THE CRYSTAL STRUCTURE AND PHASE TRANSITIONS OF β-Zn2P2O7

Canadian Science Publishing - Tập 43 Số 5 - Trang 1147-1153 - 1965
C. Calvo1
1Cl~emistry, iIIcilCaster University, fIa?ililto71, Onta~io

Tóm tắt

β-Zn2P2O7 crystallizes in the C2/m space group with lattice parameters a = 6.61 ± 0.01 Å, b = 8.29 ± 0.01 Å, c = 4.51 ± 0.01 Å, β = 105.4° ± 0.2° and z = 2. The anion, P2O7−4, is centered with its mirror plane coinciding with the mirror plane of the space group. The central oxygen atom, however, shows high anisotropic thermal motion and thus it appears that the P—O—P bond angle is linear only as a result of thermal averaging. The cations are found on twofold axes in irregular sixfold coordination and these ZnO6 groups share three edges with neighboring cations. This cation coordination is, therefore, consistent with that predicted from the red emission of β-Zn2P2O7:Mn++.

Từ khóa


Tài liệu tham khảo

CALVO., 1963, J. Phys. Chem. Solids, 24, 141, 10.1016/0022-3697(63)90049-0

CALVO., 1965, Can. J. Chelu, 43, 436, 10.1139/v65-058

1961, LIASZEWICZ. Roczniki Chern., 35, 31

LURASZEWICZ R., 1961, IEWICZ. RoczlikiChem., 35, 741

DATARS C., 1964, J. Chem. Phys., 41, 806, 10.1063/1.1725964

ROY E. T., 1948, Iileralogist, 33, 458

OETLING R. A., 1963, J. Phys. Chem., 67, 2737, 10.1021/j100806a055

CRUICKSHANK., 1964, Acta Cryst., 17, 672, 10.1107/S0365110X64001645

LEVI G., 1935, Z. Icrist., 92, 190

H., 1961, VICGEACHIN. Acta Cryst., 14, 1286, 10.1107/S0365110X61003727

CRUICRSHANK H., 1962, Acta Cryst., 15, 491, 10.1107/S0365110X62001206

IUEIS., Acta Cryst., 9, 652

HUGHES., 1941, J. Am. Chem. Soc., 63, 1737, 10.1021/ja01851a069

IIU MEL, 1958, J. Electrochem. Soc., 105, 525

Thông tin
Thông tin xuất bản

Canadian Science Publishing

Tập 43 Số 5

1147-1153

Thông tin tác giả