Sustainable Approach for Linz‐Donawitz Slag Waste as a Replacement of Cement in Concrete: Mechanical, Microstructural, and Durability Properties

Advances in Civil Engineering - Tập 2020 Số 1 - 2020
Richa Palod1, Shirish V. Deo1, Gangadhar Ramtekkar1
1Department of Civil Engineering, National Institute of Technology, Raipur 492010, Chhattisgarh, India

Tóm tắt

Linz‐Donawitz (LD) slag, solid waste produced during steel manufacture in basic oxygen furnace, is difficult when it comes to handling and disposal and has very limited utilization. To increase its reusability, the suitability of supplanting cement with LD slag in concrete was examined. To study the impact of partially replacing cement with LD slag on strength, microstructure, and durability of concrete, more than 150 samples were cast. The test results reveal that the highest compressive and flexural strengths were attained at 20% LD slag replacement and, beyond that, the strength decreased. The hydration products detected by X‐ray Diffraction (XRD) and Fourier‐transform infrared spectroscopy (FTIR) were calcium silicate hydrate (C‐S‐H), ettringite, and calcium aluminosilicate hydrate (C‐A‐S‐H). The scanning electron microscope (SEM) images of binary cement concrete showed denser microstructure and lesser voids. The sulphuric acid resistance, electrical resistivity, and carbonation resistance tests done reveal that acceptable durability could be achieved when cement is replaced by LD slag. It is deduced that LD slag can be utilized in partially replacing cement to achieve the desired strength. This research gives another comprehension of simultaneously managing steel industry waste for sustainable development and contributing added advantages to the economy.

Từ khóa


Tài liệu tham khảo

Indian Minerals Yearbook (IBM), 2018, Slag-Iron and Steel (Advance Release)

Federation of Indian Chambers of Commerce and Industry, 2014, Using Steel Slag in Infrastructure Development

10.1016/j.jhazmat.2006.02.060

Palod R., 2017, Review and suggestions on use of steel slag in concrete and its potential use as cementitious component combined with GGBS, International Journal of Civil Engineering and Technology, 8, 1026

10.1016/j.jclepro.2019.04.363

10.1016/j.conbuildmat.2014.12.007

10.1016/j.cemconcomp.2015.04.006

10.1016/j.jhazmat.2008.09.105

10.1016/S0008-8846(02)00763-9

10.1061/(asce)0899-1561(2004)16:6(639)

10.1016/j.jhazmat.2010.08.071

PalodR. DeoS. V. andRamtekkarG. D. Parametric study of steel slag powder as cementitious material on cement mortars Proceedings of the Urbanization Challenges in Emerging Economies 2018 New Delhi India 445–451 https://doi.org/10.1061/9780784482032.045.

10.1016/j.cemconres.2010.11.018

10.1016/s0956-053x(00)00102-1

10.1061/(asce)0899-1561(2004)16:3(230)

10.1016/s0921-3449(99)00060-9

10.1016/j.jhazmat.2007.07.093

10.1016/j.jclepro.2019.01.260

10.1016/j.conbuildmat.2015.02.062

10.1016/j.conbuildmat.2009.12.028

10.1016/j.cemconres.2007.03.008

10.1007/s11431-010-4204-0

10.4028/www.scientific.net/KEM.539.235

10.1016/j.conbuildmat.2013.06.044

BIS 8112, 2013, Ordinary Portland Cement, 43 Grade-Specification (Second Revision)

BIS 383, 1970, Specifications for Coarse and Fine Aggregates from Natural Sources for Concrete

Mason B., 1944, The constitution of some basic open-hearth slags, Journal of Iron and Steel Institution, 11, 69

BIS 10262, 2009, Concrete Mix Proportioning-Guidelines

Rai S., 2006, Interaction of tartaric acid during hydration of Portland cement, Indian Journal of Chemical Technology, 13, 255

BIS 5514, 1996, Apparatus Used in “Le-Chatelier” Test-Specification

BIS 13311, 1992, Non-Destructive Testing of Concrete—Methods of Test

10.1016/j.conbuildmat.2011.06.072

10.1016/j.cemconres.2013.05.021

10.1016/j.cemconres.2009.01.003

BIS 4031, 1988, Methods for Physical Test of Hydraulic Cement

ACI Committee 222 Protection of metals in concrete against corrosion 2001 American Concrete Institute Farmington Hills MI USA 1–41 ACI 222R-01.

Thông tin
Thông tin xuất bản

Advances in Civil Engineering

Tập 2020 Số 1

Thông tin tác giả