Self-Bonded Zeolite Beta/MCM-41 Composite Spheres
Tóm tắt
Self-bonded zeolite Beta/MCM-41 composite spheres were prepared using a two-step synthesis procedure. In the first step, mesoporous zeolite Beta spheres were obtained using anion exchange resin as macrotemplate. In the second step, the MCM-41 or Al-MCM-41 was grown both on sphere surfaces and in the pore structure of the pre-formed zeolite Beta spheres. Finally, the templating agents used in the synthesis of mesophase were removed by calcination leaving behind self-bonded Beta/MCM-41 composite spheres. Beta/MCM-41 composites were characterized by XRD, SEM and nitrogen adsorption measurements. Materials with controlled macroshape, composition and complex porosity were prepared by the approach.
Tài liệu tham khảo
J.S. Beck, J.C. Vartuli, W.J. Roth, M.E. Leonowicz, C.T. Kresge, K.D. Schmitt, C.T-W. Chu, D.H. Olson, E.W. Sheppard, S.B. McCullen, J.B. Higgins, and J.L. Schlenker, J. Am. Chem. Soc. 114, 10834 (1992).
Karlsson, M. Stöcker, and R. Schmidt, Microporous Mesoporous Mater. 27, 181 (1999).
X. Chen and S. Kawi, Chem. Commun. 1354 (2001).
L. Huang, W. Guo, P. Deng, Z. Xue, and Q. Li, J. Phys. Chem. B 104, 2817 (2000).
W. Guo, C. Xiong, L. Huang, and Q. Li, J. Mater. Chem. 11, 1886 (2001).
M.J. Verhoef, P.J. Kooyman, J.C. van der Waal, M.S. Rigutto, J.A. Peters, and H. van Bekkum, Chem. Mater. 13, 683 (2001).
K.R. Kloestra, H.W. Zandbergen, J.C. Jansen, and H. van Bekkum, Microporous Mater. 6, 287 (1996).
D.T. On and S. Kaliaguine, Angew. Chem. Int. Ed. 41, 1036 (2002).
P. Prokešova, S. Mintova, J. Čejka, and T. Bein, Microporous Mesoporous Mater. 64, 165 (2003).
L. Tosheva, B. Mihailova, V. Valtchev, and J. Sterte, Microporous Mesoporous Mater. 35/36, 621 (2001).
M.E. Davis, Nature 417, 813 (2002).
R.C. Hayward, P. Alberius-Henning, B.F. Chmelka, and G.D. Stucky, Microporous Mesoporous Mater. 44/45, 619 (2001).
L. Tosheva, V. Valcthev, and J. Sterte, Microporous Mesoporous Mater. 48, 31 (2000).
Y. Goto, Y. Fukushima, P. Ratu, Y. Imada, K. Kuboda, Y. Sugi, M. Ogura, and M. Matsukata, J. Por. Mater. 9, 43 (2002).