Spall Strength of Shock-Heated Hafnium and the Equation of State of Its Polymorphic Modifications
Tóm tắt
We determined the spall strength of hafnium heated by a loading shock wave to thousands of degrees and subjected to transformations into denser polymorphic modifications. To achieve this goal, the following tasks were solved. The pressure profiles at the interface between the sample and soft buffer material in the spall experiments with flat, one-dimensional loading are measured. The equations of state of three polymorphic modifications of hafnium are constructed in the pressure range up to 100 GPa. The thermodynamic states of hafnium were calculated under the conditions of the performed experiments, which, together with the results of measurements of pressure profiles, made it possible to determine the spall strength of hafnium heated in a cycle of shock compression–unloading. The spall strength of hafnium was –4(1) GPa at a temperature of 1680(380) K. The spall experiments were mathematically simulated in the framework of a one-dimensional hydrocode.
Tài liệu tham khảo
A. M. Molodets, A. S. Savinykh, A. A. Golyshev, and G. V. Garkushin, Tech. Phys. Lett. 45, 27 (2019).
K. A. Gschneidner, Solid State Phys. 16, 275 (1964).
D. E. Grady and M. E. Kipp, in High-Pressure Shock Compression of Condensed Matter, Ed. by J. R. Asay and M. Shahinpoor (Springer, New York, 1992), p. 265.
A. A. Golyshev and A. M. Molodets, Combust. Explos., Shock Waves 49, 219 (2013).
Shock Hugoniot Data, Ed. by S. P. Marsh (Univ. California LASL, Berkeley, 1980).
S. A. Ostanin and V. Y. Trubitsin, Comput. Mater. Sci. 17, 174 (2000).
R. Hrubiak, PhD Thesis (Florida Int. Univ., Miami, 2012).
Cheng-Bin Zhang, Wei-Dong Li, Ping Zhang, and Bao-Tian Wang, Comput. Mater. Sci. 157, 121 (2019).
R. McQueen, S. Marsh, J. Taylor, J. Fritz, and W. Carter, in High Velocity Impact Phenomena, Ed. by R. Kinslow (Academic, New York, 1970), p. 293.
A. A. Bakanova, I. P. Dudoladov, and Yu. N. Sutulov, Sov. Phys. Solid State 11, 1515 (1969).
A. M. Molodets, J. Exp. Theor. Phys. 80, 467 (1995).
A. M. Molodets, High Press. Res. 30, 325 (2009).
L. V. Al’tshuler, S. B. Kormer, A. A. Bakanova, and R. F. Trunin, Sov. Phys. JETP 11, 573 (1960).
K. Pandey, J. Gyanchandani, M. Somayazulu, G. K. Dey, Surinder M. Sharma, and S. K. Sikka, J. Appl. Phys. 115, 233513 (2014).
V. V. Kim, A. A. Golyshev, D. V. Shakhrai, and A. M. Molodets, in Proceedings of the 11th International Conference Zababakhin’ Scientific Readings, Snezhinsk, 2012. http://www.vniitf.ru/images/zst/2012/s6/6-24.pdf.
A. M. Molodets, Phys. Solid State 57, 2045 (2015).
W. Carter and S. Marsh, Report No. LA-13006-MS (Los Alamos National Labor., NM, 1995).
A. M. Molodets, Phys. Solid State 56, 2233 (2014).