Synthesis of Ordered Mesoporous Carbon with Bimodal Pore System and High Pore Volume

Advanced Materials - Tập 15 Số 19 - Trang 1602-1606 - 2003
An‐Hui Lu1, Wolfgang Schmidt2, Bernd Spliethoff3, Ferdi Schüth1
1Research Department Schüth, Max-Planck-Institut für Kohlenforschung, Max Planck Society
2Research Group Schmidt, Max-Planck-Institut für Kohlenforschung, Max Planck Society
3Service Department Lehmann (EMR), Max-Planck-Institut für Kohlenforschung, Max Planck Society

Tóm tắt

Ordered mesoporous carbon, named as NCC‐1, has been synthesized via a nanocasting process using SBA‐15 as the template and diluted furfuryl alcohol solution as the carbon source. NCC‐1 shows a bimodal pore size distribution (see Figure) in the mesopore range and a high pore volume up to 3.2 cm3 g–1. Since the pore systems are independently generated at different stages during the synthesis, they can also be modified independently.

Từ khóa


Tài liệu tham khảo

10.1016/0008-6223(95)00054-H

10.1016/S0008-6223(97)89878-8

10.1016/0927-6513(95)00014-Z

10.1007/BF01139044

10.1002/adma.200390020

10.1021/jp991673a

10.1002/1521-4095(200105)13:9<677::AID-ADMA677>3.0.CO;2-C

10.1021/jp013583n

10.1039/a906872d

10.1038/35084046

10.1126/science.279.5350.548

10.1002/1521-4095(20021203)14:23<1776::AID-ADMA1776>3.0.CO;2-A

10.1021/ja011564l

10.1002/1521-3773(20020916)41:18<3489::AID-ANIE3489>3.0.CO;2-M

10.1021/jp002597a

10.1021/cm000164e

Thông tin
Thông tin xuất bản

Advanced Materials

Tập 15 Số 19

1602-1606

Thông tin tác giả