Reduced Lithium/Nickel Disorder Degree of Sodium‐Doped Lithium‐Rich Layered Oxides for Cathode Materials: Experiments and Calculations

ChemElectroChem - Tập 7 Số 1 - Trang 246-251 - 2020
Yongyuan Hu1, Zhongzheng Qin1, Jian Pei1, Bowen Cong1, Xu Yang1, Gang Chen1
1MIIT Key Laboratory of Critical Materials Technology for New Energy Conversion and Storage, School of Chemistry and Chemical Engineering, Harbin Institute of Technology, Harbin, 150001, P. R. China

Tóm tắt

AbstractSluggish kinetics and poor electrochemical stability limit the implications of Li‐rich layered oxide cathode materials, which are regarded as one of the most promising potential cathode materials for lithium‐ion batteries. In this work, a Na‐doped Li‐rich layered oxide (abbreviated as N‐LLO) cathode material is prepared through co‐precipitation combined with calcination. During the annealing process, partial Li2CO3 is substituted by Na2CO3, which helps to optimize the primary particles and realize Na doping. The obtained N‐LLO cathode exhibits a greater specific capacity and excellent rate performance. The characterization and DFT calculations suggest that the doped Na ions could reduce the formation of Li/Ni disorder defects, change local bond length, and enlarge Li interslab spacing conducive to Li‐ion diffusion, improving the rate performance.

Từ khóa


Tài liệu tham khảo

 

10.1038/451652a

10.1021/ja507828x

 

10.1039/b702425h

10.1021/ja108588y

 

Shi J. L., 2018, Adv. Mater., 30

10.1002/adma.201702794

10.1149/2.0071514jes

10.1038/s41560-018-0097-0

 

10.1016/j.nanoen.2016.10.066

10.1002/aenm.201300950

 

10.1149/2.0351701jes

10.1016/j.nanoen.2017.04.005

10.1002/aenm.201700708

10.1016/j.jpowsour.2014.11.133

10.1016/j.nanoen.2019.03.012

10.1021/acs.inorgchem.7b01035

Liu S., 2018, Adv. Energy Mater., 8

10.1016/j.electacta.2015.06.085

10.1039/C7TA07659B

10.1039/C6TA10297B

10.1002/celc.201500148

10.1002/adma.201402541

10.1039/C7TA08735G

10.1039/C6CS00875E

10.1016/j.jechem.2019.08.022

 

10.1038/s41560-018-0180-6

10.1002/adfm.201400436

10.1016/j.electacta.2017.01.137

10.1002/celc.201700913

10.1016/j.jpowsour.2019.227195

 

10.1021/acsami.7b02944

10.1002/adma.201500956

 

10.1016/j.jallcom.2014.09.203

10.1016/j.jpowsour.2013.04.047

10.1021/am5017649

Qing R. P., 2016, Adv. Energy Mater., 6

10.1016/j.jpowsour.2017.11.042

10.1016/j.electacta.2015.08.163

 

10.1149/1.3571479

10.1126/science.1122152

10.1039/c3ee42398k

10.1021/cm400193m

 

10.1149/2.005207jes

10.1021/acsami.5b00645

 

10.1021/nl4019275

10.1021/acsami.6b06733

10.1021/acs.jpcc.7b01168

 

10.1021/acsaem.8b00630

10.1016/j.jpowsour.2013.08.081

Thông tin
Thông tin xuất bản

ChemElectroChem

Tập 7 Số 1

246-251

Thông tin tác giả