al2O3 Metal Matrix Nanocomposite Materials by Using High-Energy Ball Milling, Mater. Sci. Eng. A, 2000, 226, p 152–156
D.J. Lloyd, Particles Reinforced Aluminum and Magnesium Matrix Composites, Int. Mater. Rev., 1994, 39, p 1–23
H. Ferkel, Properties of Copper Reinforced by Laser-Generated Al2O3-Nanoparticles, Nanostruct. Mater., 1999, 11, p 595–602
R. Jamaati, M.R. Toroghinejad, and A. Najafizadeh, An Alternative Method of Processing MMCs by CAR Process, Mater. Sci. Eng. A, 2010, 527, p 2720–2724
R. Jamaati, M.R. Toroghinejad, and A. Najafizadeh, Application of Anodizing and CAR Processes for Manufacturing Al/Al2O3 Composite, Mater. Sci. Eng. A, 2010, 527, p 3857–3863
R. Jamaati and M.R. Toroghinejad, Manufacturing of High-Strength Aluminum/Alumina Composite by Accumulative Roll Bonding, Mater. Sci. Eng. A, 2010, 527, p 4146–4151
R. Jamaati and M.R. Toroghinejad, High-Strength and Highly-Uniform Composite Produced by Anodizing and Accumulative Roll Bonding Processes, Mater. Des., 2010, 31(10), p 4816–4822
R. Jamaati and M.R. Toroghinejad, Effect of Al2O3 Nano-Particles on the Bond Strength in CRB Process, Mater. Sci. Eng. A, 2010, 527, p 4858–4863
F. Bratu, L. Benea, and J.P. Celis, Tribocorrosion Behaviour of Ni-SiC Composite Coatings Under Lubricated Conditions, Surf. Coat. Technol., 2007, 201, p 6940–6946
M. Azzi and J.A. Szpunar, Tribo-Electrochemical Technique for Studying Tribocorrosion Behavior of Biomaterials, Biomol. Eng., 2007, 24, p 443–446
E.E. Stansbury and R.A. Buchanan, Fundamentals of Electrochemical Corrosion, ASM International, Materials Park, OH, 2000
P. Ponthiaux, F. Wenger, D. Drees, and J.P. Celis, Electrochemical Techniques for Studying Tribocorrosion Processes, Wear, 2004, 256, p 459–468
C.Y.H. Lim, S.C. Lim, and M. Gupta, Wear Behaviour of SiCp-Reinforced Magnesium Matrix Composites, Wear, 2003, 255, p 629–637
M. Kok and K. Ozdin, Wear Resistance of Aluminium Alloy and Its Composites Reinforced by Al2O3 Particles, J. Mater. Process. Technol., 2007, 183, p 301–309
I. Garcia, D. Drees, and J.P. Celis, Corrosion-Wear of Passivating Materials in Sliding Contacts Based on a Concept of Active Wear Track Area, Wear, 2001, 249, p 452–460
Sh. Hassani, K. Raeissi, M. Azzi, D. Li, M.A. Golozar, and J.A. Szpunar, Improving the Corrosion and Tribocorrosion Resistance of Ni-Co Nanocrystalline Coatings in NaOH Solution, Corros. Sci., 2009, 51, p 2371–2379