Simulating porcelain firing effect on the structure, corrosion and mechanical properties of Co–Cr–Mo dental alloy fabricated by soft milling
Shigaku = Odontology - Trang 1-18 - 2023
Tóm tắt
This study aims at evaluating the effect of simulating porcelain firing on the microstructure, corrosion behavior and mechanical properties of a Co–Cr–Mo alloy fabricated by Metal Soft Milling (MSM). Two groups of Co-28Cr-5Mo specimens (25 × 20 × 3 mm) were prepared by MSM: The as-sintered (AS) specimens and the post-fired (PF) specimens that were subjected to 5 simulating porcelain firing cycles without applying the ceramic mass onto their surface. Phase identification by X-ray Diffraction (XRD), microstructure examination by optical microscopy and Scanning Electron Microscopy combined with Energy-Dispersive X-ray Spectroscopy (SEM/EDX), corrosion testing by cyclic polarization and chronoamperometry in simulated body fluid (SBF), the latter test accompanied by Cr3+ and Cr6+ detection in the electrolyte through the 1.5-diphenylcarbazide (DPC) method and UV/visible spectrophotometry, and mechanical testing by micro-/nano-indentation were conducted to evaluate the effect of the post-firing cycles on the properties of Co–Cr–Mo. The results were statistically analyzed by the t test (p < 0.05: statistically significant). All specimens had a mixed γ-fcc and ε-hcp cobalt-based microstructure with a dispersion of pores filled with SiO2 and a fine M23C6 intergranular presence. PF led to an increase in the ε-Co content and slight grain coarsening. Both AS and PF alloys showed high resistance to general and localized corrosion, whereas neither Cr6+ nor Cr3+ were detected during the passivity-breakdown stage. PF improved the mechanical properties of the AS-alloy, especially the indentation modulus and true hardness (statistically significant differences: p = 0.0009 and 0.006, respectively). MSM and MSM/simulating-porcelain firing have been proven trustworthy fabrication methods of Co–Cr–Mo substrates for metal-ceramic prostheses. Moreover, the post-firing cycles improve the mechanical behavior of Co–Cr–Mo, which is vital under the dynamically changing loads in the oral cavity, whereas they do not degrade the corrosion performance.
Tài liệu tham khảo
Sakaguchi RL, Ferracane R. Powers JM. Graig’s restorative dental materials. 14th ed. St. Louis: Mosby; 2018.
Yan X, Lin H, Wu Y, Bai W. Effect of two heat treatments on mechanical properties of selective-laser-melted Co–Cr metal-ceramic alloys for application in thin removable partial dentures. J Prosthet Dent. 2018;119(1028):e1-6.
Al Jabbari YS. Physico-mechanical properties and prosthodontic applications of Co–Cr dental alloys: a review of the literature. J Adv Prosthodont. 2014;6:138–45.
Sahami-Nejad M, Lashgari HR, Zangeneh Sh, Kong C. Determination of residual stress on TIG-treated surface via nanoindentation technique in Co–Cr–Mo-C alloy. Surf Coat Technol. 2019;380:125020.
Al Jabbari YS, Barmpagadaki X, Psarris I, Zinelis S. Microstructural, mechanical, ionic release and tarnish resistance characterization of porcelain fused to metal Co–Cr alloys manufactured via casting and three different CAD/CAM techniques. J Prosthodont Res. 2019;63:150–6.
Dimitriadis K, Lekatou AG, Sfikas A, Roumpi M, Tsouli S, Galiatsatos A, Agathopoulos S. Influence of heat-treatment cycles on microstructure, mechanical properties, and corrosion resistance of Co–Cr dental alloys fabricated by selective-laser-melting. J Mater Eng Perform. 2021;30:5252–65.
Barazanchi A, Li KC, Al-Amleh B, Lyons K, Waddell N. Additive technology: update on current materials and applications in dentistry. J Prosthodont. 2017;26:156–63.
Koutsoukis T, Zinelis S, Eliades G, Al-Wazzan K, Rifaiy MA, Al Jabbari YS. Selective laser melting technique of Co–Cr dental alloys: a review of structure and properties and comparative analysis with other available techniques. J Prosthodont. 2015;24:303–12.
Dimitriadis K, Spyropoulos K, Papadopoulos T. Metal-ceramic bond strength between a feldspathic porcelain and a Co–Cr alloy fabricated with direct metal laser sintering technique. J Adv Prosthodont. 2018;10:25–31.
Hong MH, Lee DH, Hanawa T, Kwon TY. Comparison of microstructures and mechanical properties of 3 cobalt-chromium alloys fabricated with soft metal milling technology. J Prosthet Dent. 2022;127:489–96.
Reclaru L, Ardelean LC. Alternative processing techniques for CoCr dental alloys. In: Narayan R, editor. Encyclopedia of biomedical engineering, vol. 1. Philadelphia: Elsevier; 2019. p. 1–15.
Munir K, Biesiekierski A, Wen C, Li Y. Selective laser melting in biomedical manufacturing. In: Wen C, editor. Metallic biomaterials processing and medical device manufacturing (ch. 7). Chennai: Woodhead Publishing; 2020. p. 235–69.
Stawarczyk B, Eichberger M, Hoffmann R, Noack F, Schweiger J, Edelhoff D, Beuer F. A novel CAD/CAM base metal compared to conventional CoCrMo alloys: an in-vitro study of the long-term metal-ceramic bond strength. Oral Health Dent Manag. 2014;13:446–52.
Jang SH, Min BK, Hong MH, Kwon TY. Effect of different post-sintering temperatures on the microstructures and mechanical properties of a presintered Co–Cr alloy. Metals. 2018;8:1036.
Önöral Ö, Ulusoy M, Seker E, Etikan İ. Influence of repeated firings on marginal, axial, axio-occlusal, and occlusal fit of metal-ceramic restorations fabricated with different techniques. J Prosthet Dent. 2018;120:415–20.
Daou EE. Effect of ceramic layering on the fit of cobalt-chromium alloy 3-unit fixed dental prostheses fabricated by additive, soft milling, and casting technologies. J Prosthet Dent. 2021;126:130e-e137.
Kim HR, Kim YK, Son JS, Min BK, Kim KH, Kwon TY. Comparison of in vitro biocompatibility of a Co–Cr dental alloy produced by new milling/post-sintering or traditional casting technique. Mater Lett. 2016;178:300–3.
Kocaağaoğlu H, Albayrak H, Kilinc HI, Gümüs HÖ. Effect of repeated ceramic firings on the marginal and internal adaptation of metal-ceramic restorations fabricated with different CAD-CAM technologies. J Prosthet Dent. 2017;118:672–7.
Rylska D, Januszewicz B, Sokołowski B, Sokołowski J. Corrosion resistance of Cr–Co alloys subjected to porcelain firing heat treatment-in vitro study. Processes. 2021;9:636.
Barazanchi A, Li K, Al-Amleh B, Lyons K, Waddell J. Mechanical properties of laser-sintered 3D-printed cobalt chromium and soft-milled cobalt chromium. Prosthesis. 2020;2:313–20.
Kim HR, Jang SH, Kim YK, Son JS, Min BK, Kim KH, Kwon TY. Microstructures and mechanical properties of Co–Cr dental alloys fabricated by three CAD/CAM based processing techniques. Materials. 2016;9:596.
Jang SH, Lee DH, Ha JY, Hanawa T, Kim KH, Kwon TY. Preliminary evaluation of mechanical properties of Co–Cr alloys fabricated by three new manufacturing processes. Int J Prosthodont. 2015;28:396–8.
Ogunc A, Avcu GY. Effect of repeated firings on the marginal and internal adaptation of implant-supported metal-ceramic restorations fabricated with different thicknesses and fabrication methods. J Prosthet Dent. 2021;125:504e1-6.
ISO:10271. Dentistry—corrosion test methods for metallic materials. Switzerland, Geneva: International Organization for Standardization; 2011.
Sage M, Guillaud C. Méthode d′analyse quantitative des variétés allotropiques du cobalt pre les Rayons X. Rev Metall. 1950;49:139–45.
Bellini D, Cencetti C, Meraner J, Stoppoloni D, D’Abusco AS, Matricardi P. An in-situ gelling system for bone regeneration of osteochondral defects. Eur Polym J. 2015;72:642–50.
Lekatou AG, Sfikas AK, Karantzalis AE. The influence of the fabrication route on the microstructure and surface degradation properties of Al reinforced by Al9Co2. Mater Chem Phys. 2017;200:33–49.
Sfikas AK, Lekatou AG. Electrochemical behavior of Al–Al9Co2 alloys in sulfuric acid. Corros Mater Degrad. 2020;1:249–72.
Lekatou AG, Sioulas D, Karantzalis AE, Grimanelis D. A comparative study on the microstructure and surface property evaluation of coatings produced from nanostructured and conventional WC–Co powders HVOF-sprayed on Al7075. Surf Coat Technol. 2015;276:539–56.
Revie RW. Uhlig’s Corrosion Handbook. 3rd ed. New Jersey: John Wiley & Sons; 2011.
Kostas V, Baikousi M, Dimos K, Vasilopoulos KC, Koutselas I, Karakassides MA. Efficient and rapid photocatalytic reduction of hexavalent chromium achieved by a phloroglucinol-derived microporous polymeric organic framework solid. J Phys Chem C. 2017;121(13):7303–11.
ASTM E384–22. Standard Test Method for Microindentation Hardness of Materials. Pennsylvania: American Society for Testing and Materials; 2022.
Okamoto H. Supplemental literature review of binary phase diagrams: Ag-Yb, Al-Co, Al-I, Co–Cr , Cs-Te, In-Sr, Mg-Tl, Mn-Pd, Mo-O, Mo-Re, Ni-Os, and V-Zr. J Phase Equil Diffus. 2016;37:726–37.
Kajima Y, Takaichi A, Kittikundech N, Nakamoto T, Kimura T, Kawasaki A, Hanawa T, Takahashi H, Wakabayashi N. Effect of heat-treatment temperature on microstructures and mechanical properties of Co–Cr–Mo alloys fabricated by selective laser melting. Mater Sci Eng A. 2018;726:21–31.
Lashgari HR, Zangeneh Sh, Hasanabadi F, Saghaf M. Microstructural evolution during isothermal aging and strain-induced transformation followed by isothermal aging in Co–Cr–Mo-C alloy: a comparative study. Mater Sci Eng A. 2010;527:4082–91.
Li J, Chen C, Liao J, Liu L, Ye X, Lin S, Ye J. Bond strengths of porcelain to cobalt-chromium alloys made by casting, milling, and selective laser melting. J Prosthet Dent. 2017;118:69–75.
Karantzalis AE, Lekatou A, Diavati E. Effect of destabilization heat treatments on the microstructure of high-chromium cast iron: a microscopy examination approach. J Mater Eng Perform. 2009;18:1078–85.
Karantzalis AE, Lekatou A, Kapoglou A, Mavros H, Dracopoulos V. Phase transformations and microstructural observations during subcritical heat treatments of a high-chromium cast iron. J Mater Eng Perform. 2012;21:1030–9.
Singh R, Schneibel JH, Divinski S, Wilde G. Grain boundary diffusion of Fe in ultrafine-grained nanocluster-strengthened ferritic steel. Acta Mater. 2011;59:1346–53.
Robino CV. Representation of mixed reactive gases on free energy (Ellingharn-Richardson) diagrams. Metall Mater Trans B. 1996;27B:65–9.
Hodgson AWE, Kurz S, Virtanen S, Fervel V, Olsson COA, Mischler S. Passive and transpassive behaviour of CoCrMo in simulated biological solutions. Electrochim Acta. 2004;49:2167–78.
Milošev I, Strehblow HH. The composition of the surface passive film formed on CoCrMo alloy in simulated physiological solution. Electrochim Acta. 2003;48:2767–74.
Pourbaix M. Atlas of electrochemical equilibria in aqueous solutions. 2nd ed. Houston: NACE International; 1974.
Efremenko VG, Lekatou AG, Chabak YG, Efremenko BV, Petryshynets I, Zurnadzhy VI, Emmanouilidou S, Vojtko M. Micromechanical, corrosion and wet sliding wear behaviours of Co-28Cr-6Mo alloy: wrought vs. LPBF. Mater Today Commun. 2023. https://doi.org/10.1016/j.mtcomm.2023.105936. (Available online 5 April 2023).
Bettini E, Leygraf C, Pan J. Nature of current increase for a CoCrMo Alloy: “transpassive” dissolution vs. water oxidation. Int J Electrochem Sci. 2013;8:11791–804.
Kurosu Sh, Matsumoto H, Chiba A. Isothermal phase transformation in biomedical Co-29Cr-6Mo alloy without addition of carbon or nitrogen. Metall Mater Trans. 2010;41A:2613–25.
Al Jabbari YS, Koutsoukis T, Barmpagadaki X, Zinelis S. Metallurgical and interfacial characterization of PFM Co–Cr dental alloys fabricated via casting, milling or selective laser melting. Dent Mater. 2014;30:e79-88.
dos Santos C, Habibe AF, Simba BG, Lins JFC, Freitas BX, Nunes CA. CoCrMo-base alloys for dental applications obtained by selective laser melting (SLM) and CAD/CAM. Mat Res. 2020;23:e20190599.
Mengucci P, Barucca G, Gatto A, Bassoli E, Denti L, Fiori F, Girardin E, Bastianoni P, Rutkowski B, Czyrska-Filemonowicz A. Effects of thermal treatments on microstructure and mechanical properties of a Co–Cr–Mo–W biomedical alloy produced by laser sintering. J Mech Behav Biomed Mater. 2016;60:106–17.
Saber-Samandari S, Berndt CC, Gross KA. Selection of the implant and coating materials for optimized performance by means of nanoindentation. Acta Biomater. 2011;7:874–81.
Yu JM, Kang SY, Lee JS, Jeong HS, Lee SY. Mechanical properties of dental alloys according to manufacturing process. Materials. 2021;14:3367.
Fu W, Liu S, Jiao J, Xie Z, Huang X, Lu Y, Liu H, Hu S, Zuo E, Kou N, Ma G. Wear resistance and biocompatibility of Co–Cr dental alloys fabricated with Cast and SLM techniques. Materials. 2022;15(9):3263.
Chudoba T. Measurement of hardness and Young’s modulus by nanoindentation. In: Cavaleiro A, De Hosson JTM, editors. Nanostructured coatings (Nanostructure science and technology). New York: Springer; 2006. p. 216–60.
Labonte D, Lenz AK, Oyen ML. On the relationship between indentation hardness and modulus, and the damage resistance of biological materials. Acta Biomater. 2017;57:373–83.
Sakai M. The Meyer hardness: A measure for plasticity? J Mater Res. 1999;14:3630–9.
Sakaguchi RL, Powers JM. Graig’s restorative dental materials. 13th ed. Philadelphia: Elsevier; 2011.