Study on Viscosity of the La2O3-SiO2-Al2O3 Slag System
Tóm tắt
The viscosities and free-running temperatures of slag in a La2O3-SiO2-Al2O3 slag system were measured using an internal rotating cylinder method. For different La2O3 mass contents (45, 50, and 55 pct) in the La2O3-SiO2-Al2O3 ternary slag, the slag viscosity and free-running temperature decreased with a decrease in SiO2 content and an increase in Al2O3 content, and decreased with an increase in La2O3 content. Minor components B2O3, FeO, and MnO could decrease the viscosity and free-running temperature of La2O3-SiO2-Al2O3 ternary slag, especially FeO, and a small amount of FeO and B2O3 had an additive effect on slag viscosity and free-running temperature reduction.
Tài liệu tham khảo
T. Xu and H. Peng: Rare Earth, 2010, vol. 31, pp. 34–39.
J. Huang and R. Feng: Rare Earth Inf, 2010, vol. 8, pp. 21–23.
W. Wu and H. Zhang: Chinese Journal of Rare Metals, 2010, vol. 34, pp. 79–84.
Y. Wang, Y. Liu, J. Guo, S. Wang, and G. Weng: Hydrometall. China, 2006, vol. 25, pp. 195–97.
Y. Chen: China Resour. Compr. Util., 2006, vol.4, pp. 10-13.
C. Guo and J. Chen: An Extraction Technology of Rare Earth Nickel-Cobalt Alloy from Waste Rare Earth Hydrogen Alloy, Chinese Patent, Chinese Patent, CN1932054, 2007-03-21.
C. Guo, Q. Wang, and X. Liu: Rare earth nickel-cobalt alloy was used as the raw materials to produced hydrogen storage alloy, Chinese Patent, CN101250647, 2007-08-27.
H. Huo and C. Guo: J. Inner Mong. Univ. Sci. Technol., 2007, vol. 26, pp. 42–45.
R. Wang, J. Yan, Z. Zhou, Z. Zhou, B. Deng, and X. Gao: J. Chin. Soc. Rare, 2002, vol. 20, pp. 138–42.
J. Yan, R. Wang, D. Yan, W. Gong, Z. Zhou, and B. Deng: Regeneration method of deactivated negative alloy powder of secondary nickel-hydrogen battery, Chinese Patent, CN1295355, 2001-05-16.
T. Saito, H. Sato, and T. Motegi: J. Mater. Res., 2003, vol. 18, pp. 2814–19.
T. Saito, H. Sato, S. Ozawa, J. Yu, and T. Motegi: J. Alloy Compd., 2003, vol. 353, pp. 189–93.
H. Hagen, X. Guo, and L. Xiao: Metall Ore Dress Abroad, 2006, vol. 6, pp. 34–38.
T. Muller and B. Friedrich: Power Sources, 2006, vol. 158, pp. 1498–09.
Y. Jiang, Y. Deng, W. Bu: Metall. Mater. Trans. B, 2015, vol. 46B, pp, 2153-57.
S. Yang: Titanium Slag Melting & Pig Iron Technology, Metallurgical Industry, Publishing House, Beijing, 2006.
Y. Deng, S. Wu, Y. Jiang, and H. Li: Rare Earth, 2015, vol. 36, pp. 104–09.
Y. Jiang, G. Luo, X. Ma, J. Yang, X. Liu, and S. Song: Rare Earth, 2012, vol. 33, pp. 53–56.
L. Zhang and S. Jahanshahi: Metall. Mater. Trans. B, 1998, vol. 29B, pp. 177–86.
H. Zuo, C. Wang, C. Xu, J. Zhang and T. Zhang: Ironmak. Steelmak., 2015, vol. 43, pp. 56–63.
J. W. Kim: Proceedings of 4th International Conference on Molten slags and fluxes, Iron and Steel Institute of Japan, Tokyo, 1992, pp. 28.
J. Kijak, J. Durisim, G. Gabani and M. Cecko: Hatnik Listy, 1992, vol.7, pp. 28.
X. Huang, J. Liao, K. Zheng, H. Hu, F. Wang and Z. Zhang: Ironmak Steelmak, 2014, vol. 41, pp. 67–74.
X. Yu, G. Wen, P. Tang, and H. Wang: Ironmaking & Steelmaking, 2009, vol. 36, pp. 623–30.
H. Wang, G. Li, Q. Dai, Y. Lei, Y. Zhao, B. Li, G. Shi, and Z. Ren: Isij Int., 2006, vol.46, pp. 637.
Y. Sun, J. Liao, K. Zheng, X. Wang and Z. Zhang: JOM J. Miner. Met. Mater. Soc., 2014, vol. 66, pp.2168–75.
P. A. Tanskanen, S. M. Huttunen, P. H. Mannila and J. J. Harkki: Proceedings 6th International Conference Molten Slags, Fluxes, and Salts, KTH, Stockholm, 2000, pp. 445.
H. S. Seong, M. J. Sung, S. L. Young, J. M. Dong: Isij International, 2007, vol. 47, pp. 1090–96.
G.W. Toop and C.S. Samis: Trans. TMS-AIME, 1962, vol. 224, pp. 878–87.
G. Zhang, K. Chou, Q. Xue, K. C. Mills: Metall. Mater. Trans. Part B, 2012, vol. 43B, pp. 64–72.