The Synthesis and Martensitic Transformation of the Co2TiSb1−x Sn x (x = 0, 0.25, 0.5) Heusler Alloys
Tóm tắt
The phase component of Co2TiSb1−x
Sn
x
is strongly dependent on the preparation method. The L21-type Co2TiSb1−x
Sn
x
(x = 0.25, 0.5) alloys are successfully synthesized by the melt-spun method. And the microstructural properties of these ingots indicate that the Co2TiSb0.75Sn0.25 and Co2TiSb0.75Sn0.25 melt-spun samples exhibit the pure L21 phase. The thermal-elastic martensitic transformation has been experimentally observed in Co2TiSb0.75Sn0.25 alloy.
Tài liệu tham khảo
Kainuma, R., Imano, Y., Ito, W., Sutou, Y., Morito, H., Okamoto, S., Kitakami, O., Oikawa, K., Fujita, A., Kanomata, T., Ishida, K.: Nature 439, 957 (2006)
Yu, S.Y., Liu, Z.H., Liu, G.D., Chen, J.L., Cao, Z.X., Wu, G.H., Zhang, B., Zhang, X.X.: Appl. Phys. Lett. 89, 162503 (2006)
Barandiarán, J.M., Chernenko, V.A., Lázpita, P., Gutiérrez, J., Feuchtwanger, J.: Phys. Rev. B 80, 104404 (2009)
Krenke, T., Duman, E., Acet, M., Wassermann, E.F., Moya, X., Manosa, L., Planes, A.: Nat. Mater. 4, 450 (2005)
Ma, L., Wang, W.H., Lu, J.B., Li, J.Q., Zhen, C.M., Hou, D.L., Wu, G.H.: Appl. Phys. Lett. 99, 182507 (2011)
Webster, P.J., Ziebeck, K.R.A., Town, S.L., Peak, M.S.: Philos. Mag. B 49, 295 (1984)
Ullakko, K., Huang, J.K., Kantner, C., O’Handley, R.C., Kokorin, V.V.: Appl. Phys. Lett. 69, 1966 (1996)
Wu, G.H., Yu, C.H., Meng, L.Q., Chen, J.L., Yang, F.M., Qi, S.R., Zhan, W.S., Wang, Z., Zheng, Y.F., Zhao, L.C.: Appl. Phys. Lett. 75, 2990 (1999)
Liu, Z.H., Zhang, M., Cui, Y.T., Zhou, Y.Q., Wang, W.H., Wu, G.H., Zhang, X.X.: Appl. Phys. Lett. 82, 424 (2003)
Wuttig, M., Li, J., Craciunescu, C.: Scr. Mater. 44, 2393 (2001)
Morito, H., Fujita, A., Kainuma, R., Ishida, K.: Appl. Phys. Lett. 81, 1657 (2002)
Karaca, H.E., Karaman, I., Lagoudas, D.C., Maier, H.J., Chumlyakov, Y.I.: Scr. Mater. 49, 831 (2003)
Liu, G.D., Chen, J.L., Liu, Z.H., Dai, X.F., Wu, G.H., Zhang, B., Zhang, X.X.: Appl. Phys. Lett. 87, 262504 (2005)
Sánchez Llamazares, J.L., Sanchez, T., Santos, J.D., Pérez, M.J., Sanchez, M.L., Hernando, B., Escoda, L.L., Suñol, J.J., Varga, R.: Appl. Phys. Lett. 92, 012513 (2008)
Feng, L., Ma, L., Liu, E.K., Wu, G.H., Wang, W.H., Zhang, W.X.: Appl. Phys. Lett. 100, 152401 (2012)
Sutou, Y., Imano, Y., Koeda, N., Omori, T., Kainuma, R., Ishid, K., Oikawa, K.: Appl. Phys. Lett. 85, 4358 (2004)
Kainuma, R., Imano, Y., Ito, W., Sutou, Y., Morito, H., Okamoto, S., Kitakami, O., Oikawa, K., Fujita, A., Kanomata, T., Ishida, K. Nature 439, 957 (2006)
Luo, H.Z., Jia, P.Z., Liu, G.D., Meng, F.B., Liu, H.Y., Liu, E.K., Wang, W.H., Wu, G.H.: Solid State Commun. 170, 44 (2013)
Oikawa, K., Wulff, L., Iijima, T., Gejima, F., Ohmori, T., Fujita, A., Fukamichi, K., Kainuma, R., Ishida, K.: Appl. Phys. Lett. 79, 3290 (2001)
Webster, P.J., Ziebeck, K.R.A.: J. Phys. Chem. Solids 34, 1647 (1973)
Lee, S.C., Lee, T.D., Blaha, P., Schwarz, K.: J. Appl. Phys. 97, 10C307 (2005)
Rai, D.P., Thapa, R.K.: Chin. J. Phys. 51, 812 (2013)
Wang, L.Y., Dai, X.F., Wang, X.T., L, T.T., Chen, L., Liu, R., Cui, Y.T., Liu, G.D.: Chin. Phys. B. 24(12), 126201 (2015)
Carbonari, A.W., Saxena, R.N., Pendl, W., Mestnik Filho, J., Attili, R.N., Olzon-Dionysio, M., de Souza, S.D.: J. Magn. Magn. Mater. 163, 313 (1996)
Stadnyk, Y., Romaka, L., Horyn, A., Tkachuk, A., Gorelenko, Y., Rogl, P.: J. Alloys Compd. 387, 251 (2005)