Sulfide capacities of fayalite-base slags
Tóm tắt
The sulfide capacities of fayalite-base slags were measured by a gas-slag equilibration technique under controlled oxygen and sulfur potentials similar to those encountered in the pyrometallurgical processing of nonferrous metals. The oxygen pressure range was from 10−9.5 to 10−11 MPa and the sulfur pressure range from 10−3 to 10−4.5 MPa, over a temperature range of 1473 to 1623 K. The slags studied were FeO-SiO2 at silica saturation and those with addition of CaO, MgO, and Al2O3 to determine their effect on sulfide capacities. For these slags, the sulfide capacities were found to vary from 10−3.3 to 10−5. The sulfide capacities increased with increasing temperature from 1473 to 1623 K. A comparison of the reported plant data on sulfur content of industrial slags shows good agreement with the present experimental results. The present data will be useful in estimating metal losses in slag due to metal sulfide entrainment in nonferrous smelters.
Tài liệu tham khảo
C.J.B. Fincham and F.D. Richardson:Proc. R. Soc. A, 1954, pp. 40–62.
K.P. Abraham and F.D. Richardson:J. Iron Steel Inst., 1960, vol. 196, pp. 309–17.
A.S. Venkatadri and H.B. Bell:J. Iron Steel Inst., 1969, vol. 207, pp. 1110–15.
A. Branson and G.R. St. Pierre:Metall. Trans. B, 1981, vol. 12B, pp. 729–31.
K. Karsrud:Scand. J. Metall., 1984, vol. 13, pp. 144–50.
X.F. Zhang and J.M. Toguri:Can. Metall. Q., 1987, vol. 26 (2), pp. 117–22.
A.H. Chan and R.J. Fruehan:Metall. Trans. B, 1989, vol. 20B, pp. 71–76.
K. Susaki, M. Maeda, and N. Sano:Metall. Trans. B, 1990, vol. 21B, pp. 121–29.
N. Sano:Proc. 4th Int. Conf. on Molten Slags and Fluxes, 1992, Iron and Steel Institute of Japan, Tokyo, 1992, pp. 179–84.
R. Berryman, I.D. Sommerville, and F. Ishii:Iron Steelmaker (Trans. ISS), 1987, vol. 14, pp. 49–54.
S. Simeonov, T. Sakai, and M. Maeda:Metall. Trans. B, 1992, vol. 23B, pp. 325–30.
D.R. Haughton, P.L. Roeder, and B.J. Skinner:Econ. Geol., 1974, vol. 69, pp. 451–67.
S.R. Poulson and H. Ohmoto:Chem. Geol., 1990, vol. 85, pp. 57–75.
T. Katsura and S. Nagashima:Geochim. Cosmochin. Acta, 1974, vol. 38, pp. 517–31.
H. Bell:Can. Metall. Q., 1981, vol. 20 (2), pp. 169–79.
H. Jalkanen:Scand. J. Metall., 1981, vol. 10 (4), pp. 177–84.
R.G. Reddy and M. Blander:Metall. Trans. B, 1987, vol. 18B, pp. 591–96.
A.D. Pelton, G.E. Erikson, and A.R. Serano:Metall. Trans. B, 1993, vol. 24B, pp. 817–25.
Y.A. Chang, J.P. Newmann, and U.V. Choudary:INCRA Series on the Metallurgy of Copper, vol. VII,Phase Diagrams and Thermodynamic Properties of Ternary Copper-Sulfur-Metal Systems, International Copper Research Association, 1979, p. 84.
A.K. Biswas and W.G. Davenport:Extractive Metallurgy of Copper, Pergamon International Library, Oxford, United Kingdom, 1976, p. 118.
D.L. Kaiser and J.F. Elliot:Metall. Trans. B, 1986, vol. 17B, pp. 147–57.
K.P. Abraham, M.W. Davies, and F.D. Richardson:J. Iron Steel Inst., 1960, vol. 196, pp. 309–12.
W.G. Davenport and E.H. Partelpoeg:Flash Smelting, Pergamon Press, Oxford, United Kingdom, 1987, pp. 4–5.
R. Shimpo, S. Goto, O. Ogawa, and I. Asakura:Can. Metall. Q., 1986, vol. 25 (2), pp. 113–21.
C.J. Newman, G. MacFarlane, K. Molnar, and A.G. Storey:Pyrometallurgy of Copper, Pergamon Press, New York, NY, 1991, pp. 65–80.
S. Simeonov and J.M. Toguri: University of Toronto, Toronto, Canada, unpublished research, 1993.
H. Li and W.J. Rankin:Metall. Trans. B, 1994, vol. 25, pp. 79–89.
R.A. Sharma and F.D. Richardson:J. Iron Steel lnst., 1961, vol. 198, pp. 386–90.
P.T. Carter and T.G. Macfarlane:J. Iron Steel lnst., 1957, vol. 185, pp. 54–66.