Structural Changes and Thermal Stability of Charged LiNixMnyCozO2 Cathode Materials Studied by Combined In Situ Time-Resolved XRD and Mass Spectroscopy

American Chemical Society (ACS) - Tập 6 Số 24 - Trang 22594-22601 - 2014
Seong‐Min Bak1, Enyuan Hu2, Yong‐Ning Zhou2, Xiqian Yu2, Sanjaya D. Senanayake2, Sung Jin Cho3, Kwang‐Bum Kim4, Kyung Yoon Chung5, Xiao Qing Yang2, Kyung‐Wan Nam6
1Chemistry Department, Brookhaven National Laboratory, Upton, New York 11973 (United States)
2Chemistry#R#Department, Brookhaven National Laboratory, Upton, New York 11973 United States
3Joint School of Nano Science & Nano Engineering, North Carolina A&T State University, Greensboro, North Carolina 27401, United States
4Department#R#of Material Science and Engineering, Yonsei University, Seoul 120-749, Republic of Korea
5Center#R#for Energy Convergence Research, Korea Institute of Science and Technology (KIST), Seoul 136-791, Republic of Korea
6Department#R#of Energy and Materials Engineering, Dongguk University, Seoul 100-715, Republic of Korea

Tóm tắt

Từ khóa


Tài liệu tham khảo

Armand M., 2008, Nature, 451, 652, 10.1038/451652a

Goodenough J. B., 2010, Chem. Mater., 22, 587, 10.1021/cm901452z

Thackeray M. M., 2012, Energy Environ. Sci., 5, 7854, 10.1039/c2ee21892e

Weaving J. S., 2001, J. Power Sources, 97, 733, 10.1016/S0378-7753(01)00700-5

Lee K. K., 2001, J. Power Sources, 97, 308, 10.1016/S0378-7753(01)00516-X

Cao H., 2004, J. Alloys Compd., 376, 282, 10.1016/j.jallcom.2004.01.008

Yabuuchi N., 2003, J. Power Sources, 119, 171, 10.1016/S0378-7753(03)00173-3

Wang Y. D., 2007, Electrochem. Commun., 9, 2534, 10.1016/j.elecom.2007.07.033

Martin C., 2014, Nat. Nanotechnol., 9, 327, 10.1038/nnano.2014.92

Trippe A., 2013, Energytech, 1

Kim T. H., 2012, Adv. Energy Mater., 2, 860, 10.1002/aenm.201200028

Belharouak I., 2006, Electrochem. Commun., 8, 329, 10.1016/j.elecom.2005.12.007

Dahn J. R., 1994, Solid State Ionics, 69, 265, 10.1016/0167-2738(94)90415-4

Yoon W. S., 2006, Electrochem. Commun., 8, 1257, 10.1016/j.elecom.2006.06.005

Wu L. J., 2011, Chem. Mater., 23, 3953, 10.1021/cm201452q

Kim Y., 2012, ACS Appl. Mater. Interfaces, 4, 2329, 10.1021/am300386j

Hwang B. J., 2003, Chem. Mater., 15, 3676, 10.1021/cm030299v

Sun Y. K., 2009, Nat. Mater., 8, 320, 10.1038/nmat2418

Konishi H., 2011, J. Power Sources, 196, 6884, 10.1016/j.jpowsour.2011.01.016

Konishi H., 2013, J. Power Sources, 244, 23, 10.1016/j.jpowsour.2013.05.004

Bak S. M., 2013, Chem. Mater., 25, 337, 10.1021/cm303096e

Toby B. H., 2001, J. Appl. Crystallogr., 34, 210, 10.1107/S0021889801002242

Guilmard M., 2003, Chem. Mater., 15, 4484, 10.1021/cm030340u

Guilmard M., 2003, Chem. Mater., 15, 4476, 10.1021/cm030059f

Yoon W. S., 2005, Electrochem. Solid State Lett., 8, A83, 10.1149/1.1846714

Nam K. W., 2009, J. Power Sources, 189, 515, 10.1016/j.jpowsour.2008.10.130

Nam K. W., 2013, Adv. Funct. Mater., 23, 1047, 10.1002/adfm.201200693

Cho Y. H., 2013, J. Alloys Compd., 562, 219, 10.1016/j.jallcom.2013.02.060

Xiao J., 2008, Chem. Mater., 20, 7454, 10.1021/cm802316d

Shinova E., 2008, Solid State Ionics, 179, 2198, 10.1016/j.ssi.2008.07.026

Yabuuchi N., 2008, Chem. Mater., 20, 4936, 10.1021/cm800314d

Wang L., 2007, Chem. Mater., 19, 543, 10.1021/cm0620943

Reed J., 2004, Chem. Rev., 104, 4513, 10.1021/cr020733x