The segregation of thermal diffusion salt bath chromizing process was analyzed. The experimental chromizing ingredients were prepared by the four groups A, B, C, and D. In order to study the segregation status of this case, the cooling molten salt in the crucible was removed by drilling from the heart core of molten salt. The core of molten salt was analyzed by X-ray fluorescence spectroscopy and XRD. Through the analysis, we can conclude that the Cr element deposited in the bottom was 4.51 times than the top. Chloride added to the molten salt will reduce segregation. Meantime we proposed some measures to overcome the segregation problem.
Từ khóa
Tài liệu tham khảo
Liu XJ, Wang HC, Li YY. Effects of Rare Earths in Borax Salt Bath Immersion Vanadium Carbide Coating Process on Steel Substrate[J]. Surface&Coatings Technology, 2008, 202:4 788–4 792
Liu XJ, Wang HC, Li DW, Wu YX. Study on Kinetics of Carbide Coating Growth by Thermal Diffusion Process [J]. Surface & Coatings Technology, 2006, 201: 2 414–2 418
Wu YX. Study on Thermal Diffusion on Cold Extrusion Die [D]. Wuhan: Wuhan University of Technology, 2006
Liu XJ. Study on Vanadium Carbide Coating on Die Steels by Thermal Diffusion Process [D]. Wuhan: Wuhan University of Technology, 2007
Saduman Sen. The Characterization of Vanadium Boride Coatings on AISI 8620 Steel [J]. Surface & Coatings Technology, 2005, 190: 1–6
Herrera Y, Grigorescu IC, Ramirez J, DiRauso C, Staia MH. Micro Structural Characterization of Vanadium Carbide Laser Clad Coatings [J]. Surface & Coatings Technology, 1998, 108–109: 308–311
Aghaie-Khafri M, Fazlalipour F. Vanadium Carbide Coatings on Die Steel Deposited by the Thermoreactive Diffusion Technique [J]. Journal of Physics and Chemistry of Solids, 2008, 69: 2 465–2 470
Ugur Sen. Wear Properties of Niobium Carbide Coatings Performed by Pack Method on AISI 1040 Steel[J]. Thin Solid Films, 2005, 483: 152–157
Saduman Sen. A Stuay on Kinetics of CrxC. Coated High. Chromium Steel by Thermo-Reactive Diffusion Technique [J]. Vacuum, 2005, 79: 63–70
WANG Huachang, Qu Peng, Zhang Ying. Study on Corrosion Resistance and Oxidation Resistance of Materials Used in Borax Bath [J]. Material & Heat Treatment, 2010, 40(4): 27–33
WANG Hongfu, WANG Huachang, WANG Xiao. Ni60-SiC Coating Prepared by Plasma Spraying, Plasma Re-melting and Plasma Spray Welding on Surface of Hot Forging Die [J]. Journal of Wuhan University of Technology-Materials Science Edition, 2011, 26(4): 715–718
WANG Hongfu, WANG Huachang, PAN Chenggang. Vanadium Carbide Coating Growth on Die Steel Substrate in Borax Salt Bath [J]. Journal of Wuhan University of Technology-Materials Science Edition, 2010, 25(4): 600–603
WANG Hongfu. Research on TD Technology Several Key Issues [D]. Wuhan: Wuhan University of Technology, 2010