Synthesis and properties of carbons dispersed with α-iron particles from divinylbenzene-vinylferrocene

α-Iron-dispersed carbon was synthesized, through pressure pyrolysis of divinylbenzene-vinylferrocene above 750°C, and by reduction of magnetite-dispersed carbon. Divinylbenzenevinylferrocene copolymer was pyrolysed at 125 MPa above 750°C to yield carbons dispersed with α-iron accompanied by cementite. Magnetite in the carbon matrix was reduced to α-iron after heat treatments at 500°C in a flow of hydrogen. Carbons synthesized by the pressure pyrolysis of divinylbenzene-vinylferrocene at 800°C and 125 MPa contained iron-compound particles up to 200 nm, whereas the median diameter of α-iron particles in the carbon matrix after reduction treatments was 20 nm. α-Iron-dispersed carbon had a Curie temperature of 770°C. The saturation magnetization of iron-dispersed carbon increased with increasing the pyrolysis temperature of divinylbenzene-vinylferrocene copolymer, and reached a constant value of 183 e.m.u.g−1 at 800°C. The saturation magnetization of α-iron-dispersed carbon after the reduction treatment revealed practically the theoretical value of α-iron. Carbons finely dispersed with only α-iron particles were synthesized successfully by reduction of magnetitedispersed carbons.