The Effect of Pre‐Processing and Grain Structure on the Bio‐Corrosion and Fatigue Resistance of Magnesium Alloy AZ31

Advanced Engineering Materials - Tập 9 Số 11 - Trang 967-972 - 2007
Hao Wang1, Y. Estrin2,3, Hanguang Fu4, Guang‐Ling Song4, Zuzana Zuberova5
1Faculty of Engineering and Surveying, University of Southern Queensland, Toowoomba, Queensland 4350, Australia
2ARC Centre of Excellence for Design in Light Metals, Department of Materials Engineering, Monash University, Clayton, Vic. 3800, Australia
3CSIRO Division of Manufacturing and Materials Technology, Clayton, Vic. 3168, Australia
4School of Engineering, The University of Queensland, St. Lucia 4072, Australia
5Department of Material Science and Engineering, Clausthal University of Technology, 38670 Clausthal-Zellerfeld, Germany

Tóm tắt

Từ khóa


Tài liệu tham khảo

10.1002/adem.200500013

10.1016/S0925-8388(01)01899-0

10.1002/(SICI)1527-2648(199909)1:1<11::AID-ADEM11>3.0.CO;2-N

10.1016/j.biomaterials.2004.09.049

Ren Y. B., 2005, Acta Metall. Sinica., 41, 1228

A. Eliezer F. Witte 7thIntl. Conf. on Magn. Alloys and Their Appl.Wiley‐VCH Weinheim2007 822.

10.4028/www.scientific.net/MSF.426-432.521

10.1016/j.biomaterials.2006.09.034

10.1007/s11661‐007‐9109‐6

10.1016/j.scriptamat.2003.10.006

10.1002/adem.200600252

Song G., 2007, Corros. Sci., 49, 169

Wang H., 2006, Tissue Eng., 12, 1067

10.1149/1.2428496

H. Wang M. X. Zhang Z. M. Shi K. Yang 2006 TMS Conf.San Antonio USA March 12–16 2006.

Thông tin
Thông tin xuất bản

Advanced Engineering Materials

Tập 9 Số 11

967-972

Thông tin tác giả