Raman spectroscopic determination of phase evolutions in LiAlxCo1−xO2 battery materials
Tóm tắt
Superior battery materials LiAlxCo1−xO2 (x = 0.0, 0.1, 0.3, 0.5, and 0.7) were synthesized using a solution-based route at various sintering temperatures (450–800 °C). In this communication, we report on the use of Raman spectroscopy to study effect of composition and sintering temperature on the resulting material. The phase evolutions in LiAlxCo1−xO2 compositions were studied using micro-Raman spectroscopy and a phase diagram is proposed based on the observations. For less Al content, the low-temperature phases of LiAlxCo1−xO2 showed Raman spectra corresponding to a monoclinic (space group C2/m) structure, while a low-temperature spinel (space group Fd3m) phase was observed for 50% or more Al in these compounds. All these compositions exhibited a layered hexagonal (space group R3m) structure when sintered above 700 °C. Raman spectra also revealed residual Co3O4 in the low-temperature forms of LiCoO2 and LiA10.01Co0.9O2.
Tài liệu tham khảo
For reviews, see Mater. Res. Soc. Bull. 25, (3) (2000).
R. Koksbang, J. Barker, H. Shi, and M.Y. Saidi, Solid State Ionics 84, 1 (1996).
C.D.W. Jones, E. Rossen, and J.R. Dahn, Solid State Ionics 68, 65 (1994).
R. Stoyannova, E. Zhecheva, and L. Zarkova, Solid State Ionics 73, 233 (1994).
G. Ceder, Y-M. Chiang, D.R. Sadoway, M.K. Aydinol, Y-I. Jang, and B. Huang, Nature 392, 694 (1998).
Y-I. Jang, B. Huang, H. Wang, D.R. Sadoway, G. Ceder, Y-M. Chiang, H. Liu, and H. Tamura, J. Electrochem. Soc. 146, 862 (1999).
R.J. Gummow, M.M. Tackeray, W.I.F. David, and S. Hull, Mater. Res. Bull. 27, 327 (1992); Mater. Res. Bull. 28, 1177 (1993).
E. Rossen, J.N. Rimers, and J.R. Dahn, Solid State Ionics 62, 53 (1993).
J.N. Reimers and J.R. Dahn, J. Electrochem. Soc. 139, 2091 (1992).
T. Ohzuku and A. Ueda, J. Electrochem. Soc. 141, 2972 (1994).
W. Huang and R. Frech, Solid State Ionics 86–88, 395 (1996).
A. Honders, J.M. der Kinderen, A.H. van Heerden, J.H.W. de Wit, and G.H.J. Broers, Solid State Ionics 14, 205 (1984); Solid State Ionics 15, 265 (1985).
R.K. Moore and W.B. White, J. Am. Ceram. Soc. 53, 679 (1970).
M. Inaba, Y. Iriyama, Z. Ogumi, Y. Todzuka, and A. Tasaka, J. Raman Spectrosc. 28, 613 (1997).
D. Bersani, P.P. Lottici, and X-Z. Ding, Solid State Commun. 72, 73 (1998).
M. Inaba, Y. Todzuka, H. Yoshida, Y. Grincourt, A. Tasaka, Y. Tomida, and Z. Ogumi, Chem. Lett. 889 (1995).
V.G. Hadjiev, M.N. Iliev, and I.V. Vergilov, J. Phys. C: Solid State Phys. 21, L119 (1998).
G. Chen, W. Hao, Y. Shi, Y. Wu, and S. Perkowitz, J. Mater. Res. 15, 583 (2000).
S. Buta, D. Morgan, A. van der Ven, M.K. Aydinol, and G. Ceder, J. Electrochem. Soc. 146, 4335 (1999).