Residual failure pressures and fatigue life of filament-wound composite pipes subjected to lateral impact

SAGE Publications - Tập 46 Số 15 - Trang 1787-1794 - 2012
Murat Sari1, Ramazan Karakuzu1, Mehmet Emin Deniz1, Bülent Murat İçten1
1Department of Mechanical Engineering, Dokuz Eylül University, 35100 Izmir, Turkey

Tóm tắt

This study presents the effect of impact energy on the static failure pressures, and fatigue life of composite pipes. The specimens manufactured have inner diameter 100 mm and length 400 mm. Impact tests were realized at three different energy levels 5.0, 7.5, and 10.0 J. Force–deflection curves were plotted. Impacted and non-impacted specimens were subjected to internal pressure statically and dynamically to obtain failure pressure and fatigue life of the composite pipe, respectively. Results indicate that leakage and eruption pressures for static test decrease and perspiration, leakage, and eruption cycles decrease by lateral impact.

Từ khóa


Tài liệu tham khảo

Sari M. Sea water effect on composite pipes subjected to impact loading. MSc thesis, Graduate School of Natural and Applied Sciences, Dokuz Eylül University, 2010.

10.1016/j.compstruct.2008.06.021

10.1016/S1359-8368(00)00037-8

10.1016/S1359-8368(00)00014-7

Naik MK. The effect of environmental conditions on the hydrostatic burst pressure and impact performance of glass fiber reinforced thermoset pipes. MSc thesis, Kinh Fahd University of Petroleum & Minerals, Dhahran, 2005.

10.1016/j.compstruct.2009.07.027

10.1016/j.compositesb.2004.11.004

10.1177/0021998305048733

10.1177/0021998307074144

10.1177/002199803031032

10.1016/j.tws.2008.01.016

10.1016/j.compositesa.2005.12.010

10.1016/j.compositesa.2006.10.011

10.1007/s10853-008-2820-x

10.1016/j.compstruct.2006.05.015

10.1016/j.matdes.2009.04.025

10.1016/j.compositesa.2006.04.011

10.1177/0731684408094068

10.1016/j.ijhydene.2009.04.037

Thông tin
Thông tin xuất bản

SAGE Publications

Tập 46 Số 15

1787-1794

Thông tin tác giả