The texture ordering in L10-FePt–Ag nanocomposites
Tóm tắt
L10-FePt nanoparticles with different Ag percentages were prepared. The presence of 6% Ag in co-sputtering process with deposition rate of 1 $$ {\dot{A}}/\text{s} $$ at 500 °C led to the formation of FePt nanoparticles with 5–7 nm size in L10-fct phase. Moreover, Ag atoms laying in boundaries of these nanoparticles in these circumstances caused c axis to orient and (001) peak intensity in XRD spectrum to increase. This is the result of the indirect exchange interactions of Fe magnetic atoms through Ag atoms in these boundaries. Therefore, where L10-FePt grains have the most boundaries with each other, the order index would be maximum.
Tài liệu tham khảo
Wang, H., Shang, P., Zhang, J., Guo, M.W., Mu, Y., Li, Q., Wang, H.: One-step synthesis of high-coercivity L10-FePtAg nanoparticles: effects of Ag on the morphology and chemical ordering of FePt nanoparticles. Chem. Mater. 25, 2450–2454 (2013)
Li, Y.B., Lou, Y.F., Zhang, L.R., Ma, B., Bai, J.M., Wei, F.L.: Effect of magnetic field annealing on microstructure and magnetic properties of FePt films. J. Magn. Magn. Mater. 322, 3789–3791 (2010)
Iskandar, F., Lee, H.M., Toda, T., Iwaki, T., Okuyama, K.: Fabrication of L10 FePtAg nanoparticles and a study of the effect of Ag during the annealing process. J Magn Magn Mater 305, 514–519 (2006)
Xu, X.H., Wu, H.S., Wang, F., Li, X.L.: Structure and magnetic properties of FePt and FePt/Ag thin films deposited by magnetron sputtering. Thin solid Film 472, 222–226 (2005)
Ikeda, R., Kagami, M., Kato, T., Iwata, S., Tsunashima, S.: Perpendicular anisotropy and microstructure of MBE-grown FePt–Ag and FePt–MgO granular films. J. Magn. Soc. Jpn 33, 493–497 (2009)
Wang, H., Zhang, J., Mo, Q., Yang, F.J., Wang, H.B., Miao, X.S.: Microstructure and magnetic properties of (0 0 1)-oriented L10 FePt films: role of Ag underlayer and Fe/Pt ratio. Mater. Res. Bull. 47, 2974–2976 (2012)
Roghani, R., Sebt, S.A., Khajehnezhad, A.: High magnetic coercivity of FePt–Ag/MgO granular nanolayers. Phys. C (Amsterdam, Neth.) 549, 15–17 (2018)
Stiles, M.D.: Interlayer exchange coupling. J. Magn. Magn. Mater. 200, 322–337 (1999)
Crisan, A.D., Vasiliu, F., Mercioniu, I., Crisan, O.: Role of Ag addition in L 10 ordering of FePt-based nanocomposite magnets. Philos. Mag. 94, 174–189 (2014)
Kundu, A., Zhang, S.: Temperature dependence of RKKY interaction. J. Magn. Magn. Mater. 393, 331–333 (2015)
Granz, S.D., Barmak, K., Kryder, M.H.: Granular L10 FePt–B and FePt–B–Ag (001) thin films for heat assisted magnetic recording. J. Appl. Phys. 111, 07b709 (2012)
Dong, K., Cheng, X., Cheng, W., Chen, S., Yang, X.: Fabrication and magnetic properties of Ag/FePt thin films. Mater. Manuf. Process. 27, 1160–1163 (2012)
Scheibel, F., Hearing, F., Ziemann, P., Wiedwald, U.: Role of developing L10 chemical order on the (0 0 1)-texture formation of (Fe1-xCux) Pt films grown on amorphous substrates. J. Phys. D Appl. Phys. 48, 085001 (2015)
Kaushik, N., Sharma, P., Tanaka, S., Makino, A., Esashi, M.: Preferentially oriented growth of L10FePt on Si substrate. Acta. Phys. Pol. A 127, 611–613 (2015)