Studies on thermal decomposition of phenol binder using TG/DTG/DTA and FTIR-DRIFTS techniques in temperature range 20–500 °C
Tóm tắt
Từ khóa
Tài liệu tham khảo
Hardrict S N. Novel novolac-phthalonltrlle and slloxanephthalonltrlle resins cured with low melting novolac oligomers for flame retardant structural thermosets. Thesis of Master of Science in Chemistry. Blacksburg: Virginia Polytechnic Institute and State University, 2003.
Movahed F S, Cheng G C, Venkatachari B S, et al. Atomistic simulation of thermal decomposition of crosslinked and noncrosslinked phenolic resin chains. In: 42nd AlAAThermophysics Conference, 2011:1–13.
Poljanšek I, Krajnc M. Characterization of Phenol-Formaldehyde Prepolymer Resins by In Line FT-IR Spectroscopy. Acta Chim. Slov., 2005, 52: 238–244.
De-en Jiang, van Duin ACT, Goddard III W A, et al. Simulating the Initial Stage of Phenolic Resin Carbonization via the ReaxFF Reactive Force Field. J. Phys. Chem. A, 2009,113: 6891–6894.
Alonso M V, Oliet M, Dominguez J C, et al. Thermal degradation of lignin-phenol-formaldehyde and phenol-formaldehyde resol resins. Journal of Thermal Analysis and Calorimetry, 2011,105: 349–356.
Desai T G, Lawson J W, Keblinski P. Modeling initial stage of phenolic pyrolysis: Graphitic precursor formation and interfacial effects. Polymer, 2011, 52: 577–585.
Reghunadhan Nair C P, Bindu R L, Ninan K N. Addition curable phenolic resins based on ethynyl phenyl azo functional novilac. Polymer, 2002,43: 2609–2617.
Chen Z, Chen Y, Liu H. Pyrolisis of phenolic resin by TG-MS and FTIR analysis. Advanced Materials Research, 2013, 631-632: 104–109.
Yangfei Ch, Zhiqin Ch, Shaoyi X, et al. A novel thermal degradation mechanism of phenol-formaldehyde type resins. ThermochimicaActa, 2008, 476: 39–43.
Zhao Y, Yan N, Feng M W. Thermal degradation characteristic of phenol -formaldehyde resins derived from beetle infested pine barks. ThermochimicaActa, 2013, 555: 46–52.
Jiang H, Wang J, Wu S, et al. The pyrolysis mechanism of phenol formaldehyde resin. Polymer Degradation and Stability, 2012, 97: 1527–1533.
Poljanšek I, Šebenik U, KrajncM. Characterization of phenolurea-formaldehyde resin by inline FTIR Spectroscopy. Journal of Applied Polimer Science, 2006, 99: 2016–2028.
Costa L, di Montelera L R, Camino G C, et al. Structure-charring relationship on phenol-formaldehyde type resins. Polymer Degradation and Stability, 1997, 56: 23–35.
Bates C E, Scott W D. The decomposition of resin binders and relationship between gases formed and the casting surface quality, part 2 -gray iron. AFS Transactions, 1980, 76: 793–804.
Winardi L, Griffin R D, Littleton H E, et al. Variables Affecting Gas Evolution Rates and Volumes from Cores in Contact with Molten Metal. AFS Transactions, 2007,116: 505–521.
McKinley M D, Lytle C A, Bertsch W. Pyrolysis of core resins used in metalcasting. AFS Transactions, 2007,407–412.
Holtzer M, Bobrowski A, Dańko R, et al. Emission of polycyclic aromatic hydrocarbons (PAHs) and benzene, toluene, ethylbenzene and xylene (BTEX) from the furan moulding sands with addition of the reclaim. Metalurgija, 2014, 53 (4): 451–54.
Bobrowski A, Holtzer M, Żymankowska-Kumon S, et al. Harmfulness assessment of moulding sands with a geopolymer binder and a new hardener, in an aspect of the emission of substances from the BTEX group. Archives of Metallurgy and Materials, 2015, 60 (1): 341–344.
Bobrowski A, Holtzer M, Dańko R, et al. Analysis of gases emitted during a thermal decomposition of the selected phenolic binders. Metalurgia International, 2013,18 (7): 259–261.
Holtzer M, Bobrowski A, Dańko R, et al. Influence of a liquid metal temperature on a thermal decomposition of a phenolic resin. Archives of Foundry Engineering, 2013,13 (2): 35–38.
Grabowska B, Holtzer M, Eichholz S, et al. Thermal analysis of a sodium salt of the maleic acid-acrylic acid copolymer used as a polymeric binder. Polimery, 2011, 56 (2): 62–66.
Kaczmarska K, Grabowska B, Drożyński D, et al. Modified polysaccharides as alternative binders for foundry industry. Metalurgija, 2016, 55 (4): 839–842.
Grabowska B, Bobrowski A, Grabowski G, et al. Thermoanalytical studies (TG-DSC, FTIR-DRS) of the mouding sand with the polymer BioCO2 binder. Archives of Foundry Engineering, 2015,15 (1): 27–30.
Bobrowski A, Grabowska B. The impact of temperature on furan resin and binder structure. Metallurgy and Foundry Engineering, 2012, 38(1): 73–80.
Conley R T, Bieron J F. A kinetic study of the oxidative degradation of phenol-formaldehyde polycondensates using infrared spectroscopy. Journal of Applied Polymer Science, 1963, 7:103–117.
Lochte H W, Strauss E L, Conley R T. The thermo-oxidative degradation of phenol-formaldehyde polycondensates: Thermog ravi metric and elemental composition studies of char formation. Journal of Applied Polymer Science, 1965, 9: 2799–2810.
Jackson W M, Conley R T. High temperature oxidative degradation of phenol-formaldehyde polycondensates. Journal of Applied Polymer Science, 1964, 8: 2163–2193.
Chang Ch, Tackett J R. Characterization of phenolic resins with thermogravimetry-mass spectrometry. Thermochimica Acta. 1991,192:181–190.
Chen Y, Chen Z, Xiao S, et al. A novel thermal degradation mechanism of phenol-formaldehyde type resins. Thermochim Acta, 2008, 476 (1-2): 39–43.
Alonso M V, Oliet M, Dominguez J C, et al. Thermal degradation of lignin-phenol-formaldehyde and phenol-formaldehyde resol resins. Therm Anal Calorim, 2011,105: 349–356.
Chen Y, Fan D, Qin T, et al. Thermal degradation and stability of accelerated-curing phenol-formaldehyde resin. BioResources, 2014, 9 (3): 4063–4075.
Jiang H, Wang J, Wu S, et al. The pyrolysis mechanism of phenol formladehyde resin. Polymer Degradation and Stability, 2012, 97: 1527–1533.
Bobrowski A. Analysis of gases from BTEX group by Fourier Transform Infrared Spectroscopy (FTIR). Archives of Foundry Engineering, 2014, 14 (4): 17–20.
Żymankowska-Kumon S, Bobrowski A, Grabowska B. Comparison of the emission of aromatic hydrocarbons from moulding sands with furfural resin with the low content of furfuryl alcohol and different activators. Archives of Foundry Engineering, 2016, 16 (4): 187–190.
Holtzer M, Dańko R, Żymankowska-Kumon S, et al. Assessment of the harmfulness of moulding sands with alkyd resin subjected to the high temperature influence. Archives of Metallurgy and Materials, 2016, 61 (4): 2171–2176.
Šupová M, Svítilová J, Chlup Z, et al. Relation between mechanical properties and pyrolysis temperature of phenol formaldehyde resin for gas separation membranes. Ceramics-Silikáty, 2012, 56(1): 40–49.
Manocha S M, Patel K, Manocha L M. Development of carbon foam from phenolic resin via template route. Indian Journal of Engineering & Materials Science, 2010,17: 388–342.
Ma T F, Wang X F, Yang F L. Effect of Carbonization Temperature on the Elastic Modulus of Resin Carbon. Advanced Materials Research, 2015, 1079-1080: 83–87.
Gerakines P A, Schutte W A, Greenberg J M, et al. The infrared band strengths of H2O, CO and CO2 in laboratory simulations of astrophysical ice mixtures. Astronomy and Astrophysics, 1995, 296: 810–818.